Thermal and thermoelastic properties of fast extrusion furnace (FEF) carbon black loaded SBR vulcanizates

The effect of FEF carbon black as filler on the thermal capacity c, diffusivity a, and thermal conductivity λ, of styrene butadiene rubber (SBR) composites in the temperature range 300–420 K was studied. The filler strongly increases the thermal diffusivity, whilst strongly decreasing the thermal capacity and the thermal conductivity (except at high FEF content ≥80 phr). The influence of the filler on the thermoelastic behaviour of the same composites was also investigated. It was found that the thermoelastic temperature change (ΔT) increased with carbon black concentration as well as the entropy change per unit extension.     

Influence of the surface conditions on permeation in the deuterium–MANET system

The condition of the surfaces is of crucial importance for the deuterium permeation through materials. In this work a study of the surface constants for the adsorption (σk₁) and release (σk₂) of deuterium under different surface conditions on the martensitic steel DIN 1.4914 (MANET) has been carried out. The growth of an oxide surface layer (Cr₂O₃) of about 25–30 nm in a MANET sample, heat treated in an oxidizing environment, compared to the bare MANET that have a ‘natural' oxide of about 5 nm has provoked a reduction of both the permeation rate and the recombination coefficient (about 3 orders of magnitude). In addition, the permeation governing process has changed from diffusion-limited to surface-limited. The measurements of the permeation rate of deuterium were performed by a gas-phase permeation technique over the temperature range 574–746 K and for deuterium driving pressures in the range from 3 to 10⁵ Pa.     

浸胶工艺对Nomex蜂窝性能的影响

本文研究了浸胶工艺对Ｎｏｍｅｘ蜂窝性能的影响，分析探讨了提高Ｎｏｍｅｘ蜂窝性能及外观质量的途径。研究结果表明：采取新的浸胶工艺制作的Ｎｏｍｅｘ蜂窝，各项性能全面达到法国宇航材料标准。     

Characterization of ultrafine La x Sr1−x MnO3 powder prepared by spray pyrolysis

The characterization of La _x Sr_1−x MnO₃ powders produced by spray pyrolysis using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observation, specific surface area (Brunauer-Emett-Teller), and particle size distribution measurements shows that the resultant large particles are loose agglomerates consisting of many small particles. However, the sintered tiny particles can form hard agglomerates, and the particle size increases remarkably. The structures of the powders before and after sintering were identified by x-ray diffraction (XRD). The study of the electrical property of the powder shows that the powder is a metallic conductor. In a reducing atmosphere, the powder can be decomposed. When the powder is cofired with yttria-stabilized zirconia 5% (YSZ) powder at 1200 °C for 5 h, no new phase is produced, and the powder remains a single provskite hexagonal-rhombohedral structure.     

碳纳米管及稀土元素钇(Y)对高Ni含量Ti(C,N)基金属陶瓷组织与性能的影响

研究了不同含量的碳纳米管及0.8%稀土Y对高Ni含量Ti(C,N)基金属陶瓷组织性能的影响.将不同成分的试样分别于1400℃、1410 ℃、1420℃真空烧结,测试抗弯强度、洛氏硬度,观察背散射电子形貌、断口形貌并做能谱分析.结果表明,加入质量分数(下同)为0.8%Y及0.3%～1.0%的碳纳米管时,碳纳米管含量为0.5%的组织较均匀,芯壳结构明显,抗弯强度及硬度均较高.     

CR／MMA乳液接枝共聚物的研制

用乳液接枝共聚法制备ＣＲ／ＭＭＡ共聚物，讨论ＣＲ乳液、引发剂、接枝温度、ＭＭＡ用量对接枝共聚转化率，接枝ＭＭＡ含量、ＭＭＡ接枝效率和粘接性能的影响，用红外光谱对接枝共聚物进行表征，该共聚物具有较好的粘接性能。     

木材用交联型醋丙胶粘剂的研制

研制一种由醋酸乙烯、丙烯酸丁酯、特种单体共聚而成的水性交联型环保胶粘剂以替代目前广泛使用的氨基树脂,适应绿色环保要求。     

Zinc Coated Steel/Epoxy Adhesive Systems: Investigation of the Interfacial Zone by FTIR Spectroscopy

The present study takes advantage of the ability of Fourier Transform Infrared Spectroscopy (FTIR) for the analysis of ultrathin organic films on metals. FTIR in the reflection mode (IRRAS) is used in order to study the interaction of ultrathin films of dicyandiamide (hardener of most one-pack epoxy resins) with various substrates, model ones such as gold or zinc and industrial ones such as steel and zinc-coated steels.

Pure zinc surfaces and, to a lesser extent, zinc-coated steels are shown to react with dicyandiamide after heating at 180°C, as evidenced by the frequency shift of the absorption band (at about 2200 cm^-1) characteristic for nitrile groups. As real systems consist of thick layers of a fully formulated adhesive cured onto a metallic substrate, the direct investigation of such a buried interphase is no longer possible by FTIR and by most of the known spectroscopies. Some mechanically tested specimens are then analysed, after failure, by FTIR microspectrometry. The spectra obtained, corresponding to the fracture initiation zone which is about 100 μm in diameter, advocate for the presence of an ultrathin layer of modified polymer still covering the substrate.