对低品位钛铁矿进行预氧化、预还原等预处理后可满足硫酸法生产钛白粉工艺所需高品位钛铁矿的要求。本试验采用流态化预氧化方法处理风化程度低、含硫较高的钛铁矿。结果表明 :流态化氧化可大幅度地降低钛铁矿中硫含量 ;钛铁矿流态化氧化的适宜温度为 :80 0～ 90 0℃ ,且在此温度范围内 ,随温度的升高 ,钛铁矿的氧化速度增加 ,在 90 0℃时 ,5 0min钛铁矿基本能完成氧化     

VPI粉云母带的选型试验研究

为电机主绝缘VPI工艺选择合适的粉云母带，对几种真空压力浸渍(VPI)用云母带进行了试验研究，分析了选型原则，同时对比了几种粉云母带的性能。将它们应用于模拟线棒中，线棒的试验数据表明：选出的两种云母带的配合可获得优异的性能，达到优等品标准水平。再将少胶云母带应用于电机整机试验，试验结果表明达到了减薄绝缘、降低温升、延缓绝缘老化、提高电机使用寿命的目的。     

沙角C电厂2号发电机转子接地检测装置改造

介绍沙角发电C厂2号发电机转子接地检测装置的基本原理和在装置发出报警信号后的分析和判断过程。对该装置出现故障后ALSTOM公司提出的临时检测方案作了分析，指出了该方案的不足之处，提出并实施改进后的临时检测方案。     

单壁纳米碳管/纳米铝基复合材料的增强效果

用半连续氢电弧法和活性氢等离子蒸发法分别制备出单壁纳米碳管(SWNTs)和纳米A1粉体，然后用提纯后的SWNTs和纳米A1粉体制备出SWNTs含量(质量分数)分别为0、2．5％、5．0％、7．5％和10.0％的单壁纳米碳管／纳米铝基块体复合材料．SWNTs对高强度纳米A1基体具有显著的增强作用，当SWNTs含量小于5．0％时，材料的硬度随着SWNTs含量的提高线性上升．其中5％SWNTs和纳米A1的复合增强效果最好，其硬度可达2.89GPa，大约是粗晶A1(0．15GPa)的20倍．当SWNTs含量超过5．0％时，增强效果开始缓慢的下降．讨论了单壁纳米碳管增强纳米铝基复合材料的强化机制．     

Preparation of Compound Ultrafine CeO2 by Wet-Solid-Phase Mechanochemical Modification

To satisfy practical requirements from industrial applications, an alternate route for synthesis compound ultrafine CeO2 powders by wet-solid-phase mechanochemical modification using industrial grade hydrated cerium carbonate as raw material was proposed.The effect of modifier reaction percentage, reaction time, calcining temperature and modifier amount on particle size, density, suspensibility, and hardness of compound CeO2 powder was investigated.The phase evolutions of preparation process were characterized by XRD.SEM micrograph of the final product shows that compound CeO2 powders obtained are well-dispersed, spherically-shaped, uniformly-sized and submicron-sized particles.The method is readily available in raw material, low in cost, simple in process, and has great potential for industrialization.The compound CeO2 powders of different physical properties can be synthesized by controlling the above-mentioned influence factors in preparation process.     

Delay discounting of real and hypothetical rewards.

The degree to which real and hypothetical rewards were discounted across delays ranging from 6 hr to 1 year was explored in a within-subjects design. An adjusting-amounts procedure was used to estimate the subjective value of real and hypothetical rewards at each delay. A hyperbolic discounting function provided a significantly better fit to individual participants' preferences than did an exponential function. No significant effect of reward type on degree of hyperbolic discounting or area under the discounting curves was detected. These findings offer some support for the validity of using hypothetical rewards to estimate discounting rates in substance-abusing and other populations, but caution is suggested because this support is gleaned from a failure to detect an effect of reward type. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

Question hard, answer simply: A comment on Storms et al. (2003).

It seems clear that, for whatever reasons, the dementia of the Alzheimer type patient group (as well as other patient groups) exhibits behavior that is different from the normal control group. G. Storms, T. Dirikx, J. Saerens, S. Verstraeten, and P. P. De Deyn (2003) rightfully argue that the observed behavior (similarity judgments) does not tell us the source (cause) of the differences between the 2 groups. Rather, the focus of the study should be placed more on finding the ways the 2 groups are different. They also point out various methodological problems in some of the previous attempts to characterize the nature of the differences. Further methodological issues in G. Storms et al.'s study are examined. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

高压水射流技术粉碎原盐的研究

以原盐为被粉碎研究对象,通过对高压水射流粉碎原盐形貌的观察和成分分析、高压水射流原盐粉碎性能分析,以及高压水射流粉碎原盐各影响因素的正交分析,研究表明高压水射流粉碎技术对原盐具有良好的解理性且粉碎效率高、耗能低。各因素对原盐粉碎效果的影响顺序为:射流压力卤水喷嘴直径、料液混合喷嘴直径、靶面形状。     

汽轮机轴承烧瓦与轴颈的渗巴氏合金现象

简述轴承工作性质，巴氏合金应用与相组成的基本情况。论述汽轮机转子在两个电厂长期运行后，由于轴颈发生的不正常摩擦损伤，在大修改造中由无损检查、机械加工揭示出轴颈存在严重的渗巴氏合金现象，低熔点金属Sn、Sb与Cu向转子材料晶界的深层渗入最终导致了3根大型在投转子的严重开裂与报废。图11表2     

低松装密度水雾化铜粉工艺的研究

本文研究了氧化 还原法生产铜粉的新工艺 ,该工艺是通过氧化还原将水雾化铜粉加以表面改性 ,形成海绵状的粉末 ,显著降低水雾化铜粉的松装密度 ,这种铜粉既具有电解铜粉低的松装密度 ,又具有水雾化铜粉高的流动性。讨论了氧化时间、氧化温度对铜粉松装密度的影响。本工艺是一种新型环保、节能、可替代电解法生产铜粉的先进工艺