场激活加压燃烧合成WC-Ni复合材料的工艺参数研究

以钨、碳和镍为原料,在电场激活下,材料的燃烧合成和致密化同时进行,短时间内完成了碳化钨镍复合材料的制备。研究了场激活 加压燃烧合成中的工艺参数,如脉冲电流、能量控制模式、升温速率、最高温度和压力对反应的影响。测量了在反应合成和致密化前后的样品 收缩率。所制备的复合材料的相对密度,490N载荷下Vickers硬度和断裂韧性分别为99.2%,13.965GPa和5.9MP·m1/2。     

西霞院水利枢纽工程泄洪闸振冲碎石桩基础处理

通过西霞院水利枢纽工程泄洪闸振冲碎石桩基础处理施工方法论述,给出了加砂层振冲碎石桩施工造孔水压、水量、成孔速度、填料级配、填料方法以及振密电流值、留振时间等施工控制参数。     

蓝湿皮酶软化的特性研究

以自行研制的一种复合酶为软化剂 ,研究了 p H值、反应温度、反应时间、酶用量以及铬含量对猪蓝湿皮软化效果的影响 ,其软化效果以软化液中羟脯氨酸的浓度增量来表征。研究结果表明 :通过蓝湿皮软化来改善成品革的质量是可行的 ,而且有明显的效果 ;以软化液中羟脯氨酸的浓度来表征软化效果是一个有效的方法 ;当用该复合酶软化猪蓝湿皮时 ,最适 p H值范围为 6 .0 - 6 .5 ;反应温度在 4 0 - 6 5℃之间时 ,软化效果随温度的升高而增大 ;在 5 5℃条件下 ,该酶有很好的热稳定性 ,能长时间保持活力不衰减 ;最适酶用量为 30 0 U/ g试样 ;蓝湿皮的铬含量对软化效果有影响 ,用该方法处理的蓝湿皮 ,其铬离子质量含量一般应≤ 2 .5 %。     

A new colloidal precursor cooperative conversion route to nanocrystalline quaternary copper sulfide

A novel milk-like Cu-thiourea colloid has been synthesized. Nanocrystalline quaternary copper sulfide Cu₂FeSnS₄ was obtained through the Cu-thiourea colloidal precursor cooperative conversion route at low temperature. The samples were characterized by means of X-ray powder diffraction, transmission electron microscopy, scanning electron microscopy, inductively coupled plasma atomic emission spectroscopy, and X-ray energy dispersive spectroscopy techniques. The reaction details and features were described and discussed.     

The reaction of ceria coatings on mica with H2S: An in-situ X-ray diffraction study

Thin layers of ceria were deposited on the surface of mica platelets in solution. The reaction of such particles with hydrogen sulfide yields a red colored special effect pigment. The ceria layer reacts with H₂S to produce a variety of sulfide and oxysulfide phases. The reaction path discovered in situ by time and temperature resolved X-ray diffraction is CeO₂→CeS₂→C-Ce₂S₃→Ce₁₀S₁₄O. The reaction itself is extremely variable depending on gas flow, heating rates and decomposition atmospheres. Effects on the thin film are recorded by scanning electron microscopy (SEM) and revealed a destruction of the layer once red Ce₁₀S₁₄O was formed. The product layer then reveals the typical nonwetting behaviour of a liquid on a surface.     

A comparative study of the gas sensing behavior of nanostructured nickel ferrite synthesized by hydrothermal and reverse micelle techniques

A comparative study of gas sensing behavior of nanocrystalline nickel ferrite synthesized by micro-emulsion and hydrothermal method to liquefied petroleum gas (LPG) is presented. Nanocrystalline nickel ferrite synthesized by hydrothermal method indicated higher electrical conductivity and gas sensitivity at low operating temperature compared to nanocrystalline nickel ferrite synthesized by reverse micelle technique. This difference in the gas sensing behavior can be attributed to the presence of more oxygen vacancies (i.e. non-stoichiometry) in the hydrothermally synthesized nickel ferrite. Incorporation of palladium had a catalytic effect and the operating temperature was significantly reduced in both the samples. The higher operating temperature of the reverse micelle nickel ferrite material makes the sensor response speed faster (∼10 s) compared to the hydrothermally synthesized material (∼1 min).     

Electrical conductivity and gas sensitivity of Zn-Sb-O thick films

The thick film of Zn-Sb-O was prepared by coating the paste of nanoparticles mixture (Sb₂O₃:ZnO=1:3) on the alumina substrate, followed by sintering at 500-900 °C for 2 h in air. The electrical resistance and gas-sensing properties to benzene, alcohol and acetone of Zn-Sb-O films were found to be dependent on the change of phase structure caused by sintering temperature.     

The Influence of Ir and Pt Addition on the Synthesis of Fullerenes at Atmospheric Pressure

The addition of metallic Ir and Pt to a fullerene-forming, atmospheric-pressure plasma reactor was found to influence the generation of carbonaceous products. It was observed that the added metals were efficiently dispersed into the plasma and that their presence increased the yield of fullerenes. The addition of Ir led to a noticeable shift in the fullerene distribution towards C₆₀, whereas the addition of Pt increased the proportion of C₆₀ oxides and decreased the proportion of higher fullerenes. Addition of Ir also caused a reduction of the soot particle size and the formation of a considerable quantity of carbon nanotubes.     

聚苯硫醚复合涂层的耐磨性能

研究了用固体润滑石墨、碳化硅、二硫化钼等填料改性的聚苯硫醚 (PPS)涂层的耐磨性能。实验结果表明 ,聚苯硫醚复合涂层具有优良的耐磨性 ;加入适量 ( 3 0 % )的石墨、碳化硅等固体润滑剂 (石墨 :碳化硅 =2∶3 ) ,可以有效提高涂层的耐磨性能 ,而二硫化钼和三氧化二铬的减摩效果更佳     

利用铝（100）面隧道孔制备纳米模板及有序阵列材料

高纯铝箔通常通过电化学扩面后用作铝电解电容器的阳极材料。利用铝箔（100）面隧道孔制备纳米模板。这种纳米模板的特点是制作简单、模板面积大，纳米阵列材料形状可控性强。还利用两步电化学侵蚀铝箔的特殊工艺，研制出纵横交错的TiO2纳米有序阵列材料。