ZnFe2O4高温煤气脱硫剂的再生

在热天平上对自制的ZnFe2O4脱硫剂进行了再生工艺研究，考察了再生温度、O2浓度对ZnFe2O4脱硫剂再生性能的影响；进行了多次硫化、再生循环实验，并与加入玻璃粉的样品进行了比较。结果表明，700℃下氧含量2.0%(vol)时再生可以获得良好的再生率和二次硫化反应活性；玻璃粉的少量加入，会改善脱硫剂长期使用的稳定性，但反应活性有所下降。     

氧化还原反应式配平中可能差错的几种情况

本文通过许多实例，指出了氧化还原反应式配平中可能出现的得失电子数不等或电荷数未配平、得失电子关系不对及反应式中酸碱性介质有错误等几种差错，并归纳了在酸碱性水溶液中平衡介质的方法。     

A/O结合循环式活性污泥法处理海产品加工废水

针对海产品加工废水氨氮含量较高的特点。舟山兴业有限公司的污水处理工程采用两段A/O结合循环式活性污泥法工艺，工程验收合格后运行一年多来，排放废水的各项污染指标均达到国家《污水综合排放标准》（GB8978-1996）的二级标准，处理系统具有很好的抗冲击能力和脱氮效果。     

用纯氧化铕模拟基体AES法测定氧化铥中的钬、饵、镱、镥和钇

用于发射光谱分析的氧化铥基体不但难于寻找,而且价格昂贵.本文用氧化铕模拟氧化标基体的办法,其测定结果与别的方法基本符合.为寻找代替氧化铥基体提供了一条途径.     

Fatty acid variation among U.S. Runner-type peanut cultivars

Fatty acid composition was determined among seven U.S. runner-type peanut (Arachis hypogaea L.) cultivars: Florunner, Sunrunner, GK-7, Southern Runner, Sunbelt Runner, Okrun, and Langley. Significant year and cultivar differences were found within these fatty acid profiles. Southern Runner had the best oleic to linoleic ratio and iodine values; whereas Florunner, Sunrunner, and Langley were the highest in unsaturated and lowest in saturated and long-chain fatty acids. For the future, breeding programs need to continue developing peanut cultivars with improved oil quality.     

氧氯化反应器蛇管的制造工艺

介绍了氧氯化反应器蛇管在国产化过程中的制造简便、组装准确可靠的制造工艺，并对该蛇管中的定位套作了合理的改进     

SO2-4/La2O3-ZrO2催化合成亚油酸乙酯

将SO2-4/ZrO2负载镧制备了新型催化剂SO2-4/La2O3-ZrO2,以亚油酸和乙醇的酯化反应为探针,考察了不同制备条件对催化剂性能的影响,结果表明,La3+浸渍浓度为0.07 mol/L,经110℃烘干后于500℃焙烧3 h所得催化剂活性最好.采用正交实验法对影响酯化反应的因素进行考察,最佳实验条件为n(醇):n(酸)= 6:1,反应时间6 h,催化剂用量3%(亚油酸),酯化率可达93.7%.且该催化剂具有良好的重复使用和再生能力.     

Structure, thermal-stability and reducibility of Si-doped Ce–Zr–O solid solution

The Si-doped Ce–Zr–O solid solutions have been prepared by the reverse microemulsion method. The effects of Si and its content on the structure characters, thermal-stability and reducibility of the Ce–Zr–O solid solution have been studied by N₂ adsorption, XRD, laser Raman (LR), TPR, FT-IR, NMR and XPS methods. The results indicate that, there are the bonds of Si–O–M (Ce or Zr) in the Ce–Zr–Si–O solid solutions, and the presence of Si can increase obviously the surface area, thermal-stability, crystal lattice distortion rate, and reducibility of the solid solution. The surface area of the sample with 20 wt.% Si reaches 153 m² g⁻¹ after being calcined at 900 °C for 6 h. The Ce–Zr–O solid solution with 5.2–10 wt.% Si shows excellent thermal-stability and reducibility.     

B_2O_3和CaF_2对C_3S-C_(2.75)B_(1.25)A_3-C_2S-C_3A水泥熟料矿物体系力学性能影响

研究了B2O3和CaF2对C3S-C2.75B1.25A3S珚-C2S-C3A熟料矿物体系的组成、结构与力学性能的影响。研究结果表明:在该熟料体系中C3S,C2.75B1.25A3S珔,C2S和C3A的适宜含量分别为50%,10%,25%和15%,B2O3和CaF2的适宜掺量为2%和1.5%。在最佳组成和制备工艺条件下,合成的阿利特-硫铝酸钡钙水泥的1d,3d和28d抗压强度分别达到18MPa,48MPa和95MPa以上,展现了良好的早期力学性能。同时,掺加CaF2能有效降低熟料中游离氧化钙的含量,促进阿利特在低温条件下形成。利用SEM-EDS,XRD等测试手段对熟料的组成、结构及性能进行了分析。     

α-Fe2O3/煤矸石复合光催化剂的制备及其降解五氯酚性能的研究

以Fe（NO₃）₃、煤矸石和NaOH为原料,采用沸腾回流法制得了一系列不同质量比的α-Fe₂O₃/煤矸石复合光催化剂。采用场发射扫描电子显微镜（FESEM）、X射线衍射仪（XRD）及紫外-可见漫反射光谱（UV-Vis DRS）等多种手段对产物做了表征。以五氯酚为目标降解物,考察了模拟太阳光照下样品的光催化效果。结果表明,将球形α-Fe₂O₃负载于改性煤矸石表面可有效提高其光催化活性,且α-Fe₂O₃/煤矸石复合光催化剂的性能与α-Fe₂O₃的含量有关,当α-Fe₂O₃与煤矸石的质量比为30∶100时,样品的光催化效果最佳,180 min内即可将五氯酚降解完全。此外,α-Fe₂O₃/煤矸石复合光催化剂还具有可重复使用的特点。