Process and joint quality of ultrasonic vibration enhanced friction stir lap welding

In order to improve the process effectiveness and joint quality, ultrasonic vibrations were integrated with friction stir lap welding. Effect of ultrasonic exertion on the process and joint quality of AA 6061-T6 were investigated. Upon ultrasonic exertion, joints owned larger effective lap width, shorter hooks and improved strength. Weld fracture mode changed from a ductile–brittle mixed mode to a more ductile mode while the fracture path shifted from lap interface to beyond the stir zone. Material flow and interface defects were characterised using lap welded dissimilar aluminium alloy joints. Ultrasonic vibration improved the material flow and reduced the interfacial defects. Variations in failure load of joints were found in accordance with the variations in material flow and interfacial defects.     

Effect of microstructure on the fatigue crack growth behaviour of a near-α Ti alloy

Fatigue crack growth behaviour of Ti–6Al–2Zr–1.5Mo–1.5V (VT-20 a near-α Ti alloy) was studied in lamellar, bimodal and acicular microstructural conditions. Fatigue crack growth tests at both increasing and decreasing stress intensity factor range values were performed at ambient temperature and a loading ratio of 0.3 using compact tension samples. Lamellar and acicular microstructures showed lower fatigue crack growth rates as compared to the bimodal microstructure due to the tortuous nature of cracks in the former and the cleavage of primary α in the latter. The threshold stress intensity factor range was highest for acicular microstructure.     

Effect of microbial hydrogen consumption on the hydrogen permeation behaviour of AISI 4135 steel under cathodic protection

The feasibility of microbial hydrogen consumption to mitigate the hydrogen embrittlement (HE) under different cathodic potentials was evaluated using the Devanathan-Stachurski electrochemical test and the hydrogen permeation efficiency η. The hydrogen permeation efficiency η in the presence of strain GA-1 was lower than that in sterile medium. The cathodic potential inhibited the adherence of strain GA-1 to AISI 4135 steel surface, thereby reducing the hydrogen consumption of strain GA-1. The adherent GA-1 cells were capable of consuming ‘cathodic hydrogen’ and reducing the proportions of absorbed hydrogen, indicating that it is theoretically possible to control HE by hydrogen-consuming microbes.     

Corrosion resistance of Al–Cr-slag containing chromium–corundum refractories to slags with different basicity

Al–Cr slag is the solid waste generated by the smelting of Cr metal. It presents a range of environmental hazards. This study addressed the corrosion resistance of Al–Cr slag containing chromium–corundum refractories to slags with different basicity. Herein, we provide suggestions for the use of Cr–corundum of different basicity in kilns. Al–Cr slag, brown fused Al₂O₃, and chrome green were used as the raw materials, with pure calcium aluminate cement being used as a binder. The brick samples, prepared using different blends of chrome green and corundum, were fired at 1600?°C, and subsequently subjected to a slag corrosion test. After corrosion by slag of different basicity, the phase composition and microstructure of the sample were analyzed by X-ray diffraction, energy dispersive spectrometer and scanning electron microscopy. There were two major findings. First, Cr–corundum brick made from Al–Cr slag has a better slag corrosion resistance than that made from Cr₂O₃ and brown fused Al₂O₃. Second, Cr–corundum brick made from Al–Cr slag has superior corrosion resistance to slag with a CaO:SiO₂ ratio of 2:1.     

A dense and compact laser cladding layer with solid metallurgical bonding significantly improved corrosion resistance of Mg alloy for engineering applications

Although Mg alloy attracts great attention for engineering applications because of high specific strength and low density, low corrosion resistance limits its extensive use. In this study, Mg–Al–Zn–Mn alloy was treated via a laser cladding process to generate a dense and compact laser cladding layer with solid metallurgical bonding on the substrate for improving corrosion resistance, effectively hindering the corrosion pervasion into Mg alloy. The corrosion current density declined from 103 μA/cm² for Mg alloy to 13 μA/cm² for the laser cladding layer in NaCl aqueous solution. Moreover, the laser cladding layer was slightly corroded in comparison with Mg alloy in NaCl aqueous solution. Besides, the microhardness of the cladding layer reached a mean value of 170.5 HV, 3.1 times of Mg alloy (56.8 HV) due to the in situ formation of hardening intermetallic phases. Wear resistance of laser cladding layer was also obviously improved. These results demonstrated that the laser cladding layer obviously enhanced anticorrosion property of Mg alloy for engineering applications.     

Formation of a protective layer against corrosion on Mg alloy via alkali pretreatment followed by vanillic acid treatment

Although Mg alloy possesses high specific strength, low density, and good biocompatibility, poor corrosion resistance hinders its further applications. In the present study, an innovative protective layer against corrosion was prepared on the AZ31 Mg alloy via alkali pretreatment followed by vanillic acid treatment. The alkali pretreatment supplied –OH for the AZ31 Mg alloy surface to react with vanillic acid. The vanillic acid treatment played a crucial role in enhancing the corrosion resistance due to the excellent ability to act as a barrier and retard aqueous solution penetration, which effectively isolated the underlying Mg alloy from the corrosive environment. The corrosion current density of alkali and vanillic acid-treated Mg alloy (AZ31V) almost showed two orders of magnitude lower values in comparison with that of the AZ31 Mg alloy, and the corrosion potential of AZ31V Mg alloy increased from −1.41 to −1.25 V. The immersion tests proved that there was no occurrence of severe corrosion. Hence, the alkali pretreatment and vanillic acid treatment may represent a promising method to improve the corrosion resistance of Mg alloy.     

Animations showing Lego manipulative tasks: Three potential moderators of effectiveness

Evidence suggests that transient visual information, such as animations, may be more challenging to learn than static visualizations. However, when a procedural-manipulative task is involved, our evolved embodied cognition seems to reverse this transitory challenge. Hence, for object manipulative tasks, instructional animations may be more suitable than statics. We investigated this argument further by comparing animations with statics using a Lego task shown to university students, by examining three potential moderators of effectiveness: (a) the environment of manipulation (virtual or physical), (b) the quality of visual information (focused or unfocused), and (c) the presence of hands (no hands or with hands). In Experiment 1 we found an advantage of animation over statics, and no differences among the environments. In Experiment 2, we again observed an animation advantage, a small advantage of focused static information compared to unfocused static information, and a positive effect of not showing the hands.     

p-Median and p-dispersion problems: A bi-criteria analysis

Given a collection of n locations and a symmetric measure of distance (difference) between each pair of locations, we seek to identify (select) a subset of p locations so as to achieve two distinct objectives. The first objective is to use the selected locations as centers (medians) of p groups that would partition the entire collection and minimize the total distance between the locations and their respective group medians. The second objective is to maximize the minimum distance (diversity) among the selected locations themselves. We study this problem as a multi-objective optimization problem and propose an iterative algorithm to obtain its non-dominated frontier. At each iteration we construct and solve a 0–1 integer programming problem. Through a computational experiment we show that this algorithm is computationally effective for small to medium size instances of the problem. We also propose a Lagrangian heuristic algorithm for solving larger instances of this problem.     

Alkali catalyzed liquefaction of corncob in supercritical ethanol–water

Corncob liquefaction in supercritical ethanol–water was performed with and without the addition of an alkali catalyst by direct addition or biomass impregnation in a 250-cm³ batch reactor. The effects of temperature, solvent and alkali addition on the biomass conversion level and oil yield were investigated to find the optimum condition. For non-catalytic liquefaction using a 1:1 (v/v) ethanol: water ratio, a maximum oil yield and conversion level of 49.0% and 93.4%, respectively, were obtained at 340 °C. For alkali catalytic liquefaction, the oil yield with KOH addition (57.5%) was higher than that from KOH-impregnated corncob liquefaction (43.3%). The oil from liquefaction with KOH addition had higher heating value (26.7–35.3 MJ kg⁻¹) than the corncob (19.1 MJ kg⁻¹). The dominant components of the obtained oil were found by GC/MS analysis to be aldehyde, ester, phenol derivatives and aromatic compounds.     

Unraveling the effect of alumina-supported Y- doped ceria composition and method of preparation on the WGS activity of gold catalysts

The demands for high-purity hydrogen required in fuel-cell applications impose new goals and challenges for design of well performing water-gas shift (WGS) catalysts. Gold-based catalysts have exhibited high activity in the WGS reaction at low temperature. Preparation of appropriate and economically viable supports with complex composition by various synthesis procedures is an attractive approach to WGS performance improvement. The effect of two different preparation methods (wet impregnation or mechanical mixing) and ceria content (10, 20 or 30 wt%) on textural, structural, surface and reductive properties and WGS activity of gold catalysts was studied. Additionally, the role of Y₂O₃ as a promoter of ceria was examined. Long-term stability test was carried out at 260 °C over the most active catalyst. The composition of the best performing sample (composed of about 70 wt% alumina), prepared by mechanical mixing, was considered promising in case of practical applications because of its cost efficiency. The combination of gold nanoparticles and alumina supported Y-doped ceria proved an advantageous approach for developing new catalytic formulations with high effectiveness in clean hydrogen production.