用于镁质强化瓷的大红釉的研制

以硅酸锆包裹硫硒化镉[ZrSiO4@Cd(SxSe1-x)]为色料,长石-石灰混合生料为基釉,研制了一种适用于镁质强化瓷装饰用大红釉,研究了基釉的组成、升温速率、停留时间和燃烧气氛对呈色效果的影响。实验结果显示,该釉在氧化气氛烧成,烧成温度范围在1170～1250℃,釉料呈现鲜艳的大红色,适合用于镁质强化瓷,且完全无铅镉溶出。     

镁质强化瓷装饰用无铅镉溶出大红釉的研究

本文研制了一种适用于镁质强化瓷装饰用大红釉,大红釉以包裹型镉硒为色料,基釉为长石-石灰混合生料釉,氧化气氛烧成,烧成温度为1150~1270℃。结果表明,釉料完全无铅无镉溶出。并研究了基釉的组成、升温速率、停留时间和燃烧气氛对呈色效果的影响。最终获得了制备镁质强化瓷装饰用无铅无镉溶出大红釉制备技术。     

釉面分相对无铅CuO-MnO2系金属光泽釉的影响

以钙系生料釉为基础,引入结晶剂CuO、MnO₂制备无铅CuO-MnO₂系金属光泽釉;结合XRD、SEM-EDS进行物相组成定性分析和显微结构表征,系统探究外加TiO₂、V₂O₅以及玻璃粉对金属光泽釉釉面分相的影响。研究表明:一定量的TiO₂、V₂O₅引入能有效促进釉面的分相,将玻璃粉部分替换基础釉中的钾长石能使得釉熔体的高温粘度降低,并进一步加剧釉面分相,促进CuMn₂O₄铜锰尖晶石在釉层表面的析出和富集;当TiO₂引入量为2%,V₂O₅引入量为1%,玻璃粉引入量为25%(同为质量分数)时,金属光泽釉釉面效果最佳。     

Double layers glaze analysis of the Fujian export blue-and-white porcelain from the Witte Leeuw shipwreck (1613)

Witte Leeuw was a cargo ship owned and operated by the Dutch East Indian Company. The wreck of this vessel is known for yielding a comprehensive range of Jingdezhen manufactured, blue-and-white export porcelains, particularly kraak wares; together with Fujian blue-and-white export porcelains, known as Swatow wares. A large number of ceramic fragments have been recovered from this wreck and currently reside in collections at the Rijksmuseum. For this study nine ceramic specimens were selected for further investigation, with the aim of determining the structure, composition and manufacturing process of the double-layer glazes. Both digital optical microscopy and scanning electron microscopy were used to examine the glaze morphology and microstructure; whilst energy dispersive x-ray spectroscopy was utilised to measure the spatial distribution of chemical elements and to determine bulk elemental compositions. Raman spectroscopy was also trialled, with the technique being applied to the measurement of molecular vibrations within the silicon-oxygen network and associated alkali metal oxides, with the aim of identifying potential differences in the glaze layers. Examining the ceramic specimens, the blue decorations were applied between two layers of glaze, and the majority of the blue colour extends into the outermost layer, often exhibiting dissolution in the outer layer glaze. The two layers of the glaze appear to be formulated from different compositional recipes. Some export Swatow blue-and-white wares made in the Wanli Period (1573–1620) were glazed twice and fired twice.     

无锆生料乳浊釉的研制

通过合理设计釉组成,研制出了一种不含锆英石微粉的生料乳浊釉,应用X-ray衍射法及相图理论,初步探讨了实验释的物相组成及乳浊机理,同时分析了影响釉面质量的其他因素。     

低温快烧琉璃瓦的研制

利用丰富的红页岩、花岗岩风化砂、劣质粘土和硅灰石等原料,采用半干压成型和一次低温快烧工艺,代替传统生产工艺,制备高质量琉璃瓦,研究其工艺条件、坯釉配方以及釉坯显微结构.     

快烧无锆分相乳浊釉的形成

选择适合一次快速烧成的R2 O(K2 O ,Na2 O) -RO(CaO ,MgO ,ZnO) -Al2 O3-B2 O3-SiO2 系统 ,通过优化组成设计及物理化学过程的控制 ,实现了釉的自生分相乳浊 .实验结果表明 :快烧所得乳浊釉的分相结构中 ,一相富R2 + ,贫Si4+ ,B3+ 和Al3+ ;另一相则相反 .当(SiO2 +B2 O3)含量较高时 ,形成孤立液滴状分相结构 .釉面白度在 75以上的釉 ,其分相结构的共同特点为 :孤立相呈均匀分布的球滴状 (平均长短径比值z<1.2 ) ,其体积分数 φp 超过 3 5 % ,球滴的平均等效直径D落在 0 .15～ 1.3 2 μm范围内 ,接近可见光的波长范围 ,有利于强化乳浊效果     

搪瓷烧成温度计算方法的探讨

搪瓷釉的烧成过程是一种“液相烧结”过程,其传质有赖于熔体的粘性流动。根据玻璃态物质化学组成—结构—粘度—温度的一般关系,推导出计算瓷釉烧成温度(T_烧)的经验公式。     

常温远红外陶瓷粉和远红外日用陶瓷的研究

远红外日用陶瓷不仅对食物、饲料、水有活化作用，加速酒的发酵和成熟，而且对人体还具有保健功能。本研究采用液相法制备出纳米远红外陶瓷粉，把远红外陶瓷粉按适当比例掺入普通陶瓷釉浆中，制成常温下具有高效发射锭红外线功能的日用陶瓷产品。如瓷碗、盘、茶杯、酒具等。脸用XRD分析其物相和SEM观察其显微结构、结果表明，当远红外陶瓷粉在基釉中的添加量为10wt％时，可提高日用陶瓷釉面的光泽度和显微硬度，且釉面质量优良。经中国计量科学研究院测试，远红外陶瓷粉的法向全辐射发射率94％，远红外日用陶瓷的法向全辐射发射率达到83％以上。     

外加剂对陶瓷釉面表面性质的影响研究

研究了不同外加剂对陶瓷釉面表面性质的影响。研究表明 ,外加剂的加入可改变陶瓷釉面的表面张力 ,即影响液体对陶瓷釉面的润湿性能。在所选择的外加剂中 ,降低陶瓷釉面表面张力最强的为PbO ,其合适的加入量为 1.5 %。