Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Study on the blackening phenomenon of leaded glass during microgroove molding using nickel phosphorous mold

Precision glass molding (PGM) is a recently developed method to fabricate glass microgroove components. Lead glass is commonly used as an optical material due to its high refractive index and low transition temperature. A nickel-phosphorous (Ni–P) plated mold is traditionally employed in the PGM process for microstructures optics. However, leaded glass is subject to color change and can blacken during the PGM process, reducing the light transmittance of microgrooves. In this paper, an equation for the redox reaction between Ni and Pb is proposed, which is based on the diffusion of inner Ni atoms to the surface of the mold and the standard electrode potential of the Pb ions in leaded glass. A viscoelastic constitutive model of the glass is established to simulate the compression stress distribution during molding. Finally, the effects of molding pressure, molding temperature, and mold material on glass blackening are studied. The results show that the blackening of leaded glass is caused by Pb enriching the surface. The rise in molding stress and temperature increases the deformation of Ni–P plating, which promotes the diffusion of Ni atoms. By adding a titanium incorporated diamond-like carbon (Ti-DLC) coating, the deformation of the Ni–P plating during molding is suppressed, and the diffusion of Ni atoms can be prevented. In this way, the blackening of leaded glass can be prevented.     

Different hydrothermal corrosion results between two sides of sodalime float glass and the possible corrosion mechanism

Sodalime float (SF) glass is widely used in our societies and industries. Hydrothermal corrosion method is one of the effective ways to prepare a superhydrophobic glass, but there is still lack of knowledge about hydrothermal corrosion behavior and mechanism of SF glass. We have hydrothermally treated SF glass at 180 °C for different time, and tried to reveal the aqueous corrosion process of SF glass. We have characterized the morphologies and chemical compositions of samples, and found that (1) the two sides of SF glass have different corrosion resistances, and (2) a multilayer structural coating with a nanoflake layer (Mg-rich gel layer), a nanowire layer (Ca-rich gel layer), and a porous layer (etched layer) is formed on the air-side of SF glass. Based on the experimental results, we have proposed an aqueous corrosion mechanism of SF glass. The insights of the hydrothermal corrosion behaviors and mechanism provide helpful guidelines to glass surface structural control and functionalization.     

The influence of volume fraction of amorphous phase on corrosion resistance of Mg67Zn 29Ca 4 alloy

The aim of this study was to investigate the structure and corrosion resistance of amorphous, amorphous‐crystalline, and crystalline Mg₆₇Zn₂₉Ca₄ alloy for biodegradable applications. This paper presents a preparation method and results of the structural characterization and corrosion resistance analysis of the material. Samples were prepared in the form of 3 mm diameter rods. The structure of the alloy was examined with the use of X‐ray diffractometry and scanning electron microscopy. The thermal properties of the samples were examined with differential scanning calorimetry (DSC). Results of DSC analysis were used to determine heat treatment temperatures, allowing to obtain different fractures of crystalline phase in the material. Corrosion resistance of heat‐treated samples was investigated by immersion tests and electrochemical measurements performed in the simulated body fluid. The X‐ray diffraction results confirmed that the prepared Mg₆₇Zn₂₉Ca₄ alloy's structure is fully amorphous. After heat treatment, samples with different fractions of amorphous phase in the structure were obtained. Immersion tests of the samples showed that the structure significantly influenced corrosion resistance in examined materials. It should be pointed out, that certain amounts of crystalline phase in amorphous matrix can greatly improve the corrosion resistance of Mg₆₇Zn₂₉Ca₄ alloy.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .     

Two-step method to deposit ZrO2 coating on carbon fiber: Preparation,characterization, and performance in SiC composites

Recently, ceramic matrix composites reinforced by short carbon fibers (CFs) attracted increasing attentions. To further improve mechanical properties and oxidation resistances, CFs were subjected to oxidation and acidification followed by sol-gel dip-coating to deposit ZrO₂ on their surfaces. ZrO₂-C_f/SiC composites were fabricated by joint hot compression molding and sintering, compared to C_f/SiC and SiC prepared by the same method. Microstructural analyses indicated that ZrO₂ coatings were successfully deposited on CF surfaces, formed strong bonding and interfaces between CF and the matrix. Meanwhile, CFs were found uniformly distributed in SiC matrix with random orientations. Flexural curves of ZrO₂-C_f/SiC and C_f/SiC revealed the presence of “false plasticity” regions after sharp drops, which were quite different from brittle flexural behavior of SiC ceramic. Compression strength of the three samples showed step-up growth. ZrO₂-C_f/SiC exhibited the highest value, indicating the introduction of CFs and ZrO₂ coatings do have great influence on mechanical performances. After heat treatment, ZrO₂-C_f/SiC exhibited better oxidation resistance than C_f/SiC, with weight loss ratios estimated to ??3.76% and ??6.43%, respectively. These improved properties indicated that ZrO₂-C_f/SiC would be excellent alternatives to other existence materials under ultra-high temperature environments.     

Crystal-field engineering of ultrabroadband mid-infrared emission in Co2+-doped nano-chalcogenide glass composites

Tunable and ultrabroadband mid-infrared (MIR) emissions in the range of 2.5–4.5 μm are firstly reported from Co²⁺-doped nano-chalcogenide (ChG) glass composites. The composites embedded with a variety of binary (ZnS, CdS, ZnSe) and ternary (ZnCdS, ZnSSe) ChG nanocrystals (NCs) can be readily obtained by a simple one-step thermal annealing method. They are highly transparent in the near- and mid-infrared wavelength region. Low-cost and commercially available Er³⁺-doped fiber lasers can be used as the excitation source. By crystal-field engineering of the embedded NCs through cation- or anion-substitution, the emission properties of Co²⁺ including its emission peak wavelength and bandwidth can be tailored in a broad spectral range. The phenomena can be accounted for by crystal-field theory. Such nano-ChG composites, perfectly filling the 3–4 μm spectral gap between the oscillations of Cr²⁺ and Fe²⁺ doped IIVI ChG crystals, may find important MIR photonic applications (e.g., gas sensing), or can be used directly as an efficient pump source for Fe²⁺: IIVI crystals which are suffering from lack of pump sources.     

Importance of finding the proper ratio of alkaline earth oxide in a lithium-bismuthate-phosphate glass in order to enhance the tailoring of structural and electrical properties

Structural features of the glass family xLi₂O- yMgO (4.8 Bi₂O₃ 47.6 P₂O₅) obtained by melt quenching technique were studied taking into account the density, FTIR and UV–vis spectra and also the electrical response observed by impedance spectroscopy. In this work it becomes clarified how the alkaline earth oxides stabilize the glassy matrix and also, the fundamental importance of determining the optimal proportion in order to obtain a flabby easily polarizable matrix to enhance the electrical behavior due to a boosted cation mobility. It is evidenced that when the glass composition becomes complex it is needed to take into account a larger number of structural parameters to understand, to predict or to design the resulting physical properties.     

Tough salami-inspired Cf/ZrB2 UHTCMCs produced by electrophoretic deposition

One of the biggest challenges of the materials science is the mutual exclusion of strength and toughness. This issue was minimized by mimicking the natural structural materials. To date, few efforts were done regarding materials that should be used in harsh environments. In this work we present novel continuous carbon fiber reinforced ultra-high-temperature ceramic matrix composites (UHTCMCs) for aerospace featuring optimized fiber/matrix interfaces and fibers distribution. The microstructures – produced by electrophoretic deposition of ZrB₂ on unidirectional carbon fibers followed by ZrB₂ infiltration and hot pressing – show a maximum flexural strength and fracture toughness of 330 MPa and 14 MPa m^1/2, respectively. Fracture surfaces are investigated to understand the mechanisms that affect strength and toughness. The EPD technique allows the achievement of a peculiar salami-inspired architecture alternating strong and weak interfaces.     

Precipitating spinel into precursor glass and its assistance in crystallization

The crystallization phenomena of spinel in CaO-MgO-Al₂O₃-SiO₂-Fe₂O₃ glass have received much attention due to the particular role in preparation of glass-ceramic materials, which represent an effective option to manage hazardous waste. In this study, both preliminary spinel and secondary spinel were precipitated in the precursor glass. The formation of these spinel was meticulously assessed by a combination of X-ray diffractometry and scanning electron microscopy. The structure of the microenvironment in the precursor glass was characterized by Raman spectrums. These advanced techniques highlight the potential for one-step crystallization of the glass. The investigation, which focused on one-step crystallization, demonstrated the growth of pyroxene on spinel accompanying a migration of chromium. The results also show the microstructure of the obtained glass-ceramic was very dependent on the heat-treat temperature. This study not only unambiguously reveals the precipitation mechanisms of spinel but also provides more documentation for one-step crystallization in the glass-ceramics field.