Grain orientation evolution and multi-scale interfaces enhanced thermoelectric properties of textured Sr0.9La0.1TiO3 based ceramics

Sr_0.9La_0.1TiO₃ based textured ceramics (SLTT-S3T) with a texture fraction of 0.81 are successfully fabricated by the reactive template grain growth method, in which Sr_0.9La_0.1TiO₃/20 wt%Ti was used as matrix and 10 wt% plate-like Sr₃Ti₂O₇ template seeds were used as templates. The phase transition, microstructure evolution, and the anisotropic thermoelectric properties of SLTT-S3T ceramics were investigated. The results show that the ceramics are mainly composed of Sr_0.9La_0.1TiO₃ and rutile TiO₂ phases. Grains grow with a preferred orientation along (h00). A maximum ZT of 0.26 at 1073 K was achieved in the direction perpendicular to the tape casting direction. The low lattice thermal conductivity of 1.9 W/(m K) at 1073 K was obtained decreased by 34%, 40%, and 38% compared with non-textured, SrTiO₃ and Sr_0.9La_0.1TiO₃ ceramics prepared by the same process, can be attributed to the enhanced phonon scattering by the complex multi-scale boundaries and interfaces. This work provides a strategy of microstructural design for thermoelectric oxides to decrease intrinsic lattice thermal conductivity and further regulate thermoelectric properties via texture engineering.     

The effect of particle size distribution on the microstructure and properties of Al2O3 ceramics formed by stereolithography

Stereolithography (SL) shows advantages for preparing alumina-based ceramics with complex structures. The effects of the particle size distribution, which strongly influence the sintering properties in ceramic SL, have not been systematically explored until now. Herein, the influence of the particle size distribution on SL-manufactured alumina ceramics was investigated, including bending strength at room temperature, post-sintering shrinkage, porosity, and microstructural morphology. Seven particle size distributions of alumina ceramics were studied (in μm/μm: 30/5, 20/3, 10/2, 5/2, 5/0.8, 3/0.5, and 2/0.3); a coarse:fine particle ratio of 6:4 was maintained. At the same sintering temperature, the degree of sintering was greater for finer particle sizes. The particle size distribution had a larger influence on flexural strength, porosity and shrinkage than sintering temperature when the particle size distribution difference reached 10-fold but was weaker for 10 μm/2 μm, 5 μm/2 μm and 5 μm/0.8 μm. The sintering shrinkage characteristics of cuboid samples with different particle sizes were studied. The use of coarse particles influenced the accuracy of small-scale samples. When the particle size was comparable to the sample width, such as 30 μm/5 μm and 5 mm, the width shrinkage was consistent with the height shrinkage. When the particle size was much smaller than the sample width, such as 2 μm/0.3 μm and 5 mm, the width shrinkage was consistent with the length shrinkage. The results of this study provide meaningful guidance for future research on applications of SL and precise control of alumina ceramics through particle gradation.     

Enhanced electromagnetic microwave absorption of Fe/C/SiCN composite ceramics targeting in integrated structure and function

The Fe/C/SiCN composite ceramics were synthesized by polymer-derived method to obtain the integration of structure and functions. The electromagnetic waves (EMW) absorption properties at X and Ku bands were investigated. The addition of nano-sized Fe particles improved the magnetic loss and impedance matching, and the carbon nanotubes generated by the iron in-situ catalysis increased the internal relaxation polarization and interfacial polarization, which together improved the EMW absorption properties significantly. In particular, the Fe/C/SiCN-9 showed the optimum reflection loss (RL) of ?31.06 dB at 10.03 GHz with an effective absorption bandwidth (EAB, RL < ?10 dB) of 3.03 GHz at 2.51 mm, indicating the excellent EMW absorption properties of Fe/C/SiCN composite ceramics.     

Fabrication and laser performances of Yb:Sc2O3 transparent ceramics from different combination of vacuum sintering and hot isostatic pressing conditions

In this paper we report on the preparation and laser performance of transparent 3at.% Yb:Sc₂O₃ ceramics by reactive sintering of commercially available powders under vacuum followed by hot isostatic pressing (HIP). Combinations of different vacuum sintering temperatures (1650 °C and 1750 °C) and different HIP treatments (1700 °C and 1800 °C at 200 MPa) were tested in order to understand how these steps influence the microstructure and thus the optical and lasing properties of the ceramic samples. All the samples showed a good optical quality. The microstructure analysis and the laser tests showed that the vacuum pre-sintering temperature is the key factor determining the quality of the samples and the laser performances. The best values of slope efficiency i.e. η_L = 50 % and output power i.e. P_out = 6.62 W were obtained for the sample pre-sintered under vacuum at 1650 °C and hot isostatically pressed at 1800 °C.     

Surveying of Na2O3–BaO–PbO–Nb2O5–SiO2–Al2O3 glass-ceramics system in terms of alpha,proton, neutron and gamma protection features by utilizing GEANT4 simulation codes

In this study, nuclear shielding qualities of glass-ceramics with chemical composition Na₂O₃–BaO–PbO–Nb₂O₅–SiO₂–Al₂O₃ containing different amount of BaO and PbO were investigated. The μ_ρ values were simulated using GEANT4 toolkit at 0.015–20 MeV wide energy range and the obtained results were verified by theoretical WinXCOM results. The variables such as μ_ρ, HVL, MFP, Z_eff, N_eff, EBF and EABF were computed to determine the gamma-ray shielding performances of studied glass ceramics. The results revealed that increase in PBO and BaO percentages in glass samples has caused to decrease the HVL, MFP, EBF and EABF values and increase μ_ρ, Z_eff values. It has been seen that N28 and S24 samples own superior protection ability against gamma radiation. In addition, the shielding capacity of these glass ceramics against charged and uncharged particles were predicted by determination of MSP and PR values for alpha, proton and ΣR values for neutrons. It has been concluded that PbO and BaO addition improve radiation shielding competences of glass ceramics. The data obtained from this study will be beneficial for designing glass ceramics shields for radiation protection enforcements.     

Warm-white light performance of Dy3+, Eu3+: NaLa(WO4)2 phosphors excited with a 450-nm LED

Dy³⁺, Eu³⁺: NaLa(WO₄)₂ phosphors are successfully synthesized through the solid-state reaction technique. The phase-structure and morphology are measured via X-ray diffraction and energy dispersive spectrometry. The concentrations of Dy³⁺, Eu³⁺, La³⁺, and W⁶⁺ are measured via ICP. The absorption and excited spectra are presented, which indicate that a blue band ranging from 430 to 480 nm is suitable for excitation. Using a commercial blue LED with a wavelength of 450 nm as the excitation light source, emission spectra for samples with varying dopant concentration ratios of Dy³⁺ to Eu³⁺ are obtained, which show good tunable yellow and red emission. For the purpose of investigating white LED performance, CIE spectra and a white light photo are also presented. The results reveal that varying the dopant concentration ratio of Dy³⁺ to Eu³⁺ plays a key role in the warm-white performance. With increasing concentration of Eu³⁺, the correlated color temperature decreases from 4069 to 3172 K, which indicates good warm-white performance.     

Twin screw granulation – review of current progress

Twin screw granulation (TSG) is a new process of interest to the pharmaceutical community that can continuously wet granulate powders, doing so at lower liquid concentrations and with better product consistency than found by a high shear batch mixer. A considerable body of research has evolved over the short time since this process was introduced but generally with little comparison of results. A certain degree of confidence has been developed through these studies related to how process variables and many attributes of machinery configuration will affect granulation but some major challenges still lay ahead related to scalability, variations in the processing regimes related to degree of channel fill and the impact of wetting and granulation of complex powder formulations. This review examines the current literature for wet granulation processes studied in twin screw extrusion machinery, summarizing the influences of operational and system parameters affecting granule properties as well as strives to provide some practical observations to newly interested users of the technique.     

Bond characteristics,vibrational spectrum and optimized microwave dielectric properties of chemically substituted NdNbO4

Coordination chemistry, bond state and vibrational spectrum of co-substituted microwave dielectric NdNb_1-x(Zr_0.5W_0.5)_xO₄ ceramics (x = 0.01∼0.05) were investigated. Raman spectra and XRD refinement showed a solid solution was formed. The compressed and elongated chemical bonds are responsible for the variations of crystal parameters and cell volume. Calculated chemical bond parameters indicated bond covalency, lattice energy and Nb-site bond energy act on the fluctuations of the permittivity, quality factor and temperature coefficient, respectively. Meanwhile, the infrared vibrational spectrum is fitted to quantify the contributions of observed IR mode to the intrinsic loss. Compact ceramic possesses excellent properties: ε_r ∼ 19.2, Q × f ∼ 55282 GHz and τ_f ∼ -11.36 ppm/°C with x = 0.04, at 1250°C.     

Ablation behavior of (TiZrHfNbTa)C high-entropy ceramics with the addition of SiC secondary under an oxyacetylene flame

The ablation behavior of high-entropy ceramics (HECs) was investigated in this study using an oxyacetylene flame at 2000 °C. Spark plasma sintering was used to construct a dense HEC (TiZrHfNbTa)C with a 20 vol% of SiC addition (HEC-20SiC). The densification of HEC-20SiC can be improved to a certain extent by adding SiC particles, increasing the hardness of HEC-20SiC to up to 24.6 GPa, and the crack deflection observed through the addition of SiC particles were considered to be the strengthening and toughening mechanisms. After ablation, Hf₆Ta₂O₁₇, Ti_5.1Ta_4.9O₂₀, Nb₂Zr₆O₁₇, TaZr_2.75O₈, and SiO₂ can be detected on an ablated surface and HEC-20SiC possesses the minimum mass ablation rate (?1.9 mg s^?1) and line ablation rate (2.1 μm s^?1) among the comparative ceramics. On the one hand, the SiC phase forms gaseous CO, CO₂, and SiO as well as viscous SiO₂ during ablation and some part of the heat can be dissipated by the evaporation of gaseous CO, CO₂, and SiO; further, pore defects can be healed by viscous SiO₂, thus inhibiting the diffusion of reactive oxygen species. On the other hand, the HEC phase with a lattice-distortion caused by single-phase solid-solution can effectively inhibit the invasion of reactive oxygen species and the outward migration of metal atoms. The invasion rate of reactive oxygen is considered to be the main step during HEC-20SiC ablation, and it is believed that higher principal component HECs can improve ablation performance even further.     

Energy storage performance of 0.55Bi0.5Na0.5TiO3-0.45SrTiO3 ceramics doped with lanthanide elements (Ln = La,Nd, Dy,Sm) using a viscous polymer processing route

Lead-free bismuth sodium titanate-strontium titanate (NBT-ST) dielectric ceramic materials have been extensively investigated energy storage materials because of their relaxor characteristics. In this study, four different lanthanide elements were introduced into the ferroelectric NBT-ST ceramic to improve their relaxor properties. The introduction of the lanthanide resulted in an increase in disorder at location A within the perovskite lattice and improved relaxor characteristics, leading to a stored energy density of more than 3.5 J/cm³. In particular, an ultrahigh recoverable stored energy density of 4.94 J/cm³ and efficiency of 88.45% were achieved at 440 kV/cm when the NBT-ST ceramic was modified with neodymium. The modified ceramic also exhibited good thermal stability in the range of 30–120 °C, as well as a fast discharge time of ～153 ns, indicating that Nd-incorporated NBT-ST is a promising candidate for electrical energy storage ceramic.