Microstructure and mechanical properties of hot-pressed SiC nanofiber reinforced SiC composites

This study reports on the preparation and mechanical properties of a novel SiC_nf/SiC composite. The single crystal SiC nanofiber(SiC_nf) reinforced SiC ceramic matrix composites (CMC) were successfully fabricated by hot pressing the mixture of β-SiC powders, SiC_nf and Al–B–C powder. The effects of SiC_nf mass fraction as well as the hot-pressing temperature on the microstructure and mechanical properties of SiC_nf/SiC CMC were systematically investigated. The results demonstrated that the 15 wt% SiC_nf/SiC CMC obtained by hot pressing (HP) at 1850 °C with 30 MPa for 60 min possessed the maximum flexural strength and fracture toughness of 678.2 MPa and 8.33 MPa m^1/2, respectively. The nanofibers pull out, nanofibers bridging and cracks deflection were found by scanning electron microscopy, which are believed can strengthen and toughen the SiC_nf/SiC CMC via consuming plenty of the fracture energy. Besides, although the relative density of the prepared SiC_nf/SiC CMC further increased with the sintering temperature rose to 1900 °C, the further coarsend composites grains results in the deterioration of the mechanical properties for the obtained composites compared to 1850 °C.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

电磁精细探测法在隐伏型导水地质裂缝勘探中的应用

针对传统隐伏型导水地质裂缝勘探方法存在勘测精度较差的问题,提出电磁精细探测法探析隐伏型导水地质裂缝。依照屏蔽系数、实测场强和理论场强数据绘制综合曲线图,通过该图获取隐伏型导水地质裂缝所处位置几何阴影范围,采用层析成像法得到网格化的工作面,获取隐伏型导水地质图像。通过图像直接观测隐伏型导水地质工作面裂缝所处位置,在此基础上,观测四个电磁场分量,采用正交电磁场分量计算介质视电阻率,依据计算视电阻率数值和视电阻率分布状态研究裂缝发育情况和裂缝富水程度。结果表明:采用该方法能较为精准地获取隐伏型导水地质裂缝位置。通过裂缝位置进一步检测出隐伏型导水地质裂缝最大发育高度为63.5 m。当视电阻数值不断增加时,隐伏型导水地质裂缝和裂缝富水性逐渐减小,与实际情况较为相符,说明该种方法探析效果较好。     

Effects of SiC content on the densification,microstructure, and mechanical properties of HfB2–SiC composites

To investigate the effects of SiC on microstructure, hardness, and fracture toughness, 0, 10, 20, and 30 vol% SiC were added to HfB₂ and sintered by SPS. Upon adding SiC to 30 vol%, relative density increased about 4%; but HfB₂ grain growth had a minimum at 20 vol% SiC. This may be due to grain boundary silicate glass, responsible for surface oxide wash out, enriched in SiO₂ with higher fraction of SiC. By SiO₂ enrichment, the glass viscosity increased and higher HfO₂ remained unsolved which subsequently lead to higher grain growth. Hardness has increased from about 13 to 15 GPa by SiC introduction with no sensible variation with SiC increase. Residual stress measurements by Rietveld method indicated high levels of tensile residual stresses in the HfB₂ Matrix. Despite the peak residual stress value at 20 vol% SiC, fracture toughness of this sample was the highest (6.43 MPa m^0.5) which implied that fracture toughness is mainly a grain size function. Tracking crack trajectory showed a mainly trans-granular fracture, but grain boundaries imposed a partial deflection on the crack pathway. SiC had a higher percentage in fracture surface images than the cross-section which implied a weak crack deflection.     

Comparative studies on thermal and toughness properties of polybenzoxazine composites with two functionalized graphene oxides

Abstract

Graphene oxide (GO) was functionalized by polyether amine (PEA) via two methods which were one-pot modification in acetone (GON) and two steps with the intermediate product of GOCO-Cl generated (GONS). There were more PEA successfully grafted onto GO for GONS than GON. The onset polymerization temperatures of the benzoxazine (Bz) composites decreased by the inclusion of 1?wt% of GO, GON or GONS. Thermal stability of the polybenzoxazine (PBz) composites was significantly improved indicated from the increase of weight loss temperature. T₁₀, T₂₀ and T₅₀ values of the composites with GONS were higher than that of the others. Toughness of PBzs may be enhanced by the incorporation of nanofillers, and GONS had stronger interfacial interaction with PBz matrix than GON.     

湘中海相浅层湘冷1井酸压工艺研究及应用

湘冷1井具有气层埋藏浅（400m-500m）、纵向上裂隙发育的特点，属低孔、低渗的含泥质灰岩致密储层。大量室内实验和研究采用“前置液酸压＋闭合酸化”工艺技术，并优选了相应降阻酸和闭合酸配方。通过酸压实现了该井工业油气流的突破，取得了明显的增产效果，为新区海相浅层气的开发探索出了一套成熟的改造增产措施。     

低渗低温低压水敏性储气层压裂改造技术研究与应用

低渗低温低压水敏性储气层因压裂液快速破胶困难、黏土膨胀水敏伤害严重和压后压裂液返排动力不足等因素，使得压裂增产面临诸多难题。针对上述难题进行了技术攻关，形成了弱交联、低温活化剂与超量破胶剂的低温储层快速破胶技术、有机盐与无机盐双元体系复合防膨技术以及高比例液氮全程助排的排液技术。该压裂增产改造技术使牛101井头屯河组首次获得工业油气流，扩展了三塘湖盆地勘探空间。     

试油井选层压裂新工艺及现场试验

设计新型可洗井封隔器，保障油井有反洗井通道，有效防止封隔器以上砂埋所引发的管柱砂卡事故，并对新型封隔器、控制开关、密封接头、同心大通径压力计托筒等井下工具组合优化。解决了多层油井任意选层压裂、求产、测井温一体化的难题。     

论四川盆地天然气勘探前景

中石油及其前身已在四川盆地从事天然气勘探开发工作50余年,截至2005年底累计探明天然气地质储量逾8400×10⁸m³,累计生产天然气超过2300×10⁸m³,年产量现已超过120×10⁸m³,已成为国内目前最大的产气区。对于该盆地进一步勘探前景如何的命题,从以下4个方面给予了论证：一是资源丰富、勘探成果持久不衰，近期仍有大发现；二是要辩证地认识盆地油气地质的复杂性，探索新规律，解放新领域；三是寻求地质认识和勘探技术进步是勘探突破的关键；四是继续以盆地两大地质体系（海相古隆起体系及陆相前陆盆地体系）和8套裂缝-孔隙性储集层（中上寒武统白云岩、石炭系白云岩、上二叠统长兴组生物礁白云岩、下三叠统飞仙关组鲕状白云岩、下三叠统嘉陵江组粒屑白云岩、中三叠统雷口坡组藻粒白云岩、上三叠统须家河组长石岩屑石英砂岩和中上侏罗统红层砂岩）为对象获取更多的天然气资源量及优质储量。据此得出结论：四川盆地天然气勘探前景是广阔的，但勘探难度会逐步加大。