焊接接头微观组织演化的可视化模拟

本文主要针对焊接接头微观组织演化建模及其可视化方法进行研究。采用元胞自动机模型,通过对焊接接头的微观组织晶粒生长进行模拟来分析和研究微观组织的形态学和动力学特征;通过微观组织图像人工生成技术,直观、精确地展现出微观组织演化的可视化效果。实验结果表明,经过回归分析得到的晶粒生长指数同主流的Burke经验公式相符,使用元胞自动机算法对微观组织演化进行的可视化模拟得到了令人满意的效果。     

BaTiO3系PTCR材料电学性能的复阻抗解析

采用复阻抗解析法研究了ＢａＴｉＯ３系ＰＴＣＲ材料晶粒、晶界的电学性能。结果表明：使用欧姆接触电极的ＰＴＣＲ材料等效电路的复阻抗为：晶粒电阻呈ＮＴＣ特性，而晶界电阻天Ｔ〈Ｔｃ时呈ＮＴＣ特性，Ｔ〉Ｔｃ时呈明显的ＰＴＣ特性；ＰＴＣ效应是一种晶界效应。     

Effect of Ba6Ti17O40/BaTiO3 Interface Structure on {111} Twin Formation and Abnormal Grain Growth in BaTiO3

A structural transition of Ba₆Ti₁₇O₄₀/BaTiO₃ interfaces from faceted to rough was induced by reducing oxygen partial pressure in the atmosphere. As the oxygen partial pressure decreased, the number densities of {111} twins and abnormal grain decreased. TEM observation showed that the twin formation was governed only by the faceting of the interface. Experimental evidence of {111} twin-assisted abnormal growth of faceted BaTiO₃ grains was also obtained.     

Effects of molasses grass,Melinis minutiflora volatiles on the foraging behavior of the cereal stemborer parasitoid,Cotesia sesamiae

Olfactory responses of the cereal stemborer parasitoid Cotesia sesamiae to volatiles emitted by gramineous host and nonhost plants of the stemborers were studied in a Y-tube olfactometer. The host plants were maize (Zea mays) and sorghum ( Sorghum bicolor), while the nonhost plant was molasses grass (Melinis minutiflora). In single-choice tests, females of C. sesamiae chose volatiles from infested and uninfested host plants and molasses grass over volatiles from the control (soil). In dual-choice tests, the wasp preferred volatiles from infested host plants to those from uninfested host plants. There was no discrimination between molasses grass volatiles and those of uninfested maize, uninfested sorghum, or infested maize. The wasp preferred sorghum volatiles over maize. Combining uninfested maize or sorghum with molasses grass did not make volatiles from the combination more attractive as compared to only uninfested host plants. Infested maize alone was as attractive as when combined with molasses grass. Infested sorghum was preferred over its combination with molasses grass. Local growth conditions of the molasses grasses influenced attractiveness to the parasitoids. Volatiles from Thika molasses grass were attractive, while those from Mbita molasses grass were not. Growing the Thika molasses grass in Mbita rendered it unattractive and vice versa with the Mbita molasses grass. This is a case of the same genotype expressing different phenotypes due to environmental factors.     

Bi对Al-30% Mg_2Si复合材料组织和性能的影响

为了研究铋(Bi)对Al-30%Mg2Si复合材料显微组织和力学性能的影响,利用原位内生工艺制备了Al-30%Mg2Si复合材料,并加入不同量的Bi对其细化变质.利用扫描电镜进行显微组织观察,并利用布氏硬度计和液压式万能试验机进行力学性能测试.试验结果显示,稀土Bi的质量分数由0%增加至5%时,初生相Mg2Si的平均晶粒尺寸先减小后变大,而抗拉强度、硬度和伸长率则先提高后减小;当Bi加入量约为3%时,初生相Mg2Si显微组织细化效果最为明显,综合力学性能最好.     

Refinement mechanism of in-situ Al4C3 particles on AZ91 magnesium alloys

The effects of SrCO3 on the microstructure of AZ91 magnesium alloy were investigated by OM, SEM, EDS, XRD and DTA analyses. The results show that AZ91 magnesium alloy with 1.0% SrCO3 addition has the best refining effect at 730 ℃ for 20 min, the average size of the α-Mg grain in AZ91 matrix alloy is reduced from about 91 μm to 58 μm, with reduction of about 36%. Based on the analysis results of EDS, binding energy, and Gibbs free energy, it is evident that the grain is refined because of the generation of A14 C3 particles which can be used as the crystal nucleus of the magnesium alloy when SrCO 3 is added. Owing to the generation of A14C3 in AZ91 magnesium alloy, the grain boundary is pined and the grain growth is inhibited. In the accession to the Al4C3, small subcooling temperature difference leads to the formation of fine grain microstructure in alloy melt. Fine grain microstructure in AZ91 alloy melt with the addition of SrCO3 can be obtained on the condition of lower undercooling temperature according to the DTA analysis results.     

不同温度下AZ31镁合金绝热剪切变形局域化

为了了解镁合金在不同温度高应变率载荷作用下发生变形局域化的特点,进而揭示镁合金在高速冲击载荷作用下发生绝热剪切的特殊规律,采用分离式Hopkinson压杆对挤压态AZ31镁合金进行了常温及高温的高速冲击压缩试验,而后对不同温度冲击后的试样通过光学显微镜、扫描电镜和透射电镜进行变形机制的分析.结果表明:常温下试样在受到剪切力后,在剪切区的裂纹周围产生了大量的孪晶;高温下试样的剪切区内产生了明显的绝热剪切带,并且在剪切带周围发现了大量平行的孪晶.在TEM下观察到剪切带内为等轴晶晶粒,在剪切区内发生了动态再结晶过程.     

混菌固态发酵小曲白酒糟生产蛋白饲料的研究

以小曲白酒糟为原料,添加纤维素酶制剂预处理原料,采用白地霉、假丝酵母混菌固态发酵,生产蛋白饲料。确立了糟麸比、纤维素酶预处理方式、初始pH值、初始含水量、料层厚度、发酵时间和温度。对发酵产品的分析表明：粗蛋白增幅87．5％,粗纤维降解率达20．1％,粗脂肪降解率为61．81％。     

Microstructure and mechanical properties of AZ31 alloy ingot fabricated by semi-continuous casting

The AZ31 alloy ingot with diameter of 110 mm and length of 3500 mm was fabricated successfully. The compositions and microstructure morphologies of the ingot at different locations were performed, which indicated that the chemical composition distributed homogeneously through the whole alloy ingot and the average grain size increased from the surface to the center. The results of the EDS and element face-scanning illustrated that the eutectic compounds mainly consisted of fl-Mg17Al12 and a small amount of fl-Mgl7（AlZn）12. Furthermore, slight improvements of the strength and ductility were observed from the center to the surface along the axial direction of the alloy ingot, while both the strength and elongation to failure of the samples along the radial direction are higher than that along the axial direction. The fine grain strengthening was the main contributors to the strength of the as-casted AZ31 alloy.