电镀锌板流星状白色亮斑缺陷的研究

低碳钢(w(C)≤0.06%)作为电镀锌基材,在热轧轧制时易发生混晶现象。该缺陷表现为钢板表面电镀锌后,上表面出现流星状白色亮斑缺陷。通过冷轧和热轧原板样的金相检测,判断亮斑缺陷与基板混晶存在关联,且源于热轧工序。并对混晶发生的原因进行了分析,开展了相应的工艺调整试验,确认混晶与热轧FT7、CT目标值设定相关性显著。最终通过对FT7、CT工艺的联合调整,亮斑缺陷得以消除。     

00Cr17Ti热带退火对冷轧薄板表面皱折的影响

 通过对00Cr17Ti经热带退火、不经热带退火两种工艺的冷轧板进行对比试验,在分析显微组织、织构的基础上,研究了热带退火对00Cr17Ti薄板表面皱折的影响。研究结果表明：与不经热带退火相比,经热带退火能使成品薄板的表面皱折大大减轻,最大粗糙度仅为12.06 μm,平均粗糙度仅为1.27 μm。两种工艺的成品板表面皱折程度的不同是由两者在显微组织、微织构上的差异造成的。与不经热带退火相比,经热带退火的成品薄板在板厚方向具有较均匀的组织,板宽方向的织构梯度较小,晶粒簇较间断、细窄、分散,所有这些使得成品薄板的表面皱折大大减轻。为了满足用户对薄板表面质量的严格要求,对热轧带进行退火是很有必要的。     

载金炭解吸率低原因分析及预防措施

对脱金炭制成的薄片和光片进行镜下观测分析发现,碳酸盐对炭部分区域覆盖包裹和金粒镶嵌在炭孔隙中是使循环用活性炭活性下降、吸附金能力降低、载金炭解吸率低的主要原因.通过加强生产技术管理,采取相关措施,减少或避免碳酸盐包裹的生成及杂质进入活性炭,防止微细金粒夹带到解吸液进入活性炭孔隙,可有效改善循环使用活性炭的吸附金活性及提...     

A Study of Grain Growth Kinetics in Sintered NdFeB Magnets

ＵｐｔｏｎｏｗｈｉｇｈｐｅｒｆｏｒｍａｎｃｅａｎｉｓｏｔｒｏｐｉｃＮｄＦｅＢ ｔｙｐｅｍａｇｎｅｔｓａｒｅｍａｉｎｌｙｍａｎｕｆａｃｔｕｒｅｄｂｙｔｈｅｐｏｗｄｅｒｍｅｔａｌｌｕｒｇｙｔｅｃｈｎｉｑｕｅ[1] .Ｔｈｅｆｉ ｎａｌｍｉｃｒｏｓｔｒｕｃｔｕｒｅｏｆｓｉｎｔｅｒｅｄＮｄＦｅＢｍａｇｎｅｔｓｉｓｄｅｔｅｒｍｉｎｅｄｂｙｔｈｅｐｒｅ ａｌｌｏｙｐｏｗｄｅｒｐａｒａｍｅ ｔｅｒｓａｎｄｓｉｎｔｅｒｉｎｇｃｏｎｄｉｔｉｏｎｓ .Ｔｈｅｔｅｃｈｎｏｌｏｇｉ ｃａｌｉｍｐｏｒｔａｎｃｅｏｆＮｄ2 Ｆｅ14 Ｂｇ…     

氧化物冶金技术的最新进展及其实践

文中介绍了氧化物冶金技术提出的背景,该技术的主要内容和采用该技术对钢的组织、性能的影响.总结了该技术近十几年来在利用夹杂物钉扎晶粒的高温长大和形核晶内铁素体(特别是其机理探讨)方面的相关研究,介绍了国外一些钢铁公司在大线能量焊接过程中所开发的该领域的新技术和新应用,同时介绍了氧化物冶金技术在焊接以外的凝固、压力加工、非调质钢和厚板生产等过程中的研究和应用的最新进展.文末展望了该技术的发展趋势.     

晶界扩散Tb对烧结Nd-Fe-B组织与磁性能的影响

用磁控溅射法在烧结Nd-Fe-B磁体表面沉积Tb金属薄膜并进行晶界扩散处理,对比经不同热扩散温度及时间处理后的磁体组织和磁性能变化.结果 表明,925℃×10 h+500℃×2 h为最佳晶界扩散工艺,可将磁体矫顽力提高到1630.9 kA· m-1,较原始磁体提升50％,同时剩磁和磁能积无明显下降,磁体仍具有较高的退磁...     

Rapid growth of angle-confined large-domain graphene bicrystals

In the chemical vapor deposition growth of large-area graphene polycrystalline thin films,the coalescence of randomly oriented graphene domains results in a high density of uncertain grain boundaries (GBs).The structures and properties of various GBs are highly dependent on the misorientation angles between the graphene domains,which can significantly affect the performance of the graphene films and impede their industrial applications.Graphene bicrystals with a specific type of GB can be synthesized via the controllable growth of graphene domains with a predefined lattice orientation.Although the bicrystal has been widely investigated for traditional bulk materials,no successful synthesis strategy has been presented for growing two-dimensional graphene bicrystals.In this study, we demonstrate a simple approach for growing well-aligned large-domain graphene bicrystals with a confined tilt angle of 30° on a facilely recrystallized single-crystal Cu (100) substrate.Control of the density of the GBs with a misorientation angle of 30° was realized via the controllable rapid growth of subcentimeter graphene domains with the assistance of a cooperative catalytic surface-passivation treatment.The large-area production of graphene bicrystals consisting of the sole specific GBs with a tunable density provides a new material platform for fundamental studies and practical applications.     

Al-Sn 合金中两个不同类型的内耗峰

Al-Sn 合金多晶样品中,在传统晶界峰的高温侧发现了两个不同类型的内耗峰(记作 P_1,P_2峰),它们在单晶中均消失,因而与晶界相关。P1与晶界峰有消长关系,对时效和退火温度敏感,仅在降温过程中出现,是过程峰,存在于 Al-0.008wt-%Sn 和 Al-0.0135wt-%Sn 多晶试样中;P_2与晶粒尺寸和样品尺寸相关,是稳定的内耗峰,存在于 Al-0.067wt-%Sn 和 Al-0.136wt-%Sn 多晶试样中。P_1,P_2峰分别来源于被Sn 原子非平衡偏聚的细晶界和含有 Al-Sn 沉淀粒子的粗晶界。     

过量PbO对TGG法定向生长PMNT多晶体动力学影响的研究

采用传统陶瓷工艺和添加过量 Pb O的 TGG方法实现了 PMNT多晶体沿 <0 0 1>方向的定向生长 ,对多晶体定向生长的动力学进行了详细的研究。结果表明 ,PMNT多晶体定向生长的厚度随过量 Pb O的增加而线性增加 ,它的生长是热激活扩散与溶解 -沉积过程二者综合作用的结果。只要选择适当的生长时间 ,在 PMNT基体中添加过量的Pb O,不但不会影响陶瓷的组分还可以显著提高多晶体的定向生长速度。而且 ,PMNT多晶体定向生长厚度与生长时间的 1/3方呈线性关系 ,属于典型的扩散控制的生长行为。实验表明 ,采用添加 2 0 %过量的 Pb O、在 115 0℃生长10 h是制备 PMNT取向多晶体较为合适的工艺条件