超声雾化共沉淀法制备纳米YAG粉体

采用超声雾化共沉淀法,以Al(NO3).9H2O,Y(NO3).6H2O为原料,以聚乙二醇(PEG2000)作为分散剂,利用超声技术雾化钇铝混合液,形成气溶胶,与沉淀剂(氨水、碳酸氢铵)共沉淀反应制备纳米YAG粉体,制得粉体900、1000℃下煅烧3h,用XRD、SEM进行性能表征。结果表明:粉体均一转相;颗粒细小,平均尺寸为50nm;分散均匀,无明显硬团聚。     

SPS制备各向异性微米晶SmCo_5烧结磁体的研究

采用放电等离子烧结技术制备了各向异性微米晶SmCo_5磁体,研究了磁体的烧结工艺及添加Fe纳米粉对磁体结构和磁性能的影响。研究发现,SmCo_5烧结磁体的最佳烧结温度为830℃,此时磁体的室温磁性能最佳:B_r=8.19 kGs,H_(cj)=10.6 kOe,(BH)_(max)=13 MGOe;而添加Fe纳米粉的烧结磁体,饱和磁化强度升高,但剩磁和矫顽力降低。XRD结果表明,未添加Fe纳米粉的烧结磁体具有单相CaCu_5结构,而添加Fe纳米粉的烧结磁体出现了2∶17相和Fe-Co软磁相。SEM及能谱分析发现,添加的Fe纳米粉扩散进入了1∶5相,形成Sm(Fe,Co)_5和Sm_2(Fe,Co)_(17))。     

两种不同方法制备TSAG纳米粉体的对比研究

采用溶胶-凝胶法和共沉淀法制备TSAG纳米粉体,利用XRD和SEM等测试手段对不同方法合成的TSAG纳米粉体进行表征,并根据谢乐公式计算出粉体粒径大小。结果表明共沉淀法经1200℃煅烧6h可得纯度高,平均晶粒尺寸为49.7nm的TSAG粉体,溶胶-凝胶法经1000℃煅烧3h可得纯度高,平均晶粒尺寸为23.25nm的TSAG粉体。从煅烧温度、保温时间以及制备所得粉体粒径大小对这两种方法进行比较。相较于共沉淀法,采用溶胶-凝胶法可获得晶相更纯,粒径更小,颗粒分布均匀,分散性能好的TSAG粉体,且此方法更省时节能。     

超临界流体干燥法制备ZnS纳米粉体及其表征

采用微乳液法-超临界流体干燥法制备出ZnS纳米粉体.以无水乙醇为超临界干燥介质,超临界流体干燥工艺为260℃×7.3 MPa×10 min.采用X射线衍射(XRD)、透射电镜(TEM)对制得的粉体进行了表征.结果表明,制备得到的ZnS纳米粉具有闪锌矿晶体结构,粉体外形为球形,粒子大小均匀,粒径约为5~7 nm,分散性较好,有效的改善了粉体的团聚程度,且晶化程度稍高于550℃煅烧处理的ZnS纳米粉.     

纳米CaCO3的室温固相合成及三聚磷酸钠的控制机理

以Ca(NO3)2·4H2O和Na2CO3·10H2O为原料,采用室温固相反应合成出粒径为19 nm的CaCO3,BET比表面积为36.3 m2·g-1.反应中Na5P3O10能有效地抑制CaCO3晶体的生长和团聚.其作用在于Na5P3O10电离产生的离子可进入CaCO3晶格位置或选择性地吸附在CaCO3的晶面上,从而降低了CaCO3的表面能.当CaCO3的活性部位被完全包覆时,继续增加Na5P3O10用量,将不再抑制CaCO3的生长.     

添加碳对氧化钨氢还原制备纳米钨粉的影响

针对氧化钨氢还原过程中因"挥发-沉积"作用而导致W粉晶粒快速长大和异常长大现象,利用添加碳的方法抑制氧化钨挥发,制备了平均粒径56.4 nm的球形W粉,并研究了添加碳对还原机制的影响。结果表明,W粉的粒度和纯度与前驱体配碳比有关,最佳配碳比为2.6。W粉粒径随还原时间延长不断增加,长大趋势与还原温度密切相关。随着还原温度由680℃升高至760℃,W粉晶粒长大速率变慢,粒径和残余碳含量显著降低,分散性变好;继续升高温度,W粉粒径略有增加。在710℃以上,还原产生的水蒸气与碳反应生成CO和H_2,显著降低体系中水蒸气的分压,抑制挥发性水合物WO_2(OH)_2的产生,W粉的主导长大方式也由挥发-沉积转变为原子扩散机制。     

微乳液和碳吸附耦合法制备氧化钐、氧化钆掺杂氧化铈纳米粉体及其电性能的研究

用微乳液和碳吸附耦合法制备了氧化钐、氧化钆二元稀土掺杂氧化铈纳米粉体(Sm2O3)0.08(G d2O3)0.02(C eO2-δ)0.8。探讨了碳黑的加入量对粉体表面积的影响,得到最佳的碳黑加入量。利用XRD、TEM和BET方法对其物相、分散性、颗粒形貌和比表面积等性能进行了表征。结果表明:700℃焙烧的粉体呈现良好的结晶状态,为立方萤石结构,比表面积为65m2/g,平均颗粒直径为12nm,分散良好。利用交流阻抗法测试了材料的电导率。结果表明,电导率随烧结温度的升高而增大。     

Nanofluid performance in a solar LFR system involving turbulator applying numerical simulation

With involving innovative swirl flow tapes through the absorber tube in LFR system, the productivity of unit was improved in present study. To grow the thermal feature of water, hybrid nanoparticles (Al₂O₃ + CuO) were dispersed. For designing current solar unit, 12 mirrors, one absorber tube and secondary reflector have been used. To calculate the heat source in solid zone of tube, SolTrace has been applied. Because of low fraction of each type of nano-sized material, single phase formulation were utilized. For analyzing the 3D turbulent flow of hybrid nanomaterial within the tube, FVM was chosen with incorporating K-ε formulations. Effects of inlet flow rate (Q) and its temperature (T_in), pitch ratio (PR = 0.147059 to 0.5) and height ratio (BR = 0.16 to 0.24), have been examined in outputs. Three important functions which were calculated for all cases were: Nusselt number (Nu), thermal productivity (η_t) and Darcy factor (f). Inclusion of hybrid nanomaterial causes Nu, f and η_t to intensify around 5.26%, 4.67% and 0.316% when Q = 15, PR = 0.5, BR = 0.24. As greater value of PR has been chosen, Nu, f and η_t enhance around 22.27%, 112.45% and 0.514% when Q = 15, BR = 0.16. Intensify of BR creates more secondary flow and Nu, f and η_t augments about 6.36%, 48.7% and 0.06%, when Q = 15, PR = 0.5. With augment of Q and T_in, η_t declines around 15.35% and 0.304%. As Q increases, Nu intensifies about 60.21% but f declines about 11.1% when PR = 0.5, BR = 0.24.     

溶胶-凝胶法制备纳米Y2O3粉体

为了改善Y2O3粉体的分散性,提高其烧结活性,试验以三乙醇胺和氨水为凝胶剂,利用溶胶-凝胶方法合成了纳米级Y2O3粉体,采用差热/热重、X射线衍射、透射电镜研究了前驱体的组成、前驱体在不同的煅烧温度下的物相变化以及煅烧粉体的分散性.结果表明,前驱体的组成为Y2(OH)5.14(NO3)0.86H2O,在500℃保温2h可直接生成立方相的Y2O3,煅烧至1000℃保温2h得到了结晶度高、分散性好、平均粒径为50nm、近球形的YO纳米粉体;三乙醇胺的加入有利于提高YO粉体的分散性.     

电沉积法制备多功能复合材料研究动态与发展趋势

综述了近年来国内外在复合电沉积制备多功能复合材料方面的研究动态与发展趋势;重点探讨了多元复合电沉积、多元脉冲复合电沉积、脉冲喷射电沉积、纳米复合电沉积以及功能梯度材料的复合电沉积等方面的研究现状和发展趋势。结果表明：这五类复合材料镀层的性能比传统的单金属镀层、合金镀层及其复合镀层更加优异,在今后的发展中将有更广阔的应用前景。