采用泡沫陶瓷过滤片对高锰钢进行过滤处理，对其进行金相分析和测试密度，冲击韧性和耐磨性能，并与未过滤的高锰钢进行对比，实验结果表明，在过滤的高锰钢中，金属夹杂物明显减小，密度提高0．53％，冲击韧性39．5％，耐磨性能提高1．04倍，批量生产结果表明，过滤的高锰钢球磨机衬板的使用寿命提高0．6－0．7倍。     

Phase transition of lithiated-spinel Li2Mn2O4 at high temperature

1 Introduction Lithium manganese oxides are the most attractive cathode materials for rechargeable lithium-ion batteries because of their low-cost and less toxicity when compared with either cobaltates or nickelates[1?3]. Among these oxides, the spinel-fr…     

水韧处理工艺对合金高锰钢组织和性能的影响

研究了水韧处理工艺对Cr、V、Mo合金高锰钢金相组织和力学性能的影响.试验结果表明,水韧处理工艺对合金高锰钢金相组织和力学性能有显著影响,适宜的水韧处理工艺(加热至1100℃,保温4h)可以改善高锰钢金相组织和力学性能,使σb=780MPa、δ5 30%、αK=150J/cm2、HBS=258,使用寿命达到1800h以上.     

Process for cobalt separation and recovery in the presence of nickel from sulphate solutions by Cyanex 272

The present paper deals with the extraction of cobalt from a solution containing cobalt and nickel in a sulphate medium similar to the leach liquor obtained by the dilute sulphuric acid pressure leaching of the Pacific Ocean nodules matte followed by copper extraction. The commercial extractant Cyanex 272 (bis (2, 4, 4-trimethylpentyl) phosphinic acid) is used for this purpose. The leach liquor used for the present study contains Co =1.78 g/L and Ni=16.78 g/L. Before cobalt extraction, impurities, such as copper and iron, are removed from the leach liquor by the precipitation method. Increasing the concentration of Cyanex 272 increased the extraction percentage of cobalt due to the increase of equilibrium pH. Cobalt extraction efficiency of >99.9 % is achieved with 0.20 M Cyanex 272 in two counter-current stages at an aqueous: organic (A:O) phase ratio of 1.5∶1. Complete stripping of cobalt from the loaded organic containing 2.73 g/L Co was carried out at pH 1.4 by a synthetic cobalt spent electrolyte in two stages at an A:O ratio of 1∶2. The enrichment of cobalt during extraction and stripping operations was about 3.5 times. A complete process flowsheet for the separation and recovery of cobalt is presented.     

稀土镁对铸态高锰钢机械性能的影响

实验了稀土镁对铸态高锰钢机械性能的影响．结果表明，在一定的Ｃ、Ｍｎ、Ｓｉ成分中，加入ＲＥＭｇ合金均使其铸态机械性能有所提高．同时在工业设备上试验证实，加入ＲＥＭｇ的某种成分之高锰钢，在铸态时其耐磨性能、机械性能均已达ＺＧＭｎ１３－１和ＺＧＭｎ１３－２（ＧＢ５６８０－８５）水平并超过了铸态使用的７５Ｍｎ１３     

稀盐酸中锰结核还原浸出溶液净化除铁

针对酸性氯化物中黄铁矿还原浸出锰结核的溶液成分特点，选择黄钠铁矾法进行了沉淀分离铁的研究。结果表明温度和晶种以及溶液ｐＨ值是影响铁矾沉淀的重要因素。在ｐＨ２．０左右，溶液温度高于９０℃，足量晶种加入的情形下，１５０ｍｉｎ后可将溶液中的铁含量降至０．１ｇ／Ｌ。沉矾过程的表观活化能为９４．６６ｋＪ／ｍｏｌ。黄铁矿氧化生成的硫酸根随铁一同沉淀，从而消除了ＳＯ２－４在氯化物体系中的积累。     

渣金两相氧化锰还原的不可逆过程热力学研究

将仅能描述近平衡体系发生物理化学变化时物理量间的线性关系式——线性不可逆过程热力学扩展到远离平衡体系,建立了有界面存在的远离平衡的化学反应体系的不可逆过程热力学方程,并将其应用于渣-金间的氧化锰还原反应,得到的氧化锰还原的不可逆过程热力学的动力学方程与实验数据能很好地吻合,这表明不可逆过程热力学可以应用于远离平衡的体系。     

High-temperature oxidation of aluminum electroplated Fe-Mn alloys

Austenitic Mn-Al alloys (20–32 W/O Mn, 7–10 Al, 2–3 Si, 1C) were found to have satisfactory oxidation resistance up to 950°C under isothermal conditions in air. Surface enrichment of aluminum is a necessary condition for obtaining an almost pure alumina scale for uses at higher temperatures. Four different Mn-steels were Al-coated by the Capuano electroplating process. In all the steels there was an increase in the hot-oxidation resistance. The best results were obtained with steels containing both Al and Si, and this for temperatures up to 1100°C. No spalling was noticed during rapid cooling of the test pieces. Silicon was found to act as a diffusion barrier to outward iron diffusion. It appears that there is formation of a pure, thin film of alumina from the matrix which interacts with the aluminum diffusing from the superimposed, coating for the formation of good bonds.     

锰掺杂对PNW-PMS-PZT压电陶瓷结构和性能的影响

采用传统陶瓷工艺制备了Pb(Ni1/2W1/2)O3-Pb(Mn1/3Sb2/3)O3-Pb(Ti，Zr)O3-xMnO2压电陶瓷，分析了经1150℃烧结2h制备的陶瓷样品的相结构组成。实验结果表明：所有陶瓷样品均为钙钛矿相，未发现其它晶相。随着锰掺杂量的增加，陶瓷晶粒逐渐长大。研究了不同剂量的锰掺杂对压电陶瓷介电和压电性能的影响。结果表明：随着锰掺杂量的增加，材料逐渐变“硬”，当MnO2掺杂量少于0．2％(按质量计，下同)时，相对介电常数εr、压电常数d33和机械品质因数Qm逐渐增加，介电损耗tanδ减小；当MnO2掺杂量多于0．2％时，εr、d33和Qm逐渐降低，tanδ增加。随着锰掺杂量的增加，机电耦合系数kp和Curie温度θc逐渐减小。MnO2掺杂量为0．2％的压电陶瓷适合制作大功率压电陶瓷变压器。其压电性能为：εr=2138，tanδ=0．0058，kp=0．613，Qm=1275，d33=380pC／N和θc=205℃。     

A kinetic study on medium temperature desulfurization using a natural manganese ore

Natural manganese ores were selected as raw materials for the desulfurization sorbent because of economical efficiency and high reactivity on hydrogen sulfide. Initial reaction rates between H₂S and desulfurization sorbent of natural manganese ores were determined in a temperature range of 400-800°C using a thermobalance reactor. All reactions were first order with respect to H₂S and were expressed by the Arrhenius relation. When the sulfidation reaction was controlled by diffusion, the temperature dependence of the effective diffusivity was given by the Arrhenius equation. Activation energies and frequency factors were obtained from the product layer diffusion coefficient of various sorbents by plotting as an Arrhenius equation form. Several additives were mixed to improve the sulfidation capacity, and NiO was the best additive.