Effects of phosphorus addition on the magnetic properties of sintered Fe-50 wt.% Ni alloys

Phosphorus was added to Fe-50 wt.% Ni in the form of a coated composite powder via an electroless plating process. Addition of phosphorus to Fe-50 wt.% Ni facilitated increases in density and grain size, both of which were beneficial to magnetic performance. Because of the homogeneous distribution of phosphorus in the powder, the optimal phosphorus addition was much lower than for those using Fe₃P as the phosphorus precursor. The optimal phosphorus addition was close to its maximum solubility in Fe-50 wt.% Ni (about 0.5 wt.%), above which precipitation of excessive phosphorus in the form of iron nickel phosphide, (Fe,Ni)₃P, effectively degraded the magnetic properties of Fe-50 wt.% Ni. Without the addition of phosphorus, good magnetic properties could be achieved only when the sintering temperature was high enough (>1200 °C) to result in a high sintered density and large grains in the sintered structure.     

卡尔曼滤波分光光度法同时测定钛锡钼钨

以两性表面活性剂溴化十六烷基二甲基氨基乙酸作为新增效试剂，研究了钛、锡、钼、钨邻氯苯基荧光酮显色体系的光度性质，并用卡尔曼滤波分光光度法进行同时测定。合成试样中钛、锡、钼、钨的回收率范围及相对标准偏差分别为９６．２％～１０６．３％、９６．７％～１０４．５％、９２．２％～１０７％、９７．７％～１０５．６％和３．７６％、３．２４％、５．０９％、２．８１％；合金钢样中微量钛、锡、钼、钨测定的相对误差为５．０％～１１．８％。     

Nickel Electroplating

NICKEL ELECTROPLATING has been practicallyused for decades.There is an unknown part in theplating,although this is easy to plate.Applications ofthe plating are described from the practical viewpoint.Purpose of Nickel Electroplating(1)Decorative,and corrosion resistanceNickel electroplating is deposited on iron,cupper,zinc and aluminum substrate etc.,and chromiumplating is usually deposited on nickel plating.Hexavalent chromium plating has an important effecton the corrosion resisitan…     

Initial stages of tin electrodeposition from sulfate baths in the presence of gluconate

Tin electrodeposition in its initial stages in acid sulfate/gluconate baths was studied with varying tin and gluconate concentrations using potential-controlled electrochemical techniques. The deposit morphology was observed by scanning electron microscopy (SEM). A comparison with tin electrodeposition from acid sulfate baths in the absence of gluconate was also carried out. Use of a highly acidic bath leads to nonuniform deposits, even in the presence of gluconate; at pH 4 deposits are uniform, brilliant and suitable for finishing applications. Tin crystallites have a well defined morphology which depends on bath agitation conditions. In the absence of agitation, the crystallites have the same tetragonal shape as in a sulfate bath without gluconate.     

换热器表面预处理及防腐工艺

石化换热器许多设备都由碳钢制作,需要涂镀渗防腐,为保证防腐层质量,需要进行严格的表面预处理。概述了机械与化学表面预处理及相关的防腐工艺。     

有机锡化合物引发D,L-丙交酯的开环聚合

D,L-丙交酯在有机锡化合物四苯基锡(Ph4Sn)、三正丁基醋酸锡(Bu3SnOAc)、辛酸亚锡(SnOct2)等催化剂引发下开环聚合,得到高分子量的聚D,L-乳酸,讨论了聚合单体D,L-丙交酯纯度、聚合温度、聚合时间、聚合体系真空度以及引发剂有机锡催化剂与聚合单体D,L-丙交酯的比例对聚D,L-乳酸合成的影响,通过红外光谱和核磁共振光谱对聚D,L-乳酸的结构进行了表征。实验结果表明,D,L-丙交酯开环聚合反应的较佳工艺路线是:D,L-丙交酯重结晶5次,聚合温度140℃,聚合时间24 h,聚合体系真空度13.3~133.3 Pa,引发剂有机锡催化剂与单体D,L-丙交酯比例0.2‰~0.5‰,此时聚D,L-乳酸的粘均分子量最高,分别达到32.46×104,33.43×104和41.36×104。     

连续电镀锌镍合金的研究

提出了一种高氯化铵弱酸型镀液体系连续电镀锌镍合金工艺，研究了m(Ni^2 )/[m(Ni^2 ) m(Zn^2 )]、氯化铵浓度，电流密度、温度、PH值对镀层镍含量的影响，推导出连续镀的镀速计算公式，采用此工艺可获得外观良好、镍含量在13％－15％的锌镍合金镀层。     

化学镀Ni-P合金工艺的研究

本文研究了以硫酸镍作为主盐、次磷酸钠为还原剂的酸性化学镀镍磷合金工艺，并通过实验详细分析了主盐和还原剂、络合剂、催化剂、温度、pH值、前处理、亚磷酸钠等因素对化学镀镍磷合金工艺的影响，找出了最适合的镀浴配比和组成以及最佳的操作务件。     

光亮镀镍液pH值计算机控制系统

光亮镀镍液的ｐＨ值控制得稳定否，对于镀层质量有重要的影响，本文介绍了在电镀生产过程中，对镀镍液的ｐＨ值进行自动控制的一个计算机系统，该系统在广州五羊自行车厂电镀车间投入使用后，镀件质量有了明显的提高。     

脉冲电流对锌酸盐镀锌层的影响