高速气流冲击式粉体表面改性装置——HYBRIDIZATION系统及应用

利用高速气流冲击法进行粉体/粉体系表面改性技术,是迄今为止各种粉体材料开发中最为引人注目的技术之一。HYBRIDIZATION(下称HYB)系统是利用高速气流冲击法对微粉体进行干式/机械化处理,是使材料复合化的最实用的装置,可对各类有机物、无机物、金属等进行广泛组合,通用性很强,适用于许多行业领域。从本文所述的系统构成、型式,有关的典型球形化处理的运转特性,利用复合化高温粉体测定被处理粉体表面温度,利用颜料改变色调等的处理特点及该系统的适用性等(一部分是从已发表的学术论文及专利上摘录的),可以说明HYB系统的概况。     

自控温加热带的研制

研究了炭黑含量、辐照剂量以及体系共结晶性对以高密度聚乙烯/乙烯 丙烯酸乙烯酯共聚物为基材的自控温加热带电阻率及电热稳定性能的影响,以及加工条件和后处理工艺对材料电性能的影响。结果表明,50～80kGy的辐照剂量为本体系提供优异的电热稳定性,适当的加工及后处理工艺能大大改善该体系的导电性。     

6m大容积焦炉烘炉实践与体会

介绍了 6 m大容积焦炉由冷态到转入正常加热温度的烘炉操作过程中 ,按照一定的升温曲线 ,通过对焦炉热工和炉体膨胀的科学管理 ,确保新建焦炉顺利由冷态过渡到生产状态。     

IR study of the interaction of hydroxyl groups of silica gel with Cr species of Phillips' type catalysts

Spectroscopic evidence for the interaction of hydroxyl groups and chromium ions was obtained using a catalyst prepared from chromyl chloride. A new OH peak, observed at 3705 cm^–1 after pumping away CO gas, is attributed to the direct interaction of OH with the low-valent chromium. This peak shifts to 3590 cm^–1 on contact with O₂ at room temperature and it is assigned to a hydroxyl interacting with the oxidized chromium. New assignments are also proposed for IR bands of CO presorbed on the catalyst. The peak due to CO at 2188 cm^–1 decreases as the OH intensity at 3705 cm^–1 increases, suggesting that the former peak arises from adsorption on Cr(II) species to which two oxygen atoms are attached.     

Carbon Aerogels as Electrode Material in Supercapacitors

Due to their large specific surface area and their high electrical conductivity carbon aerogels are promising materials for electrodes in electrochemical double-layer capacitors (supercapacitor). The carbon aerogels were made via pyrolysis of resorcinol formaldehyde aerogels. The latter were prepared by supercritical and subcritical drying as well. The important findings of our investigation were, that the highest capacities of 46 F/cm³ were measured for samples with a density of about 800 kg/m³ pyrolyzed at 800°C. Also it was shown that RF-gels with molar resorcinol/catalyst ratios 1000 or higher can be dried subcritically without cracking or significant shrinkage. Carbon aerogels derived from these RF-aerogels have a small mesopore surface area, however an especially large micropore area. They provide electrical capacities which are most suitable for their use in supercapacitors.     

Effect of particle size on the surface oxidation and flotation behavior of galena particles in lime system

ABSTRACT

In this research, the effect of particle size on the surface oxidation and flotation behavior of galena in the lime system was studied. Coarse (?0.074 + 0.038 mm), intermediate (?0.038 + 0.025 mm) and fine (?0.025 mm) galena particles were used in the experiment. The dissolution tests, flotation tests, and sorption tests were accomplished. Through further analysis by XPS, the effect of particle size and lime was observed. The decrease of mineral particle sizes increased the adsorption ratio of collector and the dissolution of galena, while the hydrophilic product OH^?/Ca(OH)⁺ produced by dissolution occupied the dominant position, which led to the minerals hydrophilic.     

碳纤维经氧等离子/KH550处理后的表面形态和结构

碳纤维(CF)表面经氧等离子、KH550和 LiAlH_4处理后,其物理和化学性能得以改善.由于提高了 CF 和树脂间的联结,使 CF 复合材料的层间剪切强度提高50%以上,在湿热下的强度保留率达94%以上.使用纤维接触角测定仪,SEM 和 XPS 等对 CF 表面的浸润性、形态和化学组成进行了研究.实验指出:CF 经等离子和 KH550处理后,其临界表面能有了提高;CF 本身仅受氧离子刻蚀,故其拉伸强度的损失小于其他处理方法.     

纳米碳酸钙的表面活化改性研究

本文主要介绍通过加入特定的表面改性剂,制得了表面改性的活性碳酸钙.并对活化过程中的一系列影响因素,如活化温度、活化时间、碳酸钙悬浊液浓度、表面改性剂用量进行了研究.     

改性活性炭的表面特性及其对苯酚的吸附性能

研究了表面改性对活性炭吸附苯酚性能的影响。研究发现,硫酸氧化可增加活性炭表面酸性基团的含量,提高了活性炭的表面亲水性,降低pHPZC值,因而对吸附水中的苯酚的性能产生明显影响,降低了对苯酚的吸附。