稀土变质剂对铸造铝合金性能的影响

采用正变试验法，探讨了稀土变质剂对铸造结合金ZL102性能提高的可行性．试验选用了不同的稀土添加量，考察了不同的变质时间及热处理制度对ZL102的强度、硬度、流动性以及重熔性等性能的综合影响规律．试验表明，稀土是铸造铝合金的优良变质剂，并且添加单一稀土的变质效果优于混合稀土．     

Li2O在保护渣中的作用

采用在不同玻璃性的两种基渣中加入Ｌｉ２Ｏ为研究Ｌｉ２Ｏ对保护渣粘度，熔化温度及玻璃性能的影响，并对Ｌｉ２Ｏ改善保护渣玻璃性的机理进行了探讨，提出了寻找高速连铸保护渣中Ｌｉ２Ｏ的代用物的一种方法。     

用过滤工艺全面提高铸锭质量

探讨了过滤器孔径对6063铝合金铸锭组织和性能的影响规律。在此基础上指出,在过滤工艺恰当时,不仅可以减少铸锭中的夹杂物,而且可以有效地防止裂纹、羽毛晶等连续铸锭中的常见缺陷。     

奥钢联板坯连铸计算机系统升级研究

某钢厂板坯连铸过程控制系统采用的奥钢联(VAI)技术,运行数年来,由于模型不透明,维护和调整困难,迫切需要升级改造。改造后的计算机系统充分考虑现有资源和需求,能够达到升级改造的目的。     

Fast dynamic casting

We describe a scheme for implementing dynamic casts suitable for systems where the performance and predictability of performance is essential. A dynamic cast from a base class to a derived class in an object‐oriented language can be performed quickly by having the linker assign an integer type ID to each class. A simple integer arithmetic operation verifies whether the cast is legal at run time. The type ID scheme presented uses the modulo function to check that one class derives from another. A 64‐bit type ID is sufficient to handle class hierarchies of large size at least nine levels of derivation deep. We also discuss the pointer adjustments required for a C++ dynamic_cast. All examples will be drawn from the C++ language. Copyright © 2005 John Wiley & Sons, Ltd.     

板坯连铸涡流检测钢水液位系统的应用

介绍了新一代RAM型涡流传感钢水液位控制仪在莱钢板坯连铸机上的应用及其效果。     

双辊薄带钢连铸在线自动检测系统

介绍了双辊薄带钢连铸工艺,设计了双辊连铸机的计算机在线自动检测系统,通过采取正确的抗干扰措施提高了检测的精度,系统在双辊薄带钢连铸试验中应用效果良好.     

连铸温度场数值模拟及冷却水参数优化

由于用实验方法来研究工艺参数对铸坯温度场的影响较困难,故而提出了一种在冶金冷却条件指导下的启发式GA(遗传算法)数值模拟优化方法,为优化工艺参数提供了理论依据,并在优化基础上采用MIMO(多输入多输出)系统PID(比例积分微分)控制器实现了二冷段配水的优化控制,改善了铸坯的质量.     

Centrifugal Casting of High Speed Steel/Nodular Cast Iron Compound Roll Collar

Ｈｉｇｈ ｓｐｅｅｄｓｔｅｅｌ (ＨＳＳ) ,ｉｓｃｈａｒａｃｔｅｒｉｚｅｄｂｙｅｘ ｃｅｌｌｅｎｔｈａｒｄｎｅｓｓ ,ｗｅａｒｒｅｓｉｓｔａｎｃｅ ,ａｎｄ ｇｏｏｄｒｅｄｈａｒｄｎｅｓｓ .Ｒｅｃｅｎｔｌｙ ,ＨＳＳｉｓａｐｐｌｉｅｄｔｏｍａｎｕｆａｃｔｕｒｅｈｏｔｒｏｌｌｉｎｇｒｏｌｌｓｔｏｐｒｏｄｕｃｅｓｔｒｉｐｓｏｆｇｏｏｄｓｈａｐｅａｎｄｓｍａｌｌｃｒｏｗｎｗｉｔｈｅｘｔｅｎｄｅｄｒｏｌｌｓｅｒｖｉｃｅｌｉｆｅ[1,2 ] .ＴｈｅＨＳＳｉｓａｐｐｌｉｅｄｔｏｍａｎｕｆａｃｔｕｒｅｒｏｌｌｃｏｌｌａｒｆｏｒ…     

Durability of hygrothermally aged graphite/epoxy woven composite under combined hygrothermal conditions

The objective of this study was to examine the effects of hygrothermal aging on the durability of a graphite/epoxy woven composite material system. The study was part of a larger project in which the objective was to evaluate and model the effects of moisture, temperature, and combined hygrothermal conditions on the strength and life of a graphite/epoxy woven composite material system. The results presented here represent an extension of the work by Patel and Case (Int. J. Fatigue 22 (2000) 809).

The hygrothermal aging consisted of cyclical temperature and moisture variations which were meant to simulate mission conditions for an advanced subsonic aircraft. Durability studies were carried out on the aged material system in the form of fatigue and residual strength testing under humid and elevated temperature environments. Damage mechanisms and failure modes were determined through fatigue testing, residual strength testing, and nondestructive evaluation.

Changes in physical appearance, thermal analysis results, fracture surfaces, and moisture diffusion behavior all supported the idea that the material was affected by the aging process. However, experimental testing also showed that the initial and residual tensile properties of the aged material were virtually unaffected by the imposed environmental aging (as compared to unaged material testing results), except when tested at elevated temperature. At elevated temperature, both the dynamic stiffness and residual strength were noticeably reduced from that at room temperature.