This paper studies a Kansas Department of Transportation welded plate girder bridge that developed fatigue cracks at small web gaps close to the girder top flange. Repair had been previously performed by softening the connection plate end with a slot retrofit, but cracks were recently found to have reinitiated at some of the repaired details and are again propagating. A comprehensive finite-element method study was performed to investigate the cracking behavior observed in the bridge and to recommend appropriate measures for future bridge retrofit. The analytical results show that stresses developed at the top flange web gaps could exceed yielding under the loading of an HS15 fatigue truck. The current slot repair used in the bridge was found to have introduced higher magnitude fatigue stresses in the web gap. To achieve a permanent repair of the bridge, it is recommended that a welded connection plate to flange attachment be used during future bridge retrofit. The web gap details should be able to withstand unlimited number of load cycles once this additional repair is performed.     

含V、N无缝钢管表面外折缺陷产生原因的分析

通过对鞍钢生产的部分批号V、N微合金强化无缝钢管及生产该钢管的原料连铸坯和连轧管坯的表面缺陷进行研究，分析了含V、N钢管表面外折缺陷的成因，提出了改善钢管表面质量的方法。采用改进后工艺生产的无缝管，其表面外折废品量大幅度降低。     

薄板坯连铸生产SS400钢工艺技术研究

对唐钢薄板坯连铸机生产的SS400钢的生产工艺进行了分析,认为薄板坯连铸机生产的SS400钢,在采取了精炼站在线定氧,将钢水全氧控制在25×10~(-6)左右,同时连铸采取保护浇注和轻压下等技术后,能够确保薄板坯连铸SS400钢的顺利浇注,轧制的板带材表面质量良好,机械性能符合要求。     

25Cr3Mo3NiNb二次硬化钢中的碳化物

利用TEM和萃取相分析方法，研究了25Cr3Mo3NiNb二次硬化钢淬火回火组织中的碳化物。结果表明，随淬火奥氏体化温度的升高，M6C型碳化物逐渐溶解。于1050℃奥氏体化时M6C型碳化物全部溶解，淬火态试样中只有少量的Nb(C，N)颗粒和自回火M3C型碳化物。随回火温度的升高，先后析出ε、M3C、M2C和M7C3等类型的碳化物。Nb(C，N)颗粒可以阻止淬火奥氏体晶粒的异常长大，而高温回火析出的M2C碳化物有二次硬化作用，从而提高回火稳定性和高温强韧性。     

爆炸焊接——热轧双相不锈钢复合钢板研制

本文主要阐述了通过爆炸焊接和热轧的方法,研制成功可焊性良好的且具有较好强度、韧性与综合性能的双相耐应力腐蚀的不锈复合钢板。还将热轧与热处理的两种试验作了较全面的常规、特殊检验试验,结果完全达到使用要求。     

Study on Hot Deformation Cracks of Steel D2 Using Procesing Map

ＳｔｕｄｙｏｎＨｏｔＤｅｆｏｒｍａｔｉｏｎＣｒａｃｋｓｏｆＳｔｅｅｌＤ２ＵｓｉｎｇＰｒｏｃｅｓｉｎｇＭａｐＧａｏＳｈａｎ，ＬｉｕＸｉａｎｇｈｕａ，ＷａｎｇＧｕｏｄｏｎｇＡＢＳＴＲＡＣＴＴｈｅｈｏｔｄｅｆｏｒｍａｔｉｏｎｂｅｈａｖｉｏｒｓｏｆｓｔｅｅｌ...     

Experimental and numerical investigation of fracture in double-edge notched steel plates

Double-edge notched (DENT) steel plates were pulled until complete fracture and several experimental observations were made (using profilometry and scanning electron microscopy). The essential work of fracture (EWF) model was found to be well verified. Numerical simulations—up to the maximum load only—of some experiments were performed using the finite element method (FEM), and incorporating geometric and material non-linearities (large deformation elasto-plasticity). Some experimental measurements were compared with the corresponding numerical computations and excellent agreement was found.     

PVDF中空纤维滤膜的形态结构

用Ｌ－Ｓ相转换法制备了聚偏氟乙烯（ＰＶＤＦ）中空纤维不对称滤膜。铸膜液由聚合物、溶剂和添加剂组成。用电子显微镜（ＳＥＭ）考察了聚合物浓度、添加剂用量及种类对膜形态结构的影响。实验结果表明，聚合物浓度对膜形态结构有显著影响，当铸膜液中聚合物浓度较低时，无论用什么种类添加剂，都能形成大、且多的孔，但孔的形状随添加剂不同而异。当恒定聚合物浓度时，添加剂的用量对膜形态结构有很大的影响，但孔的大小及多少与添加剂含量的多少不成正比。     

NH_4Cl水溶液在成膜过程中的致孔作用

本文以ＮＨ４Ｃｌ饱和水溶液做添加剂，对ＰＶＤＦ／ＮＭＰ体系在成膜过程中的致孔作用做了研究。铸膜液中随ＮＨ４Ｃｌ水溶液加入量的改变，膜孔径也发生变化，并出现最大值。通过Ｘ－射线衍射扫描发现制膜液中存在无机盐时膜中无定形态结构增加，表明无机盐的加入有助于膜孔形成     

简易炉外处理在电炉钢生产中的应用

阐述了小电炉采用投资少，见较快，简单易行的炉外处理措施，提高了钢质量和生产率，生产实践和应用结果表明，本措施可为同类型企业的炼钢工艺完善和技术进步提供参考。