Ermüdungsverhalten und Dauerfestigkeit von Graphit und Aluminium – infiltriertem Graphit

Fatigue behaviour and endurance limit of graphite and of aluminium‐infiltrated graphite Fatigue properties of polycrystalline, isotropic graphite FU2590 and of FU2590 infiltrated with AlSi7Mg (FU2590/AlSi7Mg) were investigated in reversed bending tests at 25 Hz at numbers of cycles below 10⁷ and in tension‐compression tests at 20 kHz below 10⁹ cycles. The open porosity of Graphite (10‐11 Vol.‐%) was infiltrated with the aluminium alloy using the squeeze casting infiltration method, which led to an increase of the bending strength by 50 %, increase of tensile strength by 30 % and increase of stiffness by 15 %. Fully reversed tension‐compression loading of FU2590 delivers a mean endurance limit at 10⁹ cycles at the normalized maximum stresses (i.e. maximum tension stress of a cycle divided by the static strength) of 0,65±0,03. Mean numbers of cycles to failure of 10⁴ were found in fully reversed bending tests at the normalized maximum stress of 0,78. The infiltrated material shows approximately 30 % higher cyclic strength in reversed bending tests, and the mean endurance limit under tension compression loading increases by 15 %. The increased endurance limit of the infiltrated material is caused by the increased stiffness. The increased toughness of graphite due to the infiltration with aluminium is of additional beneficial influence at the higher cyclic stresses investigated in reversed bending tests and in static tests.     

用超声处理在石墨表面形成梯度孔洞

研究了超声处理对石墨表面状况的影响。超声处理初期，增加超声处理时间使石墨显气孔率增加，表面孔洞数量增多，尺寸变大；超声处理5min后，超声处理时间增加，显气孔率和孔洞状态基本不变。用超声处理能在石墨表面内层附近形成比较理想的梯度分布孔洞。     

膨胀石墨对各种油类的吸附动力学

通过对吸附率(有效吸附系数)Ks和饱和吸附量msat的测量,描述了粘度为0.001 Pa·s～0.850 Pa·s的各种油类在膨胀石墨柱中的吸附动力学,发现吸附率Ks对油类粘度有很强的相关性.吸入膨胀石墨柱中的饱和吸附量msat几乎恒定在50kg/kg,该值略低于由膨胀石墨块直接浸渍在油中测得的吸附容量,这是由于所吸附的油沿膨胀石墨柱高度存在重力梯度.     

Tearing, folding and deformation of a carbon-carbon sp-bonded network

A monolayer and a few layers of carbon sp²-bonded networks were torn and folded by the tip of an atomic force microscope at the steps on newly cleaved highly oriented pyrolytic graphite. It was found that the preferential breaking directions and folding axes are along the symmetry directions of the graphite hexagonal structure. Depending on the force exerted by the tip, breaking may occur along other directions. The torn part of the graphene sheet can even be stretched and deformed, and does not resume its original shape after release from the tip.     

石墨电极高温抗氧化技术研究现状

概述石墨电极抗氧化技术的研究现状，重点介绍选择抗氧化涂层体系的要求及涂层制备方法，包括包埋浸渗法、化学气相沉积法、等离子喷涂法及溶胶--凝胶法．展望了石墨电极材料高温抗氧化涂层研究的方向．     

A Simple Quasi-2D Numerical Model of a Thermogage Furnace

A simple quasi-2D model for the temperature distribution in a graphite tube furnace is presented. The model is used to estimate the temperature gradients in the furnace at temperatures above which contact sensors can be used, and to assist in the redesign of the furnace heater element to improve the temperature gradients. The Thermogage graphite tube furnace is commonly used in many NMIs as a blackbody source for radiation thermometer calibration and as a spectral irradiance standard. Although the design is robust, easy to operate and can change temperature rapidly, it is limited by its effective emissivity of typically 99.5–99.8%. At NMIA, the temperature gradient along the tube is assessed using thermocouples up to about 1,500°C, and the blackbody emissivity is calculated from this. However, at higher operating temperatures (up to 2,900°C), it is impractical to measure the gradient, and we propose to numerically model the temperature distributions used to calculate emissivity. In another paper at this conference, the model is used to design an optimized heater tube with improved temperature gradients. In the model presented here, the 2-D temperature distribution is simplified to separate the axial and radial temperature distributions within the heater tube and the surrounding insulation. Literature data for the temperature dependence of the electrical and thermal conductivities of the graphite tube were coupled to models for the thermal conductivity of the felt insulation, particularly including the effects of allowing for a gas mixture in the insulation. Experimental measurements of the temperature profile up to 1,500°C and radial heat fluxes up to 2,200°C were compared to the theoretical predictions of the model and good agreement was obtained.     

制备低硫可膨胀石墨的研究

研究了以过二硫酸铵作氧化剂低硫可膨胀石墨的制备，找到了在较低温度下，制备低硫可膨胀石墨的最佳条件。即过二硫酸铵和石墨的重量比为１５％；反应温度为５５℃；反应时间为４０ｍｉｎ；硫酸浓度为９８％；硫酸与石墨的重量比为４∶１，草酸和硝酸（浓度为６５％）的重量比为７．５％时，所制得的可膨胀石墨含硫量为０．６５％，膨胀容积为２００ｍＬ／ｇ可膨胀石墨。并且，其终端产品柔性石墨具有优良的力学性能和抗氧化性能。     

真空阴极弧离子镀类金刚石碳（DLC）膜的碳弧稳定性研究

选用氩气、氩气加氢气、氩气加乙炔等气体作为介质，石墨作为靶材进行真空阴极弧离子镀来制备类金刚石碳膜。石墨电弧有其独特的电弧特性曲线，不同气体介质对碳弧特性的影响不同，磁场的大小对电弧的稳定性有很大作用，碳弧下基片偏流随电弧电压的增加而减小，试验得到表面光滑的类金刚石碳（DLC）膜，对膜的表面进行了SEM分析。     

WCp增强球铁基复合材料模具的制备及其磨损性能

针对耐火砖模具的工矿特点,将复合材料设计原理和铸造技术相结合,采用复合剂技术,在普通砂型条件下制备了WCp增强球墨铸铁基表层复合材料模具,并对其三体磨粒磨损性能进行了研究.结果表明,合适的球墨铸铁基体材料的主要成分w为3.7%C、2.1%Si、1.0%Cu和0.3%Mn;铸件表面平整,复合层厚度均匀,可达7～9 mm,复合组织的硬度达到HRC 62以上;复合材料相对于基体材料的耐磨性提高到8以上.