Ni基高温合金表面涂覆Al_2O_3-SiO_2涂层的高温氧化特性研究(英文)

在高温合金表面涂覆耐高温陶瓷涂层是一种提高合金高温性能的有效方法。本研究按照铝、硅元素摩尔比3:2的比例,采用溶胶-凝胶法制备Al2O3-SiO2复合溶胶,并涂敷于Ni基高温合金表面。为考察该涂层的高温氧化特性,分别对涂层进行1000和1200℃下20h长时热处理和800℃循环氧化20次试验。利用SEM观察涂层表面和截面的微观状态,利用红外光谱(FT-IR)分析凝胶的结构变化。结果表明,复合涂层与Ni基高温合金基体间结合紧密,在1000℃长时间热处理后涂层无明显剥落,并可经历800°C多次热循环处理,具有良好的耐高温氧化特性。     

PVD技术在镁合金表面防护领域的应用及研究进展

综述了近年来国内外镁合金表面PVD技术制备的膜层对其耐蚀性的影响研究,提出:PVD膜层能够降低镁合金的腐蚀电流,提高其耐蚀性;造成膜层失效的主要原因是由于膜层中存在的微孔等结构缺陷充当了腐蚀通道;通过膜层体系的结构设计、制备工艺参数优化等方法,可降低膜层结构缺陷、提高膜基体系耐蚀性.     

Investigation on dual corrosion performance of magnesium-rich primer for aluminum alloys under salt spray test (ASTM B117) and natural exposure

Magnesium-rich primers perform very well on outdoor exposure and actual test conditions, yet fail rapidly in accelerated corrosion testing (salt spray test - ASTM B117). To investigate the behavioral dichotomy, Mg-rich primers exposed to salt spray testing and natural weathering were characterized at periodic intervals. The results revealed the presence of a thin and porous magnesium hydroxide layer in primers exposed to salt spray, and in natural exposure, a thicker, protective magnesium carbonate layer was detected and characterized. Samples exposed to atmospheric carbon dioxide exhibit excellent corrosion resistance but salt spray conditions are not conducive to facilitate magnesium carbonate formation.     

20% Al2O3-SiO2(sf)/AZ91D镁基复合材料微弧氧化陶瓷层电化学腐蚀性能

在磷酸盐体系电解液中,对20%(体积分数)硅酸铝短纤维(Al2O3-SiO2)增强AZ91D镁基复合材料进行微弧氧化表面处理获得陶瓷层。利用扫描电子显微镜(SEM)和X射线衍射(XRD)仪分析陶瓷层的表面形貌、截面组织和相组成,采用动电位极化和电化学阻抗谱(EIS)测试评价微弧氧化陶瓷层的电化学腐蚀性能。结果表明,该陶瓷层主要由MgO和MgAl2O4相组成。陶瓷层的腐蚀电流密度比镁基复合材料基体低3个数量级,电化学阻抗大幅升高,耐腐蚀性能明显高于复合材料基体     

Nanoindentation and scratch behaviour of Ni–P electroless coatings

ABSTRACT

In the present paper, the mechanical properties and the scratch failure mechanisms of Ni–P electroless coatings are described. The material microstructure was studied in as-deposited and annealed conditions through SEM and EDS analyses. Nanoindentation measurements on the coatings showed a remarkable hardening due to the crystallization and precipitation behaviour produced by annealing. The scratch tests, conducted by increasing the load during scratch, revealed the coating failure mechanisms in a broad range of applied stresses up to delamination.     

草浆黑液的化学改性和作为混凝土减水剂的应用

采用催化氧化再磺化工艺制备了水溶性草浆黑液木质素磺酸盐(SBT-LSN)混凝土减水剂。混凝土试验结果表明,经磺化改性后的产品分散性能得到明显改善,在0.25%掺量下,混凝土减水率达11.4%,含气量为4%,有一定的缓凝作用;对混凝土抗压强度有较大的提高,3d和28d抗压强度比分别达125%和110%,对混凝土早期强度的改善更明显。其适宜的掺量范围为水泥含量的0.1%～0.5%,适合于配制C40(及以下)中低强度混凝土。     

弹性建筑涂料不合格配方的比较研究

利用红外光谱、热失重分析、动态热机械分析等方法,对多款不同厂家生产的不合格弹性建筑涂料进行了配方分析,讨论了不合格弹性建筑涂料的配方的缺点,建立了利用动态热机械分析方法快速鉴别不合格弹性建筑涂料的方法。     

ICP-AES法测定黑色石材全组分元素的研究

采用偏硼酸锂熔样,电感耦合等离子体原子发射光谱(ICP-AES)法对黑色石材实现了一次熔样、全组分同时分析。对影响其光谱测量的各种因素进行了较为详细的研究,确定了实验的最佳测定条件。结果表明,方法的检出限为0.005～0.796μg·mL-1,回收率为93.16%～107.80%,RSD小于3.79%。该法准确、快速、简便,应用于黑色石材中全组分的测定,结果满意。     

熔盐环境下热障涂层的等温热腐蚀行为研究

采用电子束物理气相沉积（EB-PVD）在镍基高温合金表面制备了YSZ/NiCoCrAlY双层结构热障涂层,研究了其在熔盐环境下的等温热腐蚀行为。结果表明,涂层在加热过程中发生相变引起体积收缩,导致涂层内部产生微裂纹。熔盐填充涂层内微裂纹和柱状晶间隙,降低了涂层的应变容限,引起涂层内应力升高。同时,熔盐促使热生长氧化层（TGO）碱性溶解,产生疏松多孔的氧化物层,导致TGO层加速增厚。在热应力作用下,疏松层氧化物破碎,最终导致涂层剥落。     

镁合金表面处理的研究进展

综述了热喷涂、表面激光熔覆、化学转化膜、阳极氧化、等离子微弧氧化、表面渗层处理、表面电镀、迭克罗表面涂层和协合涂层等方法在镁合金表面处理中的应用，总结并展望了镁合金表面处理的发展趋势。