表面稳定模式铁电液晶的电光特性测试

采用一种改进的高分子膜摩擦定向法成功地实现了表面稳定模式铁电液晶的光学双稳态，对比度大于１４０，响应时间达１００微秒。     

核孔膜生产线膜微孔制备工艺实验研究

本文介绍核孔膜生产线,重点描述了膜微孔制备工艺的实验研究。对于PC和PES膜,已得到32种工况下的扩孔公式,其形式为D=A+Bt,其中D——孔径,t——扩孔时间,A,B为特定工艺参数下的常数值.通过实验。得到了膜孔密度N与300~#核反应堆功率P、热柱辐照位置L的经验公式,即N=6.97×10~5×10~3×101~(1.18L).在本生产线上可生产最大幅面为3 140mm×240mm,孔径为0.04～10 μm的多系列多规格的核孔膜产品。     

High-temperature,high-pressure thermophysical measurements on liquid zinc

Wire-shaped zinc samples were resistively volume heated as part of a fast-capacitor discharge circuit. Time-resolved measurements with submicrosecond resolution of the current through the specimen, the voltage drop across it, and the thermal expansion of the specimen as a function of time allow determination of the enthalpy, electrical resistivity, and density at different temperatures up to superheated liquid states of zinc far above the normal boiling point. High static pressures, up to 3800 bar of the ambient medium water, were used. An estimate of the critical pressure for zinc is given by investigations of the stability of the sample with a framing CCD camera, taking pictures of different samples varying the ambient static pressure. The critical volume and the critical temperature are obtained by means of an extrapolation of measured data at different pressures.Paper presented at the Fourth International Workshop on Subsecond Thermophysics, June 27–29, 1995, Köln, Germany.     

富集孢粉化石的一种方法

本论述了孢粉，沟鞭藻化石与矿物颗粒相互分离的方法，并与传统的氢氟酸冷处理方法进行实验对比。结果表明，该方法摒弃有毒重液，提高了化石收获率。     

如何延长高压液相色谱柱的使用寿命

分析了液相色谱柱失效的诸多现象和原因，并论述了极性溶剂冲洗法等一些使色谱柱恢复活性的方法。     

热致液晶性纤维素衍生物及其热塑性塑料复合物熔体流变行为的研究

用毛细管流变仪研究了乙基纤维素（ＥＣ）及其高密度聚乙烯（ＨＤＰＥ）复合物，纤维素芳族酯（ＣＡＥ）及其聚碳酸酯（ＰＣ）复合物的剪切流变特性和机理。结果表明，ＥＣ对ＨＤＰＥ／ＥＣ复合物的粘度影响不大，而少量（５％）ＣＡＥ的加入使ＰＣ／ＣＡＥ复合物粘度大大下降，且复合物流变曲线呈现新的特征。     

Asymmetric alumina membranes electrochemically formed in oxalic acid solution

Alumina membranes were fabricated by anodizing aluminium metal in 0.15 M oxalic acid. The growth kinetics of the porous layer were investigated in the temperature range –1 to 16 °C using linear potential scans up to 70 V. The faradaic efficiencies of metal oxidation and of porous layer formation, determined by applying Faraday's law, were found to be independent of both temperature and electrical charge. SEM analysis of the metal-side and solution-side surfaces revealed different morphologies. After dissolution of the barrier layer in phosphoric acid, the metal-side surface showed circular pores whose size of about 90 nm was found to be uniform and independent of temperature. The pore population was also practically independent of temperature and a value of about 4 × 10¹³ pores m^–2 was determined. On the solution-side surface the presence of a deposit partially occluding the mouths of pores was observed. This coating could be removed by chemical etching in NaOH or thermal treatment at 870 °C, where decomposition of oxalate occurs. This supports the hypothesis that the deposit consists of an aluminium salt containing oxalate anions precipitated from the solution. The results show that it is possible to control the morphological characteristics of the anodic alumina membranes by careful choice of experimental conditions.     

Two dimensional deformation characteristics of bloom CC with liquid core reduction

A two-dimensional model was applied to simulate the liquid core reduction(LCR) technology of bloom CC using ANSYS software.The deformation characteristics of bloom under different liquid fraction and reducing amount are obtained.The results indicate that the main deformation condition of bloom shell is compressive strain,mainly undertaken by the liquid core,which increases with the enhancement of reducing amount.Solidified shell takes minor deformation.The longitudinal section of bloom appears sunken and the narrow side bulges,which grow serious when the liquid fractionincreases.     

高合金铁基烧结材料在轧钢导位中的应用研究

本文研究了高合金铁基烧结材料在轧钢导位中的应用。实验表明,通过粉末冶金液相烧结技术,可以获得具有优良综合性能的制品,材料密度ρ≥7.5 g/cm3,硬度≥55 HRC,抗弯强度≥1 000 MPa,冲击韧度αk≥3.9 J/cm2,满足了轧钢导位辊的工作要求。材料利用率可达95%以上、降低了制备成本。使用寿命是普通轧辊寿命的3~6倍,适用于线材和小型型材的轧钢生产。     

铸件浸渗系统脱液机故障树的建立和分析

利用FTA方法对脱液机的各种故障进行系统分析,建立了脱液机的故障树,并对故障树进行定性分析.找出了影响脱液机可靠性的主要因素,提出了提高脱液机可靠性的相应措施.