废镍触媒的综合利用

本文采用酸溶，除渣，分离及蒸发浓缩，冷却，过滤等操作步骤，从废镍触媒中回收得有实用价值的硫酸镍，硫酸镁晶体，其回收率分别为７５％和９０％，经济效益也比较好。     

Suppression of the α → β-nickel hydroxide transformation in concentrated alkali: Role of dissolved cations

The presence of dissolved cations such as Al and Zn in alkaline electrolyte (6 M KOH) suppresses the -nickel hydroxide transformation. The uptake of Al (10 mol%) and Zn (30 mol%) exhibited by the active material likely stabilizes the -phase. Dissolved Al is deleterious to the performance of the nickel hydroxide electrode, whereas, dissolved Zn enhances the specific discharge capacity of nickel hydroxide by approximately 25% showing that the mode of metal uptake is different in the two cases.     

Activity–Composition Relations in NiAl2O4─MnAl2O4 Solid Solutions and Stabilities of NiAl2O4 and MnAl2O4 at 1300° and 1400°C

Activities of NiO were measured in the oxide and spinel solutions of the system MnO–NiO–Al₂O₃ at 1300° and 1400° C with the aim of deriving information on the thermodynamic properties of the spinel phases. Synthetic samples in selected phase assemblages of the system were equilibrated with metallic nickel and a gas phase of known oxygen partial pressures at a total pressure of 1 atm. The data on NiO activities and directions of conjugation lines between coexisting oxide and spinel phases were used to establish the activity–composition relations in spinel solid solutions at 1300° and 1400°C. The MnAl₂O₄–NiAl₂O₄ solid solutions exhibit considerable negative deviations from ideality at these temperatures. The free energy of formation of MnAl₂O₄ from its oxide components (MnO + Al₂O₃) at 1300° and 1400°C is calculated to be −24.97 and −26.56 kJ. mol⁻¹, respectively. The activities determined in the stoichiometric spinel solid solutions are more negative as compared with those predicted from cation distribution models.     

化学镀Ni-P-Cr2O3和Ni-P-SiO2复合镀层的研究

本文对化学镀镍及化学镀镍磷基质中SiO2与Cr2O3的共沉积进行了研究.微粒在不断生长的膜层中共沉积引起了新的化学复合镀层的出现,这些复合镀层许多都具有优异的耐磨及耐蚀性能.通过选取镀层合金/复合微粒/金属基体的组分可改进镀层,获得所需的性能,以满足特别的需求.在对这些复合镀层的应用需求正在迫近与增长的同时,其市场正在迅速扩张.本文开发出了一种合适的复合化学镀镍液,并通过维氏硬度法对化学复合镀镍层进行了表征.采用动电位极化及交流阻抗法测定了镀层的Taber耐磨性能及耐蚀性能.采用SEM及XRD对复合镀层的表面形貌进行了分析.     

负载型复合载体对Ni基催化剂催化性能的影响

将ZrO2直接负载在MxOy（Al2O3,SiO2,CeO2）上组成负载型ZrO2/MxOy复合载体,并以此负载型复合载体制备Ni基催化剂,用BET、XRD、TPR和TPD等对催化剂的比表面积、晶相结构、还原性能等进行了表征,同时以CO2重整CH4为探针考察了催化剂的活性和稳定性。结果表明,复合载体对Ni基催化剂的性能有较大的影响：Ni/ZrO2/SiO2具有较好的初活性,但反应5 h后明显下降;Ni/ZrO2/Al2O3在反应50 h后CO2和CH4的转化率基本保持不变。     

纳米氧化镍纤维的制备及表征

利用静电纺丝法,制备出聚乙烯吡咯烷酮(PVP)/四水乙酸镍纤维前躯体,通过焙烧前躯体制备出纳米氧化镍纤维,并用透射电子显微镜(TEM),扫描电子显微镜(SEM),X-射线衍射(XRD)以及热重分析(TG)对纤维进行了表征.     

Electroless nickel plating on the surface of carbon fibers

The electroless nickel plating on the surface of carbon fibers was prepared by pretreating the carbon fibers in order to increase their conductivity,and consequently enhance the EMI shielding effectiveness of the composites.The relationship between the performance of depositing coat and pH value,temperature,reaction time and the way of agitation was studied.Results show that the depositing quality is stable under pH between 4.5 and 5.0,temperature between 75 ℃ and 85 ℃,reaction time for 10 min and air agitation.The uniform and compact nickel layer deposited on carbon fibers was proved by XRD and SEM,and the electrical resistivity of carbon fibers with nickel coating was tested.Results indicate that the electrical resistivity of carbon fibers with electroless nickel plating is decreased by an order of magnitude compared with that of carbon fibers.It means that nickel coating can greatly improve the electromagnetic interference shielding properties of carbon fibers.     

复合掺杂Nd（III）和Zn（II）非晶态Ni（OH）2电极活性材料的制备及其表征

以NiSO4、ZnSO4和Nd（NO3）3为原料,采用共沉淀快速冷冻法制备出了复合掺杂稀土Nd（III）和Zn（II）的非晶态氢氧化镍粉体材料。测试发现：样品材料微结构无序性强,结晶水含量较高。将样品材料制备成镍电极并组装成MH—Ni电池,在80mA／g恒电流充电5．5h、40mA／g恒电流放电、终止电压为1．0V的充放电制度下,复合掺杂6％Nd（III）和6％Zn（II）样品材料电池的放电平台为1．2624V,放电比容量为343．12mAh／g,远高于目前应用的B-Ni（OH）2电极活性材料的放电比容量。     

Platymonas subcordiformis吸附镍离子的研究

分别研究了不同生长期海洋绿藻Platymonas subcordiformis对不同浓度Ni2+的吸附能力,以及藻液pH、光照强度和共存金属阳离子对藻细胞吸附能力的影响。对数生长前期藻细胞藻液和Ni2+的初始浓度为80 mg/L时的吸附能力较强,分别为7.76×10-5μg/个细胞和7.85×10-5μg/个细胞。当藻液pH介于9~10,光照强度为4 500 Lx时,藻细胞吸附Ni2+能力较强。此外,共存金属阳离子会抑制藻细胞对Ni2+的吸附。     

铁氧体法处理沉镍残液研究

采用铁氧体法处理沉镍残液,此法处理沉镍残液效果明显。研究了pH值、温度、搅拌时间、投料比对处理效果的影响。试验结果表明:在pH=11~12,温度50℃,搅拌时间25~30 min,投料比10的操作条件下,处理后的沉镍残液中各重金属离子浓度均达到排放标准。