稀盐酸中锰结核还原浸出溶液净化除铁

针对酸性氯化物中黄铁矿还原浸出锰结核的溶液成分特点，选择黄钠铁矾法进行了沉淀分离铁的研究。结果表明温度和晶种以及溶液ｐＨ值是影响铁矾沉淀的重要因素。在ｐＨ２．０左右，溶液温度高于９０℃，足量晶种加入的情形下，１５０ｍｉｎ后可将溶液中的铁含量降至０．１ｇ／Ｌ。沉矾过程的表观活化能为９４．６６ｋＪ／ｍｏｌ。黄铁矿氧化生成的硫酸根随铁一同沉淀，从而消除了ＳＯ２－４在氯化物体系中的积累。     

High-temperature oxidation of aluminum electroplated Fe-Mn alloys

Austenitic Mn-Al alloys (20–32 W/O Mn, 7–10 Al, 2–3 Si, 1C) were found to have satisfactory oxidation resistance up to 950°C under isothermal conditions in air. Surface enrichment of aluminum is a necessary condition for obtaining an almost pure alumina scale for uses at higher temperatures. Four different Mn-steels were Al-coated by the Capuano electroplating process. In all the steels there was an increase in the hot-oxidation resistance. The best results were obtained with steels containing both Al and Si, and this for temperatures up to 1100°C. No spalling was noticed during rapid cooling of the test pieces. Silicon was found to act as a diffusion barrier to outward iron diffusion. It appears that there is formation of a pure, thin film of alumina from the matrix which interacts with the aluminum diffusing from the superimposed, coating for the formation of good bonds.     

纳米层状双金属氢氧化物的制备及结构表征

采用恒定pH 12±0.2,按n(Mg2+)∶n(Al3+)∶n(OH-)∶n(CO2-3)=6∶2∶16∶1配制溶液,采用一步反应液相法,制备纳米层状双金属氢氧化物(LDH)粉体.为了获得无团聚、分散均匀的纳米粉体,探讨了溶剂置换干燥、真空干燥、常压干燥对纳米LDH粉体形成团聚的影响;用X射线衍射仪、透射电镜、红外光谱仪和元素分析仪对样品的物相、形貌、粒径和组成进行了表征.结果表明,溶剂置换干燥能够有效防止纳米粉体形成硬团聚,样品分散性好,呈针状形态,长50 nm,宽5 nm.     

锰掺杂对PNW-PMS-PZT压电陶瓷结构和性能的影响

采用传统陶瓷工艺制备了Pb(Ni1/2W1/2)O3-Pb(Mn1/3Sb2/3)O3-Pb(Ti，Zr)O3-xMnO2压电陶瓷，分析了经1150℃烧结2h制备的陶瓷样品的相结构组成。实验结果表明：所有陶瓷样品均为钙钛矿相，未发现其它晶相。随着锰掺杂量的增加，陶瓷晶粒逐渐长大。研究了不同剂量的锰掺杂对压电陶瓷介电和压电性能的影响。结果表明：随着锰掺杂量的增加，材料逐渐变“硬”，当MnO2掺杂量少于0．2％(按质量计，下同)时，相对介电常数εr、压电常数d33和机械品质因数Qm逐渐增加，介电损耗tanδ减小；当MnO2掺杂量多于0．2％时，εr、d33和Qm逐渐降低，tanδ增加。随着锰掺杂量的增加，机电耦合系数kp和Curie温度θc逐渐减小。MnO2掺杂量为0．2％的压电陶瓷适合制作大功率压电陶瓷变压器。其压电性能为：εr=2138，tanδ=0．0058，kp=0．613，Qm=1275，d33=380pC／N和θc=205℃。     

A kinetic study on medium temperature desulfurization using a natural manganese ore

Natural manganese ores were selected as raw materials for the desulfurization sorbent because of economical efficiency and high reactivity on hydrogen sulfide. Initial reaction rates between H₂S and desulfurization sorbent of natural manganese ores were determined in a temperature range of 400-800°C using a thermobalance reactor. All reactions were first order with respect to H₂S and were expressed by the Arrhenius relation. When the sulfidation reaction was controlled by diffusion, the temperature dependence of the effective diffusivity was given by the Arrhenius equation. Activation energies and frequency factors were obtained from the product layer diffusion coefficient of various sorbents by plotting as an Arrhenius equation form. Several additives were mixed to improve the sulfidation capacity, and NiO was the best additive.     

Fischer–Tropsch synthesis over Co–SiO2 catalysts prepared by the sol–gel method

Fischer–Tropsch synthesis was carried out in slurry phase over uniformly dispersed Co–SiO₂ catalysts prepared by the sol–gel method. When 0.01–1 wt.% of noble metals were added to the Co–SiO₂ catalysts, a high and stable catalytic activity was obtained over 60 h of the reaction at 503 K and 1 MPa. The addition of noble metals increased the reducibility of surface Co on the catalysts, without changing the particle size of Co metal significantly. High dispersion of metallic Co species stabilized on SiO₂ was responsible for stable activity. The uniform pore size of the catalysts was enlarged by varying the preparation conditions and by adding organic compounds such as N,N-dimethylformamide and formamide. Increased pore size resulted in decrease in CO conversion and selectivity for CO₂, a byproduct, and an increase in the olefin/paraffin ratio of the products. By modifying the surface of wide pore silica with Co–SiO₂ prepared by the sol–gel method, a bimodal pore structured catalyst was prepared. The bimodal catalyst showed high catalytic performance with reducing the amount of the expensive sol–gel Co–SiO₂.     

Lanthanum-Magnesium and Lanthanum-Manganese Donor-Acceptor-Codoped Semiconducting Barium Titanate

BaTiO₃ powder doped with La donor and codoped with Mn or Mg acceptor was sintered at 1350°C/1 h in air. For Ladoped BaTiO₃, the room-temperature resistivity decreased to a minimum at [La³⁺] ∼ 0.15 mol%. For La-Mn-codoped BaTiO₃, the minimum resistivity occurred at [La³⁺] - 2[Mn²⁺] ∼ 0.15 mol%. When the ceramic was changed to a fine-grained insulator by high donor doping ([La³⁺] >0.15 mol%), its semiconductivity was restored, and the relatively homogeneous, coarse-grained microstructure recurred by codoping with either Mg or Mn acceptor, with the transition at [La³⁺] - 2[Mg²⁺] = 0.15 mol% or [La³⁺] - 2[Mn²⁺] = 0.15 mol%. The analogy of a compensation effect between La-Mn- and La-Mg-codoped BaTiO₃ suggested that Mn acceptor added to BaTiO₃ exists as Mn²⁺ ion in the bulk grain region; its influence on the positive temperature coefficient of resistivity behavior is then discussed.     

Selective oxidation of styrenes under oxygen catalyzed by cobalt chloride

The cobalt(II) chloride-catalyzed oxidative cleavage of -methylstyrene with oxygen in t-BuOH gives acetophenone and formaldehyde in good yield. The competing reactions between C=C cleavage and formation of polymeric products are strongly affected by the solvent, cobalt catalyst and concentration used, as well as the reaction temperature. A free radical mechanism involving a cyclic peroxide intermediate is proposed to give the cleavage products. Oxidation of various alkenes using CoCl₂/t-BuOH/O₂ system shows that only activated styrenes can be oxidized effectively. The reactivity of various styrenes and their selectivity towards giving cleavage products or polymers are strongly influenced by the electronic and steric properties of the substrate.     

Investigation of bio-ethanol steam reforming over cobalt-based catalysts

The catalytic performance of cobalt catalysts supported on γ-Al₂O₃, TiO₂, ZrO₂ were studied for bio-ethanol steam reforming (BESR) reaction. The supported catalysts (10 wt%Co) were prepared by impregnation and characterized through Thermogravimetric analysis (TGA), H₂ chemisorption, laser Raman Spectroscopy, Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS), and temperature-programmed reaction (TPRxn). The metallic cobalt sites were found to correlate with the BESR reaction activity. The reaction and H₂ chemisorption showed that ZrO₂ supported catalyst showed the best dispersion and best catalytic activity. Over the 10% Co/ZrO₂ catalyst, using a H₂O:EtOH:inert molar ratio of 10:1:75 and a GHSV = 5000 h⁻¹, 100% ethanol conversion and a yield of 5.5 mol H₂/mol EtOH were obtained at 550 °C and atmospheric pressure.     

Synthesis and electrochemical characterization of a new Se-doped spinel material for lithium secondary batteries

A new Se-doped spinel material, LiAl_0.18Se_0.02Mn_1.8O₄ powder with a phase-pure polycrystalline was synthesized by a sol–gel method. The material in the 3 V region (2.4 3.5 V) and both the 3 and 4 V region (2.4 4.4 V) initially deliver a discharge capacity of 81 and 178 mA h g^–1 which increase with cycling to reach 110 and 204 after 50 cycles, respectively. The material shows excellent cycleability in the 4 V region (3.0 4.4 V) with almost no capacity loss. The structural integrity of the Se-doped spinel was characterized by charge–discharge cycling tests and X-;ray diffraction.