不同线密度粘胶原丝及其碳纤维的结构性能对比

用Weibull分析处理 10mm长的 4种不同线密度粘胶原丝和相应碳纤维的单丝断裂强度 ,得到原丝线密度、强度分布和碳纤维强度的对应关系。采用透射电镜 (TEM )和小角X散射 (SAXS)分析粗旦原丝 ,发现孔洞较多 ,并存在大于 70nm的大孔洞。截面和表面照片也揭示出细旦原丝截面相对规整 ,表面较光滑 ,粗旦原丝则反之。结果表明 ,原丝线密度小 ,截面形状圆整 ,缺陷少 ,所制得的碳纤维强度高。     

Isosteric heat of sorption of CO2 in poly(ethylene terephthalate)

Sorption isotherms for carbon dioxide in poly(ethylene terephthalate) have been measured at 35–55°C. The isotherms were measured gravimetrically on a Mettler Thermoanalyzer-1 from vacuum to 1 atmosphere. The sorption data were used to generate sorption isotherms from which the isosteric heat of sorption of CO₂ in PET was determined. At 45°C the isosteric heat of sorption increases from −10 kcal/mole at a concentration of 0.5 cm³ (STP)/cm³ (polymer) to −8 kcal mole⁻¹ at a concentration of 1.5 cm³ (STP)/cm³ (polymer). It has been reported in the literature that the isosteric heat of sorption for this system decreased through a minimum before increasing with increasing concentration. Our measurement of the low-pressure sorption isotherms shows that this is not the case.     

Intergranular oxidation of silicon in 20Cr-25Ni niobium-stabilized stainless steel at 1140–1230 K

The kinetics of intergranular oxidation of silicon in a 20Cr-25Ni Nb-stabilized stainless steel are reported, at temperatures in the range 1140–1230 K, in CO₂ at 40 bar pressure. The depth of attack increased parabolically with respect to time, with an activation energy of 335±30 kJ/mol. The mechanism of growth is discussed in terms of classical internal-oxidation theories, and an alternative explanation based on an available-space theory is developed. The internal oxidation rates in a number of different alloys are compared with diffusivities of metals in the base alloy. It is proposed that intergranular oxidation in the 20–25 Nb steel is controlled by the rate of outward diffusion of iron or chromium in the alloy.     

基于脱钩模型的新疆碳排放与经济增长的关系研究

在共建丝绸之路经济带以及生态文明的大背景下,新疆作为丝路经济带的核心区与中国西部重要的桥头堡,其经济发展的速度与效益值得关注。尤其新疆是我国重要的能源资源储备区,如何协调好能源开发过程中的碳排放与经济增长之间的关系,是当前摆在我们眼前的一大课题。本文旨在通过脱钩模型分析新疆碳排放与经济增长之间的关系,得出新疆碳排放与经济增长总体上呈现弱脱钩的结论,据此分析弱脱钩状态产生的原因,并提出了有针对性的对策建议,以期促进新疆经济能更好的适应经济新常态。     

40Cr钢渗氮过程中碳原子的迁移

将正火４０Ｃｒ钢样在不同温度下进行不同时间的气体渗氮，对其横断面进行波谱分析，发现渗氮前沿附近自始至终存在着典型的贫碳区，其两侧为富碳区，透射电镜分析结果表明，碳原子的重新分布包括碳化物的回溶、碳的扩散及碳化物长大三个过程。     

低碳低合金铸钢力学性能的研究

利用Olympus光学显微镜、扫描电镜(SEM)及能谱分析(EDAX)探讨了等温淬火工艺对低碳低合金CrMnSi铸钢力学性能的影响,并通过XRD定量分析了相的组成.结果表明,合适的等温淬火工艺,可获得一定数量的贝氏体和残余奥氏体(约6%)的复合组织,冲击断口形貌由解理刻面变为韧窝状,铸造成形无缺口试样(10 mm×10 mm×55 mm)的冲击韧度由ακ≤30 J/cm2增加至ακ≥170 J/cm2,硬度HRC≥40,具有较高硬度和冲击韧度的配合.     

碳含量对Ti(CN)基金属陶瓷力学性能的影响

研究了Ti(CN)基金属陶瓷的碳含量对其物理力学性能的影响。结果表明 ,在一定范围内 ,随着碳含量的减少 ,Ti(CN)基金属陶瓷的矫顽磁力、钴磁和硬度降低 ;而抗弯强度则明显增高。     

连续碳分CO2吸收率分析及探讨

本文简述了CO2 气体吸收率的测定原理 ,着重分析了影响连续碳分CO2 气体吸收率的因素 ,提出了提高连续碳分CO2 气体吸收率的途径     

活性炭吸附硫脲溶液中的金离子之形态

由实验得出活性炭从硫脲溶液中吸附金的特点,根据络合化学原理找到溶液中被吸附离子形态是AuTu~+,AuTu_2~+和Au~+,并解释了实验现象。     

葵花盘基炭材料对三硝基苯酚的吸附性能

首先对提取果胶后的葵花盘进行炭化,然后用蒸馏水在800℃条件下活化,制得炭材料800SP-W。800SP-W的比表面积可以达到389.72 m~2·g~(-1)。研究了炭材料对三硝基苯酚的吸附性能,800SP-W对三硝基苯酚的吸附在140 min达到平衡,吸附量为95.57 mg·g~(-1)。三硝基苯酚在800SP-W上的吸附行为服从一级动力学模型。800SP-W对三硝基苯酚的吸附符合Langmuir和Freundlich吸附模型,为单分子层吸附。