The influence of volume fraction of amorphous phase on corrosion resistance of Mg67Zn 29Ca 4 alloy

The aim of this study was to investigate the structure and corrosion resistance of amorphous, amorphous‐crystalline, and crystalline Mg₆₇Zn₂₉Ca₄ alloy for biodegradable applications. This paper presents a preparation method and results of the structural characterization and corrosion resistance analysis of the material. Samples were prepared in the form of 3 mm diameter rods. The structure of the alloy was examined with the use of X‐ray diffractometry and scanning electron microscopy. The thermal properties of the samples were examined with differential scanning calorimetry (DSC). Results of DSC analysis were used to determine heat treatment temperatures, allowing to obtain different fractures of crystalline phase in the material. Corrosion resistance of heat‐treated samples was investigated by immersion tests and electrochemical measurements performed in the simulated body fluid. The X‐ray diffraction results confirmed that the prepared Mg₆₇Zn₂₉Ca₄ alloy's structure is fully amorphous. After heat treatment, samples with different fractions of amorphous phase in the structure were obtained. Immersion tests of the samples showed that the structure significantly influenced corrosion resistance in examined materials. It should be pointed out, that certain amounts of crystalline phase in amorphous matrix can greatly improve the corrosion resistance of Mg₆₇Zn₂₉Ca₄ alloy.     

Crystal-field engineering of ultrabroadband mid-infrared emission in Co2+-doped nano-chalcogenide glass composites

Tunable and ultrabroadband mid-infrared (MIR) emissions in the range of 2.5–4.5 μm are firstly reported from Co²⁺-doped nano-chalcogenide (ChG) glass composites. The composites embedded with a variety of binary (ZnS, CdS, ZnSe) and ternary (ZnCdS, ZnSSe) ChG nanocrystals (NCs) can be readily obtained by a simple one-step thermal annealing method. They are highly transparent in the near- and mid-infrared wavelength region. Low-cost and commercially available Er³⁺-doped fiber lasers can be used as the excitation source. By crystal-field engineering of the embedded NCs through cation- or anion-substitution, the emission properties of Co²⁺ including its emission peak wavelength and bandwidth can be tailored in a broad spectral range. The phenomena can be accounted for by crystal-field theory. Such nano-ChG composites, perfectly filling the 3–4 μm spectral gap between the oscillations of Cr²⁺ and Fe²⁺ doped IIVI ChG crystals, may find important MIR photonic applications (e.g., gas sensing), or can be used directly as an efficient pump source for Fe²⁺: IIVI crystals which are suffering from lack of pump sources.     

Importance of finding the proper ratio of alkaline earth oxide in a lithium-bismuthate-phosphate glass in order to enhance the tailoring of structural and electrical properties

Structural features of the glass family xLi₂O- yMgO (4.8 Bi₂O₃ 47.6 P₂O₅) obtained by melt quenching technique were studied taking into account the density, FTIR and UV–vis spectra and also the electrical response observed by impedance spectroscopy. In this work it becomes clarified how the alkaline earth oxides stabilize the glassy matrix and also, the fundamental importance of determining the optimal proportion in order to obtain a flabby easily polarizable matrix to enhance the electrical behavior due to a boosted cation mobility. It is evidenced that when the glass composition becomes complex it is needed to take into account a larger number of structural parameters to understand, to predict or to design the resulting physical properties.     

Precipitating spinel into precursor glass and its assistance in crystallization

The crystallization phenomena of spinel in CaO-MgO-Al₂O₃-SiO₂-Fe₂O₃ glass have received much attention due to the particular role in preparation of glass-ceramic materials, which represent an effective option to manage hazardous waste. In this study, both preliminary spinel and secondary spinel were precipitated in the precursor glass. The formation of these spinel was meticulously assessed by a combination of X-ray diffractometry and scanning electron microscopy. The structure of the microenvironment in the precursor glass was characterized by Raman spectrums. These advanced techniques highlight the potential for one-step crystallization of the glass. The investigation, which focused on one-step crystallization, demonstrated the growth of pyroxene on spinel accompanying a migration of chromium. The results also show the microstructure of the obtained glass-ceramic was very dependent on the heat-treat temperature. This study not only unambiguously reveals the precipitation mechanisms of spinel but also provides more documentation for one-step crystallization in the glass-ceramics field.     

Effect of an abrupt change in pulling rate on microstructures of directionally solidified Al2O3-Er3Al5O12 eutectic and off-eutectic composite ceramics

Directionally solidified microstructures of Al₂O₃-Er₃Al₅O₁₂ eutectic and off-eutectic in situ composite ceramics were explored under abrupt-change pulling rate conditions. Corresponding temperature distributions and interface locations were studied. In eutectic composition, fluctuation of eutectic spacing occurred when the pulling rate increased abruptly. A gradually increase or abrupt increase in eutectic spacing was observed when the pulling rate decreased abruptly. In hypoeutectic and hypereutectic compositions, formation of the primary phases were suppressed when the pulling rate increased abruptly from 10?µm/s to 100?µm/s, while primary phases precipitated when the pulling rate decreased abruptly from 100?µm/s to 10?µm/s. The interface altitude decreased after the pulling rate increased abruptly, but increased after the pulling rate decreased abruptly. The liquid composition restriction (around the eutectic composition) at the eutectic interface plays an important role in the suppression of the primary dendrite and coupled eutectic oxides can be obtained in off-eutectic compositions even under higher solidification rate conditions.     

Physical Stability of Octenyl Succinate–Modified Polysaccharides and Whey Proteins for Potential Use as Bioactive Carriers in Food Systems

The high cost and potential toxicity of biodegradable polymers like poly(lactic‐co‐glycolic)acid (PLGA) has increased the interest in natural and modified biopolymers as bioactive carriers. This study characterized the physical stability (water sorption and state transition behavior) of selected starch and proteins: octenyl succinate–modified depolymerized waxy corn starch (DWxCn), waxy rice starch (DWxRc), phytoglycogen, whey protein concentrate (80%, WPC), whey protein isolate (WPI), and α‐lactalbumin (α‐L) to determine their potential as carriers of bioactive compounds under different environmental conditions. After enzyme modification and particle size characterization, glass transition temperature and moisture isotherms were used to characterize the systems. DWxCn and DWxRc had increased water sorption compared to native starch. The level of octenyl succinate anhydrate (OSA) modification (3% and 7%) did not reduce the water sorption of the DWxCn and phytoglycogen samples. The Guggenheim–Andersen–de Boer model indicated that native waxy corn had significantly (P < 0.05) higher water monolayer capacity followed by 3%‐OSA‐modified DWxCn, WPI, 3%‐OSA‐modified DWxRc, α‐L, and native phytoglycogen. WPC had significantly lower water monolayer capacity. All Tg values matched with the solid‐like appearance of the biopolymers. Native polysaccharides and whey proteins had higher glass transition temperature (Tg) values. On the other hand, depolymerized waxy starches at 7%‐OSA modification had a “melted” appearance when exposed to environments with high relative humidity (above 70%) after 10 days at 23 °C. The use of depolymerized and OSA‐modified polysaccharides blended with proteins created more stable blends of biopolymers. Hence, this biopolymer would be suitable for materials exposed to high humidity environments in food applications.     

Hierarchical micro-nanostructured albite-based glass-ceramic for high dielectric strength insulators

A novel glass-ceramic material based on albite type Na-rich feldspar has been synthesized by conventional ceramic process. High crystallinity, >94%?Vol.% is obtained by fast sintering which allows energy saving processing. Albite is the main crystalline phase and tetragonal SiO₂ is a secondary phase. Electrical properties were examined by complex impedance, DC measurements, and dielectric breakdown test. Dielectric characterization shows a non-Debye type dielectric behavior with low dielectric constant, 4.6 at 1?MHz, low dielectric losses, (～10^?3 at 1?MHz, and a large dielectric strength, ～60?kV/mm), that it is the largest value reported in ceramic insulators. Those dielectric properties are attained by the low glassy phase content in the samples and their unique micro-nanostructure. All these properties make this novel material a very promising candidate in the market of ceramic electrical insulator, highlighting for high-voltage applications.     

Effects of SiC content on the densification,microstructure, and mechanical properties of HfB2–SiC composites

To investigate the effects of SiC on microstructure, hardness, and fracture toughness, 0, 10, 20, and 30 vol% SiC were added to HfB₂ and sintered by SPS. Upon adding SiC to 30 vol%, relative density increased about 4%; but HfB₂ grain growth had a minimum at 20 vol% SiC. This may be due to grain boundary silicate glass, responsible for surface oxide wash out, enriched in SiO₂ with higher fraction of SiC. By SiO₂ enrichment, the glass viscosity increased and higher HfO₂ remained unsolved which subsequently lead to higher grain growth. Hardness has increased from about 13 to 15 GPa by SiC introduction with no sensible variation with SiC increase. Residual stress measurements by Rietveld method indicated high levels of tensile residual stresses in the HfB₂ Matrix. Despite the peak residual stress value at 20 vol% SiC, fracture toughness of this sample was the highest (6.43 MPa m^0.5) which implied that fracture toughness is mainly a grain size function. Tracking crack trajectory showed a mainly trans-granular fracture, but grain boundaries imposed a partial deflection on the crack pathway. SiC had a higher percentage in fracture surface images than the cross-section which implied a weak crack deflection.     

Plasmonic-excitonic multi-hybrid glass-based nanocomposites incorporating Ag plus core-shell CdSe/CdS and alloyed CdSxSe1−x nanoparticles

Successful fabrication of glass-based hybrid nanocomposites (GHNCs) incorporating Ag, core-shell CdSe/CdS and CdS_xSe_1?x nanoparticles (NPs) is herein reported. Both metallic (Ag) and semiconductor (CdSe/CdS) NPs were pre-synthesized, suspended in colloids and added into the sol-gel reaction medium which was used to fabricate the GHNCs. During fabrication of the nanocomposites a fraction (20–60%) of core-shell CdSe/CdS NPs was alloyed into CdS_xSe_1?x (0.20 < x < 0.35) NPs without changing morphology. Modulation of in situ alloying is possible via the relative content of organics added into the sol-gel protocol. Within colloids Ag (core-shell CdSe/CdS) NPs presented average diameter and polydispersity index of 49.5 nm (4.2 nm) and 0.41 (0.21), respectively. On the other hand, the Ag (core-shell CdSe/CdS) NPs’ average diameter and polydispersity index assessed from the GHNCs were respectively 51.5 nm (4.1 nm) and 0.43 (0.25), revealing negligible aggregation of the nanophases within the glass template. The new GHNCs herein introduced presented two independent excitonic transitions associated to homogenously dispersed semiconductor NPs, peaking around 420 nm (core-shell CdSe/CdS) and 650 nm (CdS_xSe_1?x) and matching the plasmonic resonance (Ag NPs) in the 400–500 nm range. We envisage that the new GHNCs represent very promising candidates for superior light manipulation while illuminated with multiple laser beams in quantum interference-based devices.     

Effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers

In this paper, polyborosilazane precursor was synthesied from HMDZ, HSiCl₃, BCl₃ and CH₃NH₂ using a multistep method. By controlling the storage conditions, parts of the polyborosilazane fibers were hydrolyzed. FT-IR, NMR, XRD, TEM and monofilament tensile strength test were employed to study the effects of hydrolysis of precursor on the structures and properties of polymer-derived SiBN ceramic fibers. FT-IR and NMR results indicate that Si-N group in PBSZ reacts with H₂O to form Si-O-Si group. After pyrolysis reaction at 1400℃, Si-O-Si group will finally transformed into highly ordered cristobalite and β-quartz, resulting in formation of the wrinkled surface of the obtained SiBN ceramic fiber. The strip-like defects on fiber surface, according to monofilament tensile strength test, had a significant effect on mechanical property of the obtained SiBN ceramic fiber and caused no increase in fiber tensile strength of hydrolytic polyborosilazane fiber before and after pyrolytic process.