Effect of Y2O3, CeO2 on Sintering Properties of Si3N4 Ceramics

The effect of rare earth oxides Y203 or Ce02 on sintering properties of Si3N4 ceramics was studied and the mechanism of assisting action during sintering was analyzed. The results in dicate that the best sintering properties appear in Si3N4 ceramics with 5% Y203 or 8% CeO2. Secondary crystallites are formed at grain boundaries after heat treatment,which decreases the amount of glass phase and contributes to the improvement of high-temperature mechanical properties of silicon nitride.     

2,4-二氯氟苯的合成

论述了2，4－二氯氟苯合成的新方法。以对氯硝基苯为起站原料，经氟化反应、硝化反应及氯化反应制得2，4-二氯氟苯，总收率达59．0％。本合成路线工艺简单、操作安全、原料易得、成本低廉，适合于工业化生产。     

高速钢W6Mo5Cr4V2的脱磷试验

在３０ｋｇ感应炉上用ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ（ＭｏＯ３）渣、ＭｏＣｌ６粉剂和Ａｌ－Ｃａ合金作脱磷剂对高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２进行脱磷试验。结果表明，ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ渣的脱磷效果最好，一般脱磷率可达２６％￣５６％。     

从水淬渣中回收镓的试验研究

对鼓风炉（ISP法）或烟化炉水淬渣中回收镓的工艺进行了研究。结果表明，利用浓硫酸恒温熟化的独特浸出工艺，克服硅对液固分离的影响；以伯胺N9123作为萃取剂在硫酸介质中萃取镓；获得了含镓品位为2.82%的富集物。     

新标准新突破--MP4NET引领安防行业发展

介绍了视频压缩技术从MPEG1、MPEG2到目前主流技术MPEG4,分析了数字视频存储、检索、传输上优于模拟技术的特点,从而使视频网络应用,数据库支撑的应用、安防行业的数字化应用的迅速发展。     

兼容IPv4及IPv6的网络程序设计

介绍了在Window系统中设计兼容IPv4及IPv6的网络程序的方法,并给出了用WinsockAPI编程的具体步骤。     

Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

Decreasing miscibility with greater heterogeneity in ternary polymer blend: poly(cyclohexyl methacrylate), poly(α‐methyl styrene) and poly(4‐methyl styrene)

A ternary blend system comprising poly(cyclohexyl methacrylate) (PCHMA), poly(α‐methyl styrene) (PαMS) and poly(4‐methyl styrene) (P4MS) was investigated by thermal analysis, optical and scanning electron microscopy. Ternary phase behaviour was compared with the behaviour for the three constituent binary pairs. This study showed that the ternary blends of PCHMA/PαMS/P4MS in most compositions were miscible, with an apparent glass transition temperature (T_g) and distinct cloud‐point transitions, which were located at lower temperatures than their binary counterparts. However, in a closed‐loop range of compositions roughly near the centre of the triangular phase diagram, some ternary blends displayed phase separation with heterogeneity domains of about 1 µm. Therefore, it is properly concluded that ternary PCHMA/PαMS/P4M is partially miscible with a small closed‐loop immisciblity range, even though all the constituent binary pairs are fully miscible. Thermodynamic backgrounds leading to decreased miscibility and greater heterogeneity in a ternary polymer system in comparison with the binary counterparts are discussed. © 2003 Society of Chemical Industry     

Schubspannungsbomben in Faserverbunden

Shear Bombs in Fibre Composites Despite an optimum external shape non‐load adapted internal fibre orientation can lead to the formation of shear cracks where crossing tension‐compression principal stress trajectories create localized shear peaks. Trees are subject to those failure because they cannot re‐arrange their fibres after wood formation. Bones can adjust their micro‐structure to changing load conditions and in this way can better control shear failure. The engineer working with fibre composites should be alert to avoid fibre arrangements not following the force flow. Localized shear zones may also form near notches similar to normal notch stresses, however they are not always situated at the contour line of the notch.