A Multiscale-Porous Anion Exchange Membrane for Convenient and Scalable Electrokinetic Concentration of Cationic Species

A device able to electrokinetically concentrate cationic samples has many potential medical and industrial applications, but until now has remained undeveloped due to the lack of a commercial anion-permselective material leading to a prohibitively complex fabrication procedure. Herein, a novel multiscale-porous anion exchange membrane (MP-AEM) that enables the convenient and scalable electrokinetic concentration of cationic species is proposed. A mechanically enhanced multiscale-porous structure with a solid framework is realized by adopting polyester resin as an additive to overcome the intrinsic limitations of the AEM material. The scalable MP-AEM-embedded electrokinetic concentrator is devised based on the peculiar properties of the MP-AEM that for allow both ion and fluid transport. With the MP-AEM, the concentrator is fabricated in a highly streamlined manner consisting only of a simple insertion and assembly. The concentration performance of the MP-AEM-embedded electrokinetic concentrator is demonstrated with a positively charged fluorescent dye and a fluorescein-labeled protein, and the results show enrichment factors of 250 and 500, respectively. The MP-AEM makes cationic electrokinetic concentration more accessible and scalable, thereby enabling further progress in a wide range of fields.     

Tailoring the electron-blocking layer by addition of YSZ to Ba-containing anode for improvement of ceria-based solid oxide fuel cell

The in-situ fabrication of an electron-blocking layer between the Ba-containing anode and the ceria-based electrolyte is an effective approach in suppressing the internal electronic leakage in ceria-based solid oxide fuel cell (SOFC). To improve the thickness of the electron-blocking layer and to research the effect of the layer thickness on the improvement of SOFC, a Ba-containing compound (0.6NiO-0.4BaZr_0.1Ce_0.7Y_0.2O_3-δ) modified by Y stabilized zirconia (YSZ) was employed as a composite anode in this research. SEM analyses demonstrated that the thickness of the interlayer can be simply controlled by regulating the proportion of YSZ at anode. The in-situ formed interlayer in the cell with the anode modified by 20?mol% YSZ possesses a thickness of 0.9?µm which is more suitable for the cell achieving an enhanced performance.     

Novel electrospun polymer electrolytes incorporated with Keggin‐type hetero polyoxometalate fillers as solvent‐free electrolytes for lithium ion batteries

In this study, solvent‐free nanofibrous electrolytes were fabricated through an electrospinning method. Polyethylene oxide (PEO), lithium perchlorate and ethylene carbonate were used as polymer matrix, salt and plasticizer respectively in the electrolyte structures. Keggin‐type hetero polyoxometalate (Cu‐POM@Ru‐rGO, Ni‐POM@Ru‐rGO and Co‐POM@Ru‐rGO (POM, polyoxometalate; rGO, reduced graphene oxide)) nanoparticles were synthesized and inserted into the PEO‐based nanofibrous electrolytes. TEM and SEM analyses were carried out for further evaluation of the synthesized filler structures and the electrospun nanofibre morphologies. The fractions of free ions and crystalline phases of the as‐spun electrolytes were estimated by obtaining Fourier transform infrared and XRD spectra, respectively. The results showed a significant improvement in the ionic conductivity of the nanofibrous electrolytes by increasing filler concentrations. The highest ionic conductivity of 0.28 mS cm^?1 was obtained by the introduction of 0.49 wt% Co‐POM@Ru‐rGO into the electrospun electrolyte at ambient temperature. Compared with solution‐cast polymeric electrolytes, the electrospun electrolytes present superior ionic conductivity. Moreover, the cycle stability of the as‐spun electrolytes was clearly improved by the addition of fillers. Furthermore, the mechanical strength was enhanced with the insertion of 0.07 wt% fillers to the electrospun electrolytes. The results implied that the prepared nanofibres are good candidates as solvent‐free electrolytes for lithium ion batteries. © 2020 Society of Chemical Industry     

Optimal scheduling of single stage batch plants with direct heat integration

This paper addresses the multi-objective optimization problem arising in the operation of heat integrated batch plants, where makespan and utility consumption are the two conflicting objectives. A new continuous-time MILP formulation with general precedence variables is proposed to simultaneously handle decisions related to timing, product sequencing, heat exchanger matches (selected from a two-stage superstructure) and their heat loads. It features a complex set of timing constraints to synchronize heating and cooling tasks, derived from Generalized Disjunctive Programming. Through the solution of an industrial case study from a vegetable oil refinery, we show that major savings in utilities can be achieved while generating the set of Pareto optimal solutions through the ɛ-constraint method.     

Effect of focused ion beam sample preparation on the phase composition of zirconia

The investigation of phase transformations in metastable ceramic systems such as zirconia often requires local phase analysis within the areas of interest. Electron backscatter diffraction is a suitable method in combination with focused ion beam sample preparation. The interaction between ion beam and sample has to be carefully considered. In case of metastable Y-PSZ and Mg-PSZ, phase transformations were observed after FIB preparation with 30?kV, 30?nA and 5° incidence angle. Damage was the dominating effect for angles of 72°. The expected local temperature increase due to the ion bombardment with 30?kV and 30?nA is 700?K for ZrO₂. Thus, the observed phase transformations can be explained on the basis of the temperature increase in the corresponding Y-PSZ phase diagram. In case of Mg-PSZ, the transition temperature is 1083?°C. The local temperature increase was obviously lower. The excitation energy for the observed phase transformation was smaller than expected from the phase diagrams of the thermodynamic equilibrium. Using 5?kV, 4.8?nA and 5° incidence angle, no phase transformations and no damage were observed. Thus, these conditions are well suited for the FIB preparation of metastable zirconia.     

Polymers dynamics of the nonfluoro,nano-brush repelling agent with self-stratifying property in water-based coatings

While perfluoroalkyl acids (PFAAs), also known as C8s, are used extensively in textile repellent coatings, concerns have arisen for their carcinogenicity and hazardous effects on the environment. In this study, a novel water-based, nonfluoro, and nanobrush textile repelling agent was prepared by conventional sol–gel chemistry using amorphous fumed silica and n-octyltriethoxysilane as the starting materials. Minimal interaction between the designed repelling agent and marketed water-based resins was confirmed using linear viscosity region (LVR) analysis and asymmetric-flow field-flow fractionation (AF4), suggesting the self-stratification potential of the repelling agent. More specifically, the repelling agent exhibited excellent compatibility and self-stratifying ability with a force-emulsified acrylic-based resin, affording a water contact angle of 104.3° when incorporated at 7% solid content. Performance tests carried out on thermoplastic polyurethane (TPU) revealed excellent adhesion (100/100) of a final formulation, and a significant increase in water contact angle from 80.1° to 103.8° after treatment. In addition, the fouling area after the removal of a submerged sample from a mixture of slurry, polymer, and oil decreased from 48 to 1% when the repelling agent was added. Moreover, the sludge-fouling property remained unchanged after 1000 cycles of abrasion. These findings demonstrate the potential of the described nonfluoro, nanobrush repelling agent as an environmentally safe alternative for use with commercial resins, in turn realizing a fully water-based hydrophobic coating. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 48003.     

聚烯烃催化剂硅胶载体的制备和表征

采用并流共沉淀法制备了适用于聚烯烃催化剂的硅胶载体,为减少颗粒的聚集,在制备过程中添加一种表面活性剂。利用透射电子显微镜(TEM)、比表面积测定(BET)和X射线粉末衍射(XRD)法对制备的硅胶载体进行了表征;考察了在制备硅胶载体过程中原料硅酸钠溶液的浓度、溶液pH以及焙烧温度对产物硅胶载体的物理性能的影响。实验结果表明,硅酸钠溶液的浓度影响硅胶的初始粒子的大小,溶液pH直接影响硅酸钠的水解速率,焙烧温度影响硅胶的孔结构和比表面积。当硅酸钠溶液的浓度为0．2mol／L、溶液pH为8-9、反应温度为70℃、焙烧温度为700℃时,硅胶载体的BET比表面积为242．22m2／g、最可几孔径为16．45 nm、堆密度为0．492 1g/mL,与进口硅胶(Silica Gel 955)的物理性能相近。     

Encapsulation and Ostwald Ripening of Au and Au–Cl Complex Nanostructures in Silica Shells

We report a general template strategy for rational fabrication of a new class of nanostructured materials consisting of multicore shell particles. Our approach is demonstrated by encapsulating Au or Pt nanoparticles in silica shells. Other superstructures of these hollow shells, like dimers, trimers, and tetramers can also be formed by nanoparticle‐mediated self‐assembly. We have also used the as‐prepared multicore Au–silica hollow particles to perform the first studies of Ostwald ripening in confined microspace, in which chloride was found to be an efficient mediating ligand. After treatment with aqua regia, Au–Cl complex is formed inside the shell, and is found to be very active under in situ transmission electron microscopy observations while confined in a microcell. This aspect of the work is expected to motivate further in situ studies of confined crystal growth.