Effect of temperature on mechanical behavior of AZ31 magnesium alloy

Strain rate sensitivity and tension/compression asymmetry of AZ31 magnesium alloy at different temperatures and strainrates were investigated.Both of mechanical behaviors are temperature dependent.Strain rate sensitivity increases with increasingtemperature.Thermally activated slip is the source of strain rate sensitivity.At the temperature below or near 373 K,strain ratesensitivity is very little.Tension/compression asymmetry in yielding decreases with increasing temperature.Twinning is the reasonof tension/compression asymmetry.At the temperature above or near 573 K,the material shows little tension/compressionasymmetry of the flow stress.     

Wear resistance of ceramic coating on AZ91 magnesium alloy by micro-arc oxidation

The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation （MAO） was characterized. The results show that the ceramic coating （3.4-23 μm in thickness）on the surface ofAZ91 alloy was attained under different micro-arc oxidation treatment conditions, which consist mainly of MgO, Mg2SiO4 and MgSiO3 phases. Nano-hardness in a cross-sectional specimen was determined by nano-indentation experiment. The MAO coatings exhibit higher hardness than the substrate. Dry sliding wear tests for the MAO coatings and AZ91 alloy were also carded out using an oscillating friction and wear tester in a ball-on-disc contact configuration. The wear resistance of the MAO coatings is improved respectively under different treatment time as a result of different structures of ceramic coatings formed on AZ91 alloy.     

粉末冶金法制备SiC晶须增强MB15镁基复合材料

采用粉末冶金法制备了SiC晶须增强镁基复合材料(SiCW／MB15)试样。通过检测基体显微硬度探讨了SiCW对镁合金时效规律的影响，并借助扫描电镜(SEM)、透射电镜(TEM)和拉伸试验，研究了混粉方式对复合材料室温力学性能、SiCW分布及显微结构的影响。结果表明，MB15及其复合材料的时效硬化曲线上均存在双峰现象；SiCW的加入既提高了MB5的硬度，又加快了其时效速度：混粉方式对晶须分布及SiCW／MB15复合材料的室温力学性能影响很大。     

复合合金化对AZ91镁合金铸态组织的影响

利用光学显微镜、扫描电镜和X射线衍射仪研究了0.5?、0.2?、0.2%Sr(质量分数,下同)复合合金化对AZ91合金铸态组织影响。结果表明,0.5?、0.2?、0.2%Sr复合加入可以显著细化合金的铸态组织,0.5?、0.2?、0.2%Sr同时加入,其细化效果优于0.5?和0.2?或0.5?和0.2%Sr的复合加入,并且在组织中出现针状或杆状的Al4Ce新相。     

Study on the anodic film formation process of AZ91D magnesium alloy

The formation of anodic film of AZ91D magnesium alloy has been investigated by means of electrochemical impedance spectroscopy (EIS), cyclic voltammetry, anodic polarization curve, current-time transients and SEM technique. The results show that, under our experimental conditions, the formation of AZ91D anodic film follows the mechanism of 3D nucleation with diffusion controlled growth. With the increase of applied anodizing potential, the nucleation type of anodic film changes from progressive to instantaneous. The results also show that the initially formed anodized film is threadlike and porous, and high potential is essential for the formation of good anodic film with excellent properties.     

关于生产精制元明粉的探讨

介绍了以山西运城南风自产芒硝为原料生产精制元明粉的几种工艺,以及国内外精制元明粉的市场及生产状况.精制工艺包括化学除杂法、原料优选法、重结晶法.结果表明,精制元明粉的生产过程实质是一个除杂、提纯过程：对于钙离子含量高的原料,可采用化学除杂法;对于氯离子含量高的原料,可采用氯离子富集法、冷冻法或洗涤法;镁离子较难去除,可采用水硝洗涤、冷冻法.     

不同形貌氢氧化镁的化学合成及影响因素

对不同形貌氢氧化镁的化学合成及外部生长环境进行了综述。尤其对影响氢氧化镁结晶性能和形貌起关键作用的因素，如碱性沉淀剂的选择、合成温度的确定、不同镁盐的影响、碱和镁盐的初始浓度及配比、水热处理、反应物的混合方式、晶形控制剂的加入等，进行了详细的阐述。     

不同品种磷肥在土壤中的退化研究

对钙镁磷肥（FMP）、过磷酸钙（SSP）和部分酸化磷肥（PAPR）在河南郑州西岗沙土和河南西华县潮土中的退化情况进行了研究。     

氢氧化镁中微量元素硼硅铝的测定

以盐湖高镁卤水为原料生产的氢氧化镁产品纯度不高,含有部分无机杂质离子,为提高产品质量,改进产品性能,通过实验确定了氢氧化镁中微量元素硼、硅、铝的分光光度测定方法。此方法准确度与精密度较高,测定样品中的硼、硅、铝加标回收率分别为98.3%-101.5%,96.0%-99.3%,96.5%-97.3%,相对标准偏差（n=6）分别为2.06%,2.27%,2.39%,快速、简便、成本低,可作为企业生产的常规检测方法使用。     

PE-LLD／EVA／Mg（OH）2／复合阻燃剂高效无卤阻燃体系的研究

采用线形低密度聚乙烯/乙烯-醋酸乙烯共聚物作为复合材料主体,表面处理过的氢氧化镁(Mg(OH)2)为主阻燃剂,以微胶囊化红磷和自制硅类阻燃剂为核心的复合阻燃剂为阻燃增效剂,重点探讨了Mg(OH)2和复合阻燃剂的阻燃效果。结果表明,Mg(OH)2与复合阻燃剂并用具有良好的协同效应,当Mg(OH)2用量40份,复合阻燃剂5～7份时,可获得较高的氧指数,垂直燃烧试验通过FV0级,且材料抗静电能力提高,力学性能、加工性能较好。