Oxidation behavior of TiAl coated with a fine-grain Co-30Cr-4Al film

The oxidation behavior of TiAl coupons coated with a fine-grain Co-30Cr-4Al (mass %) film of about 30-m thickness has been studied at 1100–1400 K in a flow of purified oxygen at atmospheric pressure for up to 500 ks. Three oxidation stages were recognized: initial transient, parabolic, and accelerated stages. However, at 1100 K a parabolic stage continues for more than 800 ks. The activation energy for parabolic oxidation agrees with reported values for the oxidation of alumina-former alloys, although the mass gains during the parabolic stages are relatively small at 1200 and 1300 K. Micropores developed mainly at the scale/coating and coating/substrate interfaces as oxidation proceeded. This is attributable to recrystallization of the coating during oxidation and a Kirkendall effect due to preferential diffusion of Co into the substrate. The accelerated oxidation can be explained in terms of the formation of rutile mounds on the scale.     

高铝锌基合金粉末冶金材料及其摩擦学特性初探

初步研究了高铝锌基合金的粉末冶金工艺及其材料的摩擦磨损性能。通过气喷气冷法制取合金粉末，用压制后真空烧结的方法制备高铝锌基合金粉末冶金材料。实验结果表明，高铝锌基合金的粉末冶金试样在干摩擦和油润滑条件下的磨损率及摩擦系数均小于同一合金的铸造试样，但其压溃强度有待提高。在实验的基础上还探讨了该材料的耐磨减摩机理     

高硅铸钢的强韧化机理

采用X射线衍射，计算了高硅铸钢等温淬火热处理后的贝氏体铁素体含碳量，采用TEM分析了贝氏体铁素体中的错位，研究了贝氏体铁素体板条尺寸与高硅铸钢屈服强度、硬度间的关系。在此基础上分析了高硅铸钢的强化以及韧化机理，高硅铸钢的强化是固溶强化，位错强化和细晶强化综合作用的合理；而高硅铸钢的韧化是存在于贝氏体铁素体板条之间富碳的薄膜状残余奥氏体，细小的贝氏体铁素体板条共同作用的结果。合适的Si含量也是影响高硅铸钢韧性重要因素。     

高精度管材拉拔过程计算机模拟研究

开发了一种适用于生产高精度管材的新型芯棒形式,利用MSC.MARC/AUTOFORGE有限元仿真软件,模拟了高精度管材的拉拔过程,分析了变形区金属变形规律、应力分布状况及拉拔力变化规律及芯棒形式与模具尺寸参数对高精度管材尺寸精度的影响规律,得出了合理的模具参数,为科研和生产提供有效的帮助。     

高速钢中贝氏体的二次硬化特征

研究了6-5-4-2高速钢中贝氏体和马氏体回火后的力学性能和组织结构。结果表明,贝氏体比马氏体具有更高的二次硬化效应以及抗回火稳定性和冲击韧性。透射电镜观察发现,马氏体在二次硬化峰温度范围回火时,有Fe_3C析出,而贝氏体铁素体和奥氏体中只析出弥散的MC和M_2C合金碳化物。这表明在贝氏体长大过程中存在合金元素的扩散。     

标准差S在材料疲劳寿命分析中的作用

目前,在评价材料的疲劳强度时,往往只注重比较材料的中值疲劳寿命,而忽略了对数据分散性的比较.事实上,数据分散性,尤其是标准差S在评价材料疲劳性能时非常重要.本文通过对比几组相同试验条件下中国和美国生产的同一铝合金材料的疲劳数据发现:两个产地材料的中值疲劳寿命基本接近,但美国产材料疲劳数据的标准差S小.其对应99.99%存活率的疲劳寿命也明显高于国产材料,这表明标准差大小对高存活率下的疲劳寿命影响很大.因此,应对标准差S给予高度重视.     

等离子无模成形叶轮的应力场分析与校核

等离子熔积无模成形是急速加热快速凝固的短流程制造技术,如何避免制件的热裂纹是该技术的关键,而热裂纹的产生取决于成形过程温度场与应力场的分布特征.用有限元法对预热和水冷两种温控方案进行了模拟仿真,对比分析可知,较预热成形,水冷成形零件表面质量良好、热裂倾向低.随后依水冷条件按跳跃路径计算了叶轮成形过程的热应力场.结果表明,该方案所得零件的温度场较均匀,热应力和热裂倾向显著降低,工艺合理,有利提高成形性.     

Effects of current waveform parameters during droplet transfer on spatter in high speed waveform controlled Short-circuiting GMAW

Aim at improving the stability of the Short-circuiting Gas Metal Arc Welding （GMAW-S） process for the enhanced speed usage, effects of current waveform parameters during short-term on the welding stability have been investigated by experimental method. The welding power source used for the research is an inverter with a special current waveform control. It is shown that the spatter decreases at first then increases with each increase of the low current period, current increase rate and the maximum current limit. The test results are provided for welding of 1 mm and 3 mm mild steel at speed of 1.2 m/min. The stable GMA W-S process under high speed welding condition has been achieved by optimizing the parameters.     

弛豫铁电体Pb(Mg1/3Nb2/3)O3-PbTiO3的相变

测量了(1-x％)镁铌酸铅-x％钛酸铅(1≤X≤11)(简称PMNTx)陶瓷样品的介电常数、内耗和Young’s模量．观测到在Tm温度附近，即在介电常数达到最大值时，出现一个内耗峰，并且模量发生软化．这反映了极化纳米微畴的弛豫．对于PMNTx(5≤x≤11)的样品，在Tm温度以下的某个温度出现附加的内耗峰和Young’s模量的异常，表明样品中发生了自发的弛豫铁电到铁电(简称R-F)的相变，对R-F相变的机制进行了讨论．     

高压缸液态挤压成形压力的分析及计算

采用液态挤压代替压力铸造生产铝合金高压缸，不仅克服了压铸件内部易形成气孔和氧化夹杂物的缺陷，而且提高了成品率，降低了产品成本，在分析了高压缸液态挤压成形过程的基础上，提出了成形压力计算的简化模型，并采用变形功法推导了成形压力计算公式，得到了适合实际应用的结果。