XRQ-Ⅱ型开车燃烧控制系统的结构及应用

XRQ-Ⅱ型开车燃烧控制系统由泵组、阀组、燃烧器、快速关断阀门及控制柜等组成,燃料经油枪喷嘴雾化喷出在燃烧器中安全稳定地燃烧,控制柜保证供油及点火、火焰检测.在600 kt/a硫磺制酸系统焚硫炉烘炉及催化剂升温中的实际应用表明,XRQ-Ⅱ型开车燃烧控制系统具有便于自控操作、提高焚硫炉烘炉内衬质量、缩短催化剂升温时间等优点.     

230 kt/a烟气制酸系统的运行及改造情况

介绍230kt／a诺兰达炉铜冶炼烟气制酸装置的运行及技术改造。装置采用稀酸洗净化、ⅣⅠ-Ⅲ Ⅱ“3 1”两转两吸工艺流程，运行中发现板式酸冷却器堵塞、电除雾器腐蚀、气体换热器积酸和漏气等现象，通过更换为阳极保护管壳式酸冷却器、在电除雾器前增设湍冲洗涤器、调整换热管的喷铝成分等措施，收到良好的效果。     

阳离子交换树脂催化合成十三碳二元酸二乙酯

以强酸性阳离子交换树脂为催化剂,十三碳二元酸与乙醇为原料合成十三碳二元酸二乙酯,考察了影响反应的因素。结果表明:醇酸摩尔比为4∶1,催化剂用量为酸质量的2%,在3分子筛脱水的情况下反应7 h,酯化率达98.4%,并且催化剂可重复使用3次。     

Boronic acid-functionalized nanoparticles: synthesis by microemulsion polymerization and application as a re-usable optical nanosensor for carbohydrates

Translucent boronic acid-carrying nanolatexes are prepared by copolymerisation of vinylbenzyl chloride in microemulsion followed by post functionalisation with 3-aminophenylboronic acid. The diol binding capacity and selectivity of the phenylboronic acid remain unchanged after anchoring to polymer nanoparticles (16 nm diameter, 0.22 mmol/g). The binding of a catechol dye, Alizarin Red S (ARS), to the boronic acid-carrying nanoparticles affords a colored, stable, nanolatex which is used for the selective visual detection of fructose in a competitive assay. The binding of fructose at pH 8.2 is readily evidenced by a color change and monitored by UV/Vis spectroscopy. The nanosensor can be regenerated in acidic medium. The entrapment of the nanolatex in a dialysis cell provides a re-usable support for binding and optical detection.     

三氯异氰尿酸生产技术研究

对三氯异氰尿酸合成反应过程中的主要工艺参数进行分析和实验研究,并成功地开发出了连续法生产三氯异氰尿酸的新工艺,该工艺和传统工艺相比,具有生产安全、高效、节能的特点。     

硝硫混酸与Ag、Cu反应的动力学

用失重法探讨了硝硫混酸此例、浸出温度和时间等因素对银的溶解和铜的钝化的影响。结果表明:在一定的[HNO_3]范周内,较高温度时,银的溶解符合一级反应规律;求得银的溶解量与时间、HNO_3起始浓度等的关系式和相应的反应活化能;铜在此条件时是钝化的。本实验再一次证实了银的溶解和铜的钝化机理的正确性,也为银、铜的分离提供了实验依据。     

A novel electroless silver depositing method for magnesium alloys

Depositing silver on magnesium alloy by both electroless plating and organic coatings was studied. The organic coating was made by immersing samples in organosilicon heat-resisting varnish. In this method the organic coating acts as interlayer between the substrate and silver film. When the reaction starts, silver deposits directly on the interlayer. X-ray diffraction and SEM analysis were used to determine the composition and morphology of the interlayer and silver film. The potentiodynamic polarization curves for corrosion studies of coated magnesium alloys were performed in a corrosive environment of 3.5% NaCl（mass fraction） at neutral pH （6.9）. The results indicate that compared with the substrate, the corrosion resistance of coated magnesium alloys increases greatly. Moreover, the method proposed in this work is environmentally friendly, non-toxic chemicals were used. In addition, it provides a new concept for the corrosion inhibition of magnesium alloys.     

易门铜业公司18kt／a粗铜及硫酸车间的技改工程

介绍了易门铜冶炼厂烟气制酸系统的技术改造工程.从工艺流程、设备复核、工艺参数、设备配置等方面阐述了技改的过程.     

Kelvin Probe measurements of polymer coated gold substrates: Mechanism studies

The origin of work-function changes induced in polymer/metal structures (polyacrylic acid (PAA), ammonium and sodium polyacrylate) upon ammonia exposure is studied. To understand and explain the mechanism systematic measurements of uncoated and polymer coated metals are performed in Kelvin Probe (KP) setups. Additional data have been acquired through gravimetric and electrochemical experiments (cyclic voltammetry (CV)). The results obtained confirm that the field effect sensitive processes are taking place at the metal/polymer interface and allow their modelling. The intrinsic sensitivity of metallic samples upon ammonia exposure is influenced by the presence of coating polymers, by their ability to sorb water and to keep the metal surface wet or dry.