气相法聚乙烯高效催化剂的进展

综述了国内外气相法聚乙烯高效催化剂研究进展概况,以及各种新型高效催化剂制备技术和性能,并对开发我国新型高效推化剂提出了看法。     

脲醛树脂微胶囊包覆红磷阻燃剂制备工艺的研究 Ⅰ.预聚物合成工艺研究

研究了脲醛树脂的预聚物通过原位聚合对红磷进行包覆的一些影响因素。实验表明影响预聚物质量的主要因素是第一阶段尿醛比(F/U)1,第二阶段尿醛比(F/U)2,反应温度和pH值。制备预聚物的最佳条件为:第一阶段尿醛比为2.3∶1(摩尔比),第二阶段尿醛比为1.3∶1(摩尔比),pH值为5.1,反应温度为75℃。制备的预聚物来包覆红磷,颜色为白色;用微胶囊红磷阻燃聚乙烯,当含量为9%时,在500℃下残余物为4.85%。     

Poly(butylene terephthalate)/organoclay nanocomposites prepared by in situ interlayer polymerization and its fiber (II)

Intercalated nanocomposites with poly(butylene terephthalate) (PBT) incorporated between the montmorillonite layers were synthesized from dimethyl terephthalate and 1,4-butane diol by using an in situ interlayer polymerization. The PBT nanocomposites were melt-spun at different organoclay contents to produce monofilaments. The samples were characterized by using wide angle X-ray diffraction, electron microscopy, thermal analysis, and tensile testing. The extent of the clay layer in the PBT was confirmed by using X-ray diffraction and electron microscopy, and the clay layer was found to be highly dispersed on a nanometer scale. The addition of only a small amount of organoclay was enough to improve the thermo-mechanical properties of the PBT hybrid fibers. The hybrids were extruded with various draw ratios (DRs) to examine the tensile mechanical property of the fibers. At DR=1, the ultimate tensile strength of the hybrid fibers increased with the addition of clay up to a critical content and then decreased. However, the initial modulus monotonically increased with increasing amount of organoclay in the PBT matrix. When the DR was increased from 1 to 6, for example, the strength and the initial modulus values of the hybrids containing 3 wt% organoclay decreased linearly.     

Reversible addition fragmentation transfer (RAFT) polymerization of styrene in a miniemulsion: A mechanistic investigation

The RAFT polymerization of styrene in miniemulsion using 1-phenylethyl phenyl-dithioacetate (PEPDTA) as a RAFT agent was investigated, in attempt to reveal the mechanism for the often observed inferior performance such as low polymerization rate, broad molecular weight distribution and particle size distribution in the RAFT miniemulsion polymerization with regular levels of surfactant and co-stabilizer (1 wt% sodium dodecyl sulfate and 2 wt% hexadecane). It is strongly evident that a few of large oligomer particles consisting of oligomer, RAFT agent (RAFT agent refers to the original RAFT agent), and monomer would be formed in the early stage of the polymerization due to the superswelling of the first nucleated droplets. With the regular levels of surfactant and co-stabilizer, the observed low polymerization rate, broadened molecular weight distribution, slow conversion of the RAFT agent, lower N_p, and broadened particle size distribution could be well explained by the formation of these large oligomer particles and their prolonged existence. When the formation of the oligomer particles was suppressed by increasing surfactant and co-stabilizer levels and wise selection of types of RAFT agent, the molecular weight distribution could be narrowed to around 1.3 and particle size distribution could be close to that of the conventional non-living miniemulsion polymerization.     

DQ型高效催化剂在环管PP装置上的应用

介绍了使用DQ型球形高效催化剂在上海石油化工股份有限公司塑料事业部70kt/a环管连续法工业聚丙烯生产装置上应用研究的结果，并对结果进行了讨论。     

Electrosyntheses and characterization of poly(5‐bromoindole) in boron trifluoride diethyl etherate

Poly(5‐bromoindole) (PBrI) films were synthesized electrochemically by direct oxidation of 5‐bromoindole in pure boron trifluoride diethyl etherate. The oxidation potential of 5‐bromoindole in this medium was measured to be only 0.97 V vs. saturated calomel electrode, which was lower than that determined in acetonitrile + 0.1 mol L^?1 Bu₄NBF₄ (1.08 V). PBrI films obtained from this medium showed good electrochemical behavior and good thermal stability. Structural studies showed that the polymerization of 5‐bromoindole ring occurred at 2,3 position. As‐formed PBrI films were thoroughly soluble in strong polar solvent dimethylsulfoxide and partly soluble in tetrahydrofuran. Fluorescent spectral studies indicated that PBrI was a good blue‐light emitter. The excitation and emission spectra of PBrI showed a significant shift to longer wavelength compared with that of the monomer, consistent with the greater extent of electron delocalization. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 539–547, 2006     

Unipol气相法聚烯烃液体催化剂技术进展

介绍了Unipol气相法聚烯烃工艺液体催化剂的成分、加入反应器的方式和喷嘴结构及控制催化剂液滴尺寸方法等方面的最新进展情况。     

悬浮法合成聚丙烯腈高吸水性树脂

以偶氮二异丁腈为引发剂，用悬浮聚合法合成了交联聚丙烯腈，然后对其进行水解，得到了高吸水性聚丙烯腈。交联剂用量和水解条件对树脂吸水倍数的影响很大。树脂吸去离子水倍数为420倍，平均粒径为250μm。     

Olefins polymerization on titania and titania-supported rhodium

The adsorption of ethene and propene on titania and titania-supported rhodium has been studied, observing a continuous adsorption even after 24 h. The samples have been reduced at 623 or 773 K, but no difference was observed, whichever the reduction temperature or the presence of rhodium, on the amount of gas adsorbed per unit of surface area of the solid. A study of the polymerization has been done following the equal reactivity hypothesis, and it has been concluded that the role played by the rhodium particles is to facilitate adsorption of the gaseous molecule, that is then transfered to the surface of the support, where it polymerizes.     

IR study of the interaction of hydroxyl groups of silica gel with Cr species of Phillips' type catalysts

Spectroscopic evidence for the interaction of hydroxyl groups and chromium ions was obtained using a catalyst prepared from chromyl chloride. A new OH peak, observed at 3705 cm^–1 after pumping away CO gas, is attributed to the direct interaction of OH with the low-valent chromium. This peak shifts to 3590 cm^–1 on contact with O₂ at room temperature and it is assigned to a hydroxyl interacting with the oxidized chromium. New assignments are also proposed for IR bands of CO presorbed on the catalyst. The peak due to CO at 2188 cm^–1 decreases as the OH intensity at 3705 cm^–1 increases, suggesting that the former peak arises from adsorption on Cr(II) species to which two oxygen atoms are attached.