Effect of in-situ formation of columnar mullite and pore structure refinement on high temperature properties of corundum casatbles

The effects of in-situ synthesis columnar mullite and pore structure on the hot modulus of rupture (HMOR), thermal shock resistance and corrosion resistance of corundum castables have been investigated in this paper. When 2% nano silica was added, the pore diameters of castables could be decreased to 15 nm (at 110 °C), 1 μm (1100 °C) and 6 μm (1500 °C), respectively. The corresponding reducing magnitude of pore size is 98.5%, 83.3% and 33.3%. The HMOR of castables fired at 1500 °C increased by 110% to 3.64 MPa. Furthermore, after three thermal shock cycles, the residual strength ratio of castables increased from 5.2% to 15.3%. A large amount of cross-distributed columnar mullite was formed between nano silica and α-Al₂O₃ by the two-dimensional nucleation mechanism, which remarkably enhanced the high temperature properties. The penetration index reduced from 30.86% to 19.88%, suggesting that smaller pore size and higher viscosity had a great influence to the penetration process.     

燃气热水器在无回水管水路中实现零冷水的方案研究

本文分析了燃气热水器行业针对无回水管水路系统实现零冷水功能的现有技术方案,指出现有技术方案存在的一些缺陷,并结合试验研究,对无回水管水路系统提出了一套全新的实现零冷水功能的技术解决方案。     

DP980+Z烘烤硬化值与退火温度的关系

摘要：为了研究退火温度对镀锌DP980+Z烘烤硬化值的影响，退火温度控制在760～820℃之间，系统分析退火温度对烘烤硬化值的影响。通过准静态拉伸试验机测量烘烤硬化值及抗拉强度，采用lepara试剂对组织中的马氏体进行着色，利用金相显微镜及图像处理软件测量马氏体的体积分数；采用扫描电镜观察DP980+Z的双相组织特点，并且将组织图片通过CAD转化成有限元图进行网格划分，建立代表性体积单元（RVE），通过有限元分析铁素体、马氏体强度对烘烤硬化值的影响。在同样的变形量情况下，DP980+Z的原始屈服强度越高，烘烤硬化值越高。     

含煤盆地深层“超饱和”煤层气形成条件

中国深层煤层气资源丰富，但总体勘探和认识程度较低，尚未形成较为系统的深层煤层气地质理论。通过解剖分析准噶尔盆地白家海凸起和鄂尔多斯盆地临兴区块深层"超饱和"煤层气井的试气/生产动态，估算原地游离气的含气量，分析了深层"超饱和"煤层气的形成条件。研究表明：①深层"超饱和"煤层气储层中除吸附气外，还含有原地游离气，用常规试气方法可直接获得气流，煤层气的产出不明显依赖于排水降压；②埋藏超过一定深度，在煤阶和温度的综合作用下，煤的吸附能力将随埋深的继续增加而降低，煤层中吸附气的饱和度有增加的趋势，在达到吸附饱和后，出现原地游离气并形成"超饱和"煤层气，盆地深层具有"超饱和"煤层气形成的优势条件；③由于地温梯度和压力梯度的不同，不同盆地"超饱和"煤层气出现的临界深度不同，异常高压和异常高热流可以降低深层"超饱和"煤层气形成的临界深度；④深层"超饱和"煤层气开发具有大大缩短见气时间、充分利用地层能量和累积产水量低等优势，有望成为未来煤层气勘探开发的一个重要领域。     

高精度多环片自动装配控制技术

为了实现对微小环片零件的自动化装配,搭建了自动装配系统.通过4根直线导向轴与4个直线轴承来提高系统的导向精度和刚度.采用直线导轨进行各装配作业模块之间的切换,保证了微小环片零件的自动装配与取出.在环片的装配方向上,螺旋升降机和光栅尺实现环片的位置精度控制.在Lab VIEW编程环境中,采用分层软件架构和模块化控制思想,避免了不必要的数据循环检测与丢失,能够达到环片组件的装配精度要求.控制系统分为系统初始化模块、参数设置模块、装配模块和取出模块,自动装配系统通过各个模块间的相互交流配合完成装配任务.采用本文中自动装配系统装配环片的实验结果表明,环片零件装配的最大位置误差为26μm,垂直度误差为17μm,平均装配时间为75 s/片,可满足环片组件所需的精度要求.     

Critical state model for structured soil

Structure is an evident determinant for macroscopic behaviors of soils. However, this is not taken into account in most constitutive models, as structure is a rather complex issue in models. For this, it is important to develop and implement simple models that can reflect this important aspect of soil behavior. This paper tried to model structured soils based on well-established concepts, such as critical state and sub-loading. Critical state is the core of the classic Cam Clay model. The sub-loading concept implies adoption of an inner (sub-loading) yield surface, according to specific hardening rules for some internal strain-like state variables. Nakai and co-workers proposed such internal variables for controlling density (ρ) and structure (ω), using a modified stress space, called t_ij. Herein, similar variables are used in the context of the better-known invariants (p and q) of the Cam Clay model. This change requires explicit adoption of a non-associated flow rule for the sub-loading surface. This is accomplished by modifying the dilatancy ratio of the Cam Clay model, as a function of the new internal variables. These modifications are described and implemented under three-dimensional (3D) conditions. The model is then applied to simulating laboratory tests under different stress paths and the results are compared to experiments reported for different types of structured soils. The good agreements show the capacity and potential of the proposed model.     

A Constitutive Equation of Thermoelasticity for Solid Materials

A new constitutive equation of thermoelasticity for crystals is presented based on the interatomic potential and solid mechanics at finite temperature. Using the new constitutive equation, the calculations for crystal copper and graphene are carried out under different loading paths at different temperatures. The calculated results are in good agreement with those of the previous thermoelasticity constitutive equation based on quantum mechanics, which clearly indicates that our new constitutive equation of thermoelasticity is correct. A lot of comparisons also show that the present theory is more concise and efficient than the previous thermal stress theory in the practical application.     

四川盆地高石梯-磨溪地区下二叠统气源示踪

以天然气、烃源岩及储层沥青的地球化学特征为主要依据,通过天然气-天然气、储层沥青-烃源岩、天然气-烃源岩3个方面对比,深入探讨四川盆地高石梯-磨溪地区下二叠统天然气来源。研究表明,四川盆地高石梯-磨溪地区下二叠统天然气主要来源于筇竹寺组泥岩。其5项证据分别为:下二叠统天然气乙烷碳同位素小于-30.5‰,甲、乙烷碳同位素倒转是由高演化程度烃源岩所致;多数下二叠统天然气与龙王庙组天然气特征最为相似;GS18,NC1井下二叠统天然气特征与寒武系相似,说明上下层气源一致;高石梯-磨溪地区下二叠统储层沥青地球化学特征与筇竹寺组泥岩最为相似;筇竹寺组泥岩主要为下二叠统供气,这一认识符合干酪根油气生成理论和同位素分馏规律。     

一种军棋机器博弈的多棋子协同博弈方法

针对在军棋博弈不完全信息对弈中，面对棋子不同价值、不同位置、不同搭配所产生的不同棋力，传统的单子意图搜索算法，不能满足棋子之间的协同性与沟通性，同时也缺乏对敌方的引诱与欺骗等高级对抗能力。本文提出一种结合UCT搜索策略的高价值棋子博弈方法，实现高价值棋子协同博弈的策略。实战经验表明:高价值多棋子军棋协同博弈策略优于单棋子军棋博弈策略。     

High-Tg porous polyimide films with low dielectric constant derived from spiro-(adamantane-2,9′(2′,7′-diamino)-fluorene)

Porous polyimide (PI) films with low dielectric constants and excellent thermal properties have been a pressing demand for the next generation of high-performance, miniature, and ultrathin microelectronic devices. A series of novel porous PI films containing fluorenyl-adamantane groups were prepared successfully via thermolysis of poly(ethylene glycol) (PEG) added in the PI matrix. The cross-sectional morphologies of porous PI films showed closed pores with diameters ranging from 135 to 158 nm, which were uniform and regular in shape without interconnectivity. These porous PI films exhibited excellent thermal properties with a glass-transition temperature at 376 °C whereas the 5% weight loss temperature in air excess of 405 °C due to enhanced rigidity afforded by fluorenyl-adamantane groups. Accompanied by thermolysis content of PEG increasing from 0 to 20 wt %, the density of porous PI films decreased, and the corresponding porosity grew significantly from 0 to 11.48%. Depending on porosity, the dielectric constant and dielectric loss of porous PI films significantly declined from 2.89 to 2.37 and from 0.050 to 0.021, respectively. These excellent properties benefit the as-prepared porous PI films for application as interlayer dielectrics, integrated circuit chips, or multichip modules in microelectronic fields. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47313.