MCS接枝共聚物的结构和形态

将甲基丙烯酸甲酯（ＭＭＡ）、苯乙烯（Ｓ）在氯化聚乙烯（ＣＰＥ）存在下进行悬浮接枝共聚，获得ＭＣＳ树脂。本文着重考察了ＭＣＳ树脂的化学结构及胶粒形态。结果表明，确实发生了接枝共聚。ＣＰＥ用量、ＲＳＨ含量、引发剂浓度、反应温度、溶胀时间及聚合转化率对ＭＣＳ树脂的接枝率、接枝效率均有影响。ＭＣＳ树脂是接枝共聚物、ＭＭＡ／Ｓ共聚物与ＭＭＡ均聚物的混合物，橡胶相ＣＰＥ在ＭＣＳ树脂中的分散情况为“海岛结构”，     

PC／ABS合金的研制及其在汽车上的应用

对ＰＣ／ＡＢＳ合金开发和研制及其在汽车上的应用作了评述。介绍了上海杰事公司在该领域的进展。     

电晕放电注入双向拉伸聚丙烯薄膜驻极性能的探讨

以一种双向拉伸聚丙烯（ＢＯＰＰ）薄膜在不同温度下进行恒温处理，然后进行负电晕驻极。结果表明，ＢＯＰＰ薄膜随恒温处理的温度升高，热刺激电流（ＴＳＣ）峰值愈低。利用经验方法，估算了它们的活化能，并探讨了导致ＴＳＣ峰温变化的原因。     

动态交联热塑性弹性体增韧聚丙烯合金

用动态交联方法制备聚烯烃热塑性弹性体（ＴＰＯ）增韧聚丙烯，制备了具有低温冲击性能良好、综合力学性能比较均衡的聚丙烯合金。同时，研究了ＴＰＯ组成、工艺及基体组成与ＴＰＯ增韧聚丙烯共混物力学性能的关系。并通过差热扫描量热计和扫描电镜考察了共混物的形态结构。     

聚乙烯接枝改性及其与铝的粘结性

聚乙烯在过氧化二异丙苯存在下分别与丙烯酸，顺丁烯酸酐，顺丁烯二酸，顺丁烯二酸钠，丙烯酸羧丙酯，甲基丙烯酸环丙酯等单体熔融挤出，产物的红外光谱表明聚乙烯不同程度地接了各种极性基团。     

Do the Kallikaks look "menacing" or "retarded?"

To extend R. E. Fancher's (see record 1987-31600-001) review of claims that photographs of the Kallikak family in H. H. Goddard's (1912) study had been retouched to make them look more menacing and retarded, 29 Ss (aged 18–69 yrs) were surveyed for their impressions of the photographs. Overall, Ss were strongly inclined to view the photographed individuals as "kind" and "very bright." (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

改善30Cr2MoV钢大锻件冲击韧性及晶粒度的研究

通过模拟试验及生产试验,对改善30Cr2MoV钢锻件冲击性能及晶粒度进行了分析研究,找到了较为有效的热处理方法,可使用的FATT达到20℃以下,晶粒度达到6级以上。     

Thermoplastic polyurethane (TPU) modifier to develop bimodal cell structure in polypropylene/TPU microcellular foam in presence of supercritical CO2

Currently, the fabrication of microcell and bimodal cell structures (BCS) in polymer foams by using supercritical fluids has become a hot as well as a challenging research area worldwide. In this work, an environmentally friendly, effective, facile, and CO₂-based foaming technique was presented to fabricate microcellular polypropylene (PP) foams with BCS via blending with thermoplastic polyurethane (TPU). The toughness, thermal properties, rheological properties, and foamability of PP were systematically investigated with gradual incorporation of TPU. Representative sea-island structure was observed in the scanning electron microscopy (SEM) images for the fracture surface of various PP/TPU samples. Rheological measurement results demonstrated that the viscoelasticity of various PP/TPU samples was improved remarkably compared with that of pure PP and pure TPU. The impact strength of various PP/TPU samples possessed the highest value as 12.4 kJ/m² with the TPU content of 15 wt%. After the addition of TPU, an ameliorative cellular morphology was observed in the SEM micrographs of various PP/TPU samples and their volume expansion ratio was enhanced significantly thanks to their improved melt elasticity. Moreover, it is worth noting that BCS appeared in various PP/TPU foams when the TPU content exceeded 5 wt%.     

H-PSMA/PVA/PP复合膜的制备及油-水乳液分离性能

通过两步法对聚丙烯（PP）膜进行了亲水改性:首先,通过在碱性条件下水解苯乙烯-马来酸酐共聚物（PSMA）制备了水解的苯乙烯-马来酸酐共聚物（H-PSMA）;然后,以聚乙烯醇（PVA）为亲水性改性剂,戊二醛（GA）为交联剂,将H-PSMA/PVA/GA复合材料浸涂在PP基底膜上,制备了亲水性水解苯乙烯-马来酸酐共聚物/聚乙烯醇/聚丙烯（H-PSMA/PVA/PP）复合膜。利用傅里叶变换红外光谱（FT-IR）分析表征了H-PSMA和H-PSMA/PVA/GA的结构;通过测试复合膜表面的静态接触角,探究了PVA和GA含量及成膜溶液的质量浓度等对膜表面润湿性能的影响;最后,测试了复合膜的油水分离效率和重复利用率。结果表明:当GA、PVA和H-PSMA的质量比为0.225∶1∶1,成膜溶液的质量浓度为0.03 g/mL时,所制备的H-PSMA/PVA/PP复合物膜对水包油乳液（O/W）表现出优异的分离性能,初次油水分离效率为99.40%,当重复分离10次后,油水乳液的分离效率仍达到98.83%以上。该复合膜的制备工艺具有安全性好、成本低和环境友好的特点。     

多回路冷凝法技术在聚丙烯装置尾气回收中的应用

陕西延长石油集团炼化公司延安石油化工厂,结合其20万t/a聚丙烯装置实际,自主开发出了一种多回路冷凝装置尾气的回收工艺技术,并成功工业化应用于该装置的3路丙烯尾气的冷凝回收系统。近5年的运行结果表明:经多种措施及操作优化后,该3路冷凝丙烯尾气回收系统,不仅实现了长周期连续平稳、安全运行,还可有效回收丙烯、丙烷分别约为2660,140 t/a。