Effect of in-situ formation of columnar mullite and pore structure refinement on high temperature properties of corundum casatbles

The effects of in-situ synthesis columnar mullite and pore structure on the hot modulus of rupture (HMOR), thermal shock resistance and corrosion resistance of corundum castables have been investigated in this paper. When 2% nano silica was added, the pore diameters of castables could be decreased to 15 nm (at 110 °C), 1 μm (1100 °C) and 6 μm (1500 °C), respectively. The corresponding reducing magnitude of pore size is 98.5%, 83.3% and 33.3%. The HMOR of castables fired at 1500 °C increased by 110% to 3.64 MPa. Furthermore, after three thermal shock cycles, the residual strength ratio of castables increased from 5.2% to 15.3%. A large amount of cross-distributed columnar mullite was formed between nano silica and α-Al₂O₃ by the two-dimensional nucleation mechanism, which remarkably enhanced the high temperature properties. The penetration index reduced from 30.86% to 19.88%, suggesting that smaller pore size and higher viscosity had a great influence to the penetration process.     

Novel electrospun polymer electrolytes incorporated with Keggin‐type hetero polyoxometalate fillers as solvent‐free electrolytes for lithium ion batteries

In this study, solvent‐free nanofibrous electrolytes were fabricated through an electrospinning method. Polyethylene oxide (PEO), lithium perchlorate and ethylene carbonate were used as polymer matrix, salt and plasticizer respectively in the electrolyte structures. Keggin‐type hetero polyoxometalate (Cu‐POM@Ru‐rGO, Ni‐POM@Ru‐rGO and Co‐POM@Ru‐rGO (POM, polyoxometalate; rGO, reduced graphene oxide)) nanoparticles were synthesized and inserted into the PEO‐based nanofibrous electrolytes. TEM and SEM analyses were carried out for further evaluation of the synthesized filler structures and the electrospun nanofibre morphologies. The fractions of free ions and crystalline phases of the as‐spun electrolytes were estimated by obtaining Fourier transform infrared and XRD spectra, respectively. The results showed a significant improvement in the ionic conductivity of the nanofibrous electrolytes by increasing filler concentrations. The highest ionic conductivity of 0.28 mS cm^?1 was obtained by the introduction of 0.49 wt% Co‐POM@Ru‐rGO into the electrospun electrolyte at ambient temperature. Compared with solution‐cast polymeric electrolytes, the electrospun electrolytes present superior ionic conductivity. Moreover, the cycle stability of the as‐spun electrolytes was clearly improved by the addition of fillers. Furthermore, the mechanical strength was enhanced with the insertion of 0.07 wt% fillers to the electrospun electrolytes. The results implied that the prepared nanofibres are good candidates as solvent‐free electrolytes for lithium ion batteries. © 2020 Society of Chemical Industry     

Effect of focused ion beam sample preparation on the phase composition of zirconia

The investigation of phase transformations in metastable ceramic systems such as zirconia often requires local phase analysis within the areas of interest. Electron backscatter diffraction is a suitable method in combination with focused ion beam sample preparation. The interaction between ion beam and sample has to be carefully considered. In case of metastable Y-PSZ and Mg-PSZ, phase transformations were observed after FIB preparation with 30?kV, 30?nA and 5° incidence angle. Damage was the dominating effect for angles of 72°. The expected local temperature increase due to the ion bombardment with 30?kV and 30?nA is 700?K for ZrO₂. Thus, the observed phase transformations can be explained on the basis of the temperature increase in the corresponding Y-PSZ phase diagram. In case of Mg-PSZ, the transition temperature is 1083?°C. The local temperature increase was obviously lower. The excitation energy for the observed phase transformation was smaller than expected from the phase diagrams of the thermodynamic equilibrium. Using 5?kV, 4.8?nA and 5° incidence angle, no phase transformations and no damage were observed. Thus, these conditions are well suited for the FIB preparation of metastable zirconia.     

动态高压微射流处理对方竹笋膳食纤维理化及结构特性的影响

以方竹笋中提取的膳食纤维为研究对象，采用动态高压微射流（dynamic high-pressure micro-fluidization, DHPM）在不同压力条件（0，50，100，150，200 MPa）下进行处理，探究其对竹笋膳食纤维（bamboo shoots dietary fiber, BSDF）理化和结构特性的影响。结果表明，随着处理压力的增大，BSDF粒径先增大后减小，当处理压力为150 MPa时，粒径最小，为（370±11） nm，此条件下BSDF的持水力、持油力和膨胀力达到最大，较对照组分别提高了47.74%，50.54%，61.27%，且差异显著（P<0.05）。红外光谱分析表明DHPM处理不会改变BSDF的官能团，但会使BSDF内部的部分氢键断裂和半纤维素、木质素等发生降解；X射线衍射和热重分析表明DHPM处理不会引起BSDF的晶体结构改变，但晶体有序度会下降，进而导致其热稳定性降低；微观结构分析显示DHPM处理会使BSDF颗粒尺寸减小、表面粗糙、组织松散，且当处理压力为200 MPa时，颗粒发生团聚。综上，DHPM可以有效改善BSDF的理化性质，在膳食纤维改性方面具有一定的应用价值。     

重力坝模型的尺寸效应

利用两个不同比尺预制缝重力坝模型的试验成果，以有限元富集技术进行非线性断裂分析，建立了极限承载力和长度比尺的确定性尺寸效应公式。混凝土重力坝的断裂尺寸效应满足指数衰减关系，用三次指数衰减公式可以准确地预测原型的极限承载力。断裂过程区的相对长度是引起模型试验尺寸效应的主要原因。数值计算结果表明，断裂过程区相对长度不仅是与材料有关的参数，能否充分发展还取决于结构尺寸和几何形状；断裂过程区相对长度的尺寸效应不同于统计尺寸效应和断裂参数尺寸效应，具有尺寸范围效应。断裂过程区相对长度在小试件、大试件和相对无穷大试件的发展程度不同。     

半导体传感器在生物分析科学中的应用(英文)

回顾了半导体生化传感器 (ISFET 和 LA PS)在医学监测、免疫检测、免疫分析、D N A 杂交以及细胞培养等方面应用的进展。为使半导体器件适用于生化检测,对其中所采用的检测手段和取得的研究结果进行了分析。展望了通过与微流体网络相结合,基于半导体传感器的实验室芯片化的可行性。     

新型壳聚糖/纳米二氧化硅杂化材料的制备与性能

在纳米S iO2颗粒表面引入羟丙基氯活性基团,得到功能化S iO2颗粒,再将羟丙基氯化的S iO2颗粒交联固定在壳聚糖上,制备了一种新型的壳聚糖/纳米S iO2杂化材料(简称杂化材料);通过傅里叶变换红外光谱、透射电镜、扫描电镜方法对杂化材料进行表征,采用热重(TG)分析研究杂化材料的热性能;考察了杂化材料的沉降速率和对金属离子Ca2+和M g2+的吸附能力。电镜分析结果表明,杂化材料微粒为纳米尺度的无机S iO2加强化的微粒,S iO2颗粒分散在材料中,形成均匀的表面;TG分析结果表明,杂化材料的热性能有所提高;沉降实验测得壳聚糖和杂化材料作为吸附剂的沉降时间分别为130.3,68.5s,表明杂化材料的沉降速率比壳聚糖的沉降速率快了近一倍;杂化材料对金属离子Ca2+和M g2+的吸附量分别可达到0.289 3,1.445 6mm ol/g。     

微构造的地震识别与应用效果

胜利油田的油气勘探具有较大的剩余勘探潜力，且大部分油气蕴藏在微构造油气藏中。微构造油气藏在胜利油田的勘探开发老区均有分布，纵向上从沙四段到东营组均有发育。该类油气藏埋深浅、储层物性好、产量高，具有较高的经济效益。微构造油气藏在国内外研究较少，国内外较注重目的层沉积微构造的研究，且主要是沉积微构造对注采关系的影响。在对复杂断块的精细研究中，以前研究的重点也主要集中在应用钻井资料对断层的成因和对断层封堵性的研究上，而对微构造圈闭的成因、识别及成图，一直没有进行系统的分类研究。文章划分了微构造的类型，研究了微构造的特点，并认为构造作用、沉积作用和后期改造作用是微构造形成的３种主要原因。同时，利用地震资料对微构造圈闭的识别方法和描述技术进行了探索，形成了一套具有针对性的技术系列，取得了显著的效果，这对油气田老区的滚动勘探开发具有重要的意义。     

Simplification of the Plasma Load of Negative-Pulse-Bias Source Used in Arc Ion Plating

Based on the voltage and current fluctuating phenomenon in the arc plasma load under the negative-pulse-bias, usingthe plasma physics theory and analysis of computer simulation expatiates that the nature of plasma load in vacuumarc plasma is a capacitance     

TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.