Trivalent chromium removal from tannery effluent using kaolin‐supported bacterial biofilm of Bacillus sp isolated from chromium polluted soil

BACKGROUND: Bacterial strains belonging to the genus Bacillus, isolated from Cr‐ polluted soil (tannery sludge) were employed as consortium for Cr(III) removal from tannery effluents. Kaolin clay, a natural adsorbent, was used as supporting material for bacterial biofilm formation. The use of clay‐supported bacterial biofilm has not previously been employed for the treatment of tannery effluents containing Cr(III) salt. RESULTS: Commercial tannery effluent containing 1000 ppm initial metal ion concentration was treated in stages. The initial Cr(III) concentration of 1000 ppm was brought down to 2 ppm, a permissible level for discharge, after the fourth stage. The bacterial isolates were found to be Bacillus subtilis VITSCCr01 and Bacillus cereus VITSCCr02 by 16s rRNA gene sequencing. Batch assay and confocal laser scanning microscopy results revealed the role of kaolin as a support material in biofilm formation. Best fit was obtained with the Freundlich adsorption isotherm. The mechanism of sorption was confirmed by Fourier transform infrared (FT‐IR) spectroscopy and scanning electron microscopy–energy dispersive X‐ray spectroscopy (SEM‐EDS). CONCLUSION: Cr(III) removal from tannery effluent using low cost adsorbents such as kaolin and bacteria proved to be effective for metal concentrations ?1000 ppm; this is normally not possible using conventional treatment methods. This work has demonstrated feasible sorption of Cr(III), especially during post‐tanning operations. Copyright © 2011 Society of Chemical Industry     

激光热源偏移对6mm A7N01铝合金激光-MIG复合焊焊接头的质量影响

针对铝合金激光-MIG复合焊接过程中的热源偏移问题,采用激光-MIG复合焊对6 mm厚A7N01P-T4铝合金进行焊接,给定热源对中偏移,并分析无对中偏移及有对中量偏移的焊接接头宏观成形、微观组织、力学性能,以此研究热源对中偏移对6 mm厚A7N01铝合金激光-MIG复合焊接接头的影响。研究结果表明,有热源对中偏移的试板接头内部存在少量的气孔缺陷,与无对中偏移试板相比,拉伸性能下降21 MPa。     

热矫形温度对6N01铝合金接头组织与性能的影响

对6N01-T5铝合金焊接接头进行了不同温度的热矫形,研究了矫形温度对接头微观组织及力学性能的影响规律。结果表明,250℃内加热时接头强度和焊缝区硬度有微量上升,HAZ和母材区硬度逐渐变大;高于250℃时强度和硬度开始下降,软化区范围加宽,分别向母材和淬火区方向延伸,高温下性能恶化严重;150℃~200℃加热时易发生弯断,且弯断角随温度升高而减小。室温时,接头母材区析出相为GP区和β″,硬度值较低,热影响区软化区晶内在只有粗大析出相;250℃加热时,母材区开始析出β′相,在β″和β'的析出转变期接头硬度与强度出现峰值,软化区因重新析出β'/β″相得到强化,拉伸断于焊缝;450℃加热时,接头处于严重过时效状态,无弥散析出相,硬度和强度降低。     

KR-01射孔保护液的开发与应用

油井补孔投入新的储量开采是油田挖潜增产中最频繁而重要的措施,中原油田大部分地层水矿化度高达4.31-30×104m g/L,且油层属中、强水敏地层,因此完井液质量直接影响补孔油井产量。文中介绍了KR-01射孔保护液的实验性能及在中原油田采油三厂补孔措施中的应用效果。现场应用及试井分析资料显示,采用KR-01射孔保护液措施井表皮系数小于零,有效的防止了油层污染,保护并改善了储层物性。     

焊接气孔缺陷对A7N01铝合金焊接接头腐蚀疲劳性能的影响

在不同环境湿度条件下制备了不同焊缝气孔率的A7N01铝合金焊接接头,并通过条件腐蚀疲劳强度和断口微观形貌研究气孔缺陷对焊接接头腐蚀疲劳性能的影响。结果表明,当焊接环境的湿度由常湿增至70%时,焊缝的平均气孔率由0.07%增大为0.16%,接头的条件腐蚀疲劳强度由110 MPa降为100 MPa,焊接气孔缺陷对A7N01铝合金焊接接头的腐蚀疲劳性能有明显影响。焊缝中的气孔会造成严重的缺口效应,引起应力集中,导致裂纹在气孔处优先萌生,并在应力和腐蚀介质的共同作用下形成沿晶与脆性疲劳条带的混合断裂形貌。     

线能量对A7N01铝合金焊接接头残余应力的影响

焊接残余应力的产生主要是焊接过程中热输入不均匀所造成,因此焊接工艺参数尤其是焊接线能量对焊接接头的残余应力影响较大。通过实际测量与仿真计算相结合的方法,研究线能量的变化对A7N01S-T5铝合金双脉冲MIG焊接头残余应力的影响。结果表明,线能量的增大提高了热输入量,使纵向残余拉应力峰值从149 MPa增加到190 MPa;横向拉应力峰值之间相差不大,但横向拉应力峰值较纵向拉应力峰值高出约27 MPa。仿真计算结果与实测值的应力分布趋势和拉应力的峰值相近,二者之间形成较好的印证关系。     

不同焊丝对A7N01铝合金焊接接头力学性能的影响

采用ER5356、ER5183和ER5087焊丝对A7N01S-T5铝合金进行MIG焊接,分析接头力学性能。试验结果表明,三种焊丝的接头焊接残余应力大小基本相当;采用ER5183焊丝焊接的接头抗拉强度和断后伸长率最高,且弯曲性能良好,原因是接头内气孔量较少;采用ER5356焊丝焊接的接头焊缝和热影响区的冲击功最高,ER5087焊丝接头焊缝和热影响区冲击功则低得多。综合来看,ER5183焊丝与A7N01S-T5铝合金的匹配性更好。     

A7N01P-T5铝合金断裂韧度的厚度效应

采用国家标准GB4161-2007对高速列车承载底架焊接结构材料A7N01P-T5铝合金型材的断裂韧度KC进行了测试和分析,测试了3种厚度母材的KC,基于能量理论和线弹性力学提出A7N01P-T5铝合金断裂韧度随试样厚度变化关系KC(B)的解析公式,并进一步采用国家标准GB21143-2007的CTOD试验对其进行验证.结果表明,该公式具有较高的精度和普适性,可用于确定不同板厚材料的KC,将公式应用于不同壁厚条件下的焊接结构的完整性评定,以此节省人力物力,并大幅度缩短焊接结构完整性评定及结构剩余寿命的计算周期.同时为各种金属材料的KC获取提供通用性的方法和参考准则.     

YT01低能量多碰塑性变形研究

为研究碰撞能对金属材料多碰塑性变形的影响,在实验室用自制的凸轮机械式多碰试验机对YT01试样进行了低能量多碰试验,采用坐标网格法、SEM、金相显微镜等方法研究了不同碰撞能对试样的塑性变形率、显微组织结构的影响.实验结果表明:峰值冲击应力不变时,多冲碰撞能量越大,试样累积塑性变形量也越大;随着碰撞次数的增加,试样塑性变形率减小并趋于平缓,塑性变形终止于距冲击表面69 mm处;256 000次碰撞后,试样显微组织细化,晶粒界增多.金属材料多冲碰撞塑性变形不仅与峰值冲击碰撞应力有关,也与冲击碰撞能有关.     

哈萨克斯坦01A井钻井技术研究

01A井是位于滨里海盆地的东缘构造带上部署的一口评价井,在钻井过程中钻遇的盐层软硬交错变化、浅层气等给施工造成了许多困难。根据实钻情况及时分析、总结,采取相应的技术措施,克服了钻井施工中出现的难题,完成了钻探任务。