用四氯化钛制备TiO2微球的研究

以阳离子交换树脂为模板，以四氯化钛为原料采用溶胶．凝胶法制备了TiO2微球，并通过X射线衍射（XRD），红外光谱（FTIR），扫描电子显微镜（SEM）等手段对样品进行了表征。结果表明：制备的多层结构的TiO2微球直径在300μm-700μm之间，微球主要组分为锐钛矿晶型的TiO2，晶粒粒度约为16．3nm。分别以300W高压汞灯和太阳光为光源进行光催化实验，研究了样品对10mg／L甲基橙溶液光催化氧化的效果，结果表明此种TiO2微球具有很好的光催化性能。     

Corrosion of Three Commercial Steels Under ZnCl2 –KCl Deposits in a Reducing Atmosphere Containing HCl and H2S at 400–500°C

The corrosion of three commercial steels in a reducing atmosphere containing HCl plus H₂S in the presence of ZnCl₂–KCl deposits has been investigated at 400–500°C and compared with the corrosion of the same materials in a similar gas mixture free from H₂S. The presence of H₂S in the gas accelerated the corrosion of the three commercial steels beneath ZnCl₂–KCl deposits. All materials suffered from severe corrosion with partial detachment and spalling of the external scales. Degradation of the steels resulted from the penetration of chlorine-containing species through the scale formed initially down to the metal matrix, because chorine-rich species were detected close to the alloy/scale interface. Although the corrosion resistance generally increased with increasing Cr content, even the high-Cr stainless steel SS304 is still unable to provide good corrosion resistance against the ZnCl₂–KCl deposits in the presence of H₂S due to the bad adherence of the scales to the alloy. The mechanisms of attack are discussed on the basis of thermodynamic considerations and of the active-oxidation model.     

Studies concerning the effect of nitrogen on the oxidation behavior of TiAl-based intermetallics at 900°C

The oxidation behavior of the titanium aluminides Ti-50Al and Ti-48Al-5Nb has been investigated in Ar+20%O₂ and in air at 900°C. Thermogravimetric studies in combination with structural analyses using optical metallography, SEM/EDX and X-ray diffraction show a marked influence of nitrogen on the composition and growth rate of the oxide scales. For a more detailed study concerning the effect of nitrogen on the scale-growth kinetics, thermogravimetrical analyses were carried out during which the gas atmosphere was changed from air to Ar–O₂, and vice versa, without intermediate cooling of the specimen. The results show, that nitrogen adversely affects the formation of the initially formed alumina scale and that it enhances the growth rate of the rapidly growing Ti-rich oxide. This effect was observed in both alloys investigated, although the thermogravimetric results at first sight indicated an opposite effect for the Nb-containing alloy. This apparent contradiction is caused by internal oxidation which occurs in this alloy during exposure in Ar–O₂.     

Nb_2O_5-MnO-SiO_2渣中Nb_2O_5和MnO活度的研究SCIEI

本文利用含NbFe液与Nb_2O_5-MnO-SiO_2渣之间平衡,在1828K温度下应用固体电解质浓差电池方法测定了Fe液中氧的活度,从而计算出渣中Nb_2O_5及MnO的活度,并绘制了Nb_2O_5-MnO-SiO_2三元系的等α_(Nb_2O_5)和等α_(MnO)图。     

High temperature oxidation of a (Cr2N−Mo2S3)/Cr double-layered coating deposited on steel by D.C. magnetron sputtering

A coating consisting of (Cr₂N−Mo₂S₃) overlay coating and an underlying Cr coating was deposited on a steel substrate by D.C. magnetron sputtering. The oxidation characteristics of the deposited double-layered coating were studied at temperatures ranging from 400 to 900 °C in air. The oxidation product was primarily Cr₂O₃. The unreacted coating beneath the oxide scale had some dissolved oxygen, sulfur, and iron. Oxidation of the coating occurred via complex routes such as the outward diffusion of chromium and nitrogen from Cr₂N and iron from the substrate, and the inward transport of oxygen from air, chromium from Cr₂N, and S from Mo₂S₃. This counter diffusion of various ions occurred easily via fine crystallites that constituted the coating, which had some solubility of S, O, and Fe.     

表面修饰TiO2光催化薄膜的表征

利用射频磁控溅射技术，以Ar和O2气混合气体为溅射气体在载玻片上制备了锐钛相TiO2薄膜。为了提高Ti02薄膜的光催化活性，在TiO2薄膜表面进行了钽修饰。利用X射线衍射(XRD)，原子力显微镜(AFM)和UV-VIS-NIR分光光度计等技术对薄膜进行了表征。结果表明：对TiO2薄膜的表面进行适量的Ta元素修饰可以提高其光催化活性。     

电沉积法制备Ni-Ti3SiC2复合镀层

以自制纯度超过98%(体积分数,下同)的Ti3SiC2陶瓷粉体为原料,加入分散剂和表面改性剂,制成稳定悬浮液,并加入Watts镀镍电镀液,利用磁力搅拌分散均匀,在阴极电流密度2 A/dm2～5 A/dm2下,在低碳钢基体表面成功得到Ni-Ti3SiC2减摩复合镀层.SEM观察表明,表面改性剂的加入有效地改变了粉体表面电导性质,得到致密平整的复合镀层结构.XRD及EDS分析表明:镀层中Ti3SiC2微粒含量为5%～14%(体积分数,下同).当制备过程中以间歇式搅拌代替连续搅拌时,可得到Ti3SiC2相含量超过30%的复合镀层.复合镀层的显微硬度随微粒含量的升高而增大.     

纳米晶Bi2Se3-Sb2Se3薄膜的SILAR法制备及表征

采用连续离子层吸附反应(SILAR)法,分别用含有Se2-,Bi3+和Sb3+的离子溶液作为独立的阴、阳离子前驱溶液,以载玻片为衬底,在室温下沉积出致密且具有镜面金属光泽的Bi2Se3-Sb2Se3薄膜材料.为了改善薄膜样品的结晶状态,对其进行了退火处理.用AFM观察了薄膜样品的表面形貌,用XRD分析了退火前后薄膜样品的结晶状态.结果表明薄膜样品经200℃较低温度下退火处理4 h以后,薄膜的结晶状态由无定形态转化为多晶态,其平均晶粒尺寸为30 nm～40 nm.     

含H2S/CO2环境中缓蚀剂对不同油管钢的缓蚀作用

选用一种自制缓蚀剂TG500(主要成分为咪唑啉含硫衍生物、有机硫代磷酸酯),对不同油管钢在含H2S/CO2腐蚀介质中进行试验。结果表明:TG500可明显降低溶液对N80、SM80SS、KO80SS油管钢的腐蚀速率,即使在较高的CO2/H2S分压下,缓蚀效率仍可达95%以上;油管钢中的合金元素Cr、Ni对于降低油管钢的腐蚀速率具有明显作用,但对于提高缓蚀剂的缓蚀效率无明显作用。     

REACTIVE DIFFUSION BETWEEN Si AND NbC AT 1300℃

ＲＥＡＣＴＩＶＥＤＩＦＦＵＳＩＯＮＢＥＴＷＥＥＮＳｉＡＮＤＮｂＣＡＴ１３００℃Ｃ．Ｒ．Ｋａｏ（ＤｅｐａｒｔｍｅｎｔｏｆＣｈｅｍｉｃａｌＥｎｇｉｎｅｅｒｉｎｇＮａｔｉｏｎａｌＣｅｎｔｒａｌＵｎｉｖｅｒｓｉｔｙＣｈｕｎｇＬｉ，Ｔａｉｗａｎ）Ｊ．Ｗｏｏｄｆ...