Effect of sodium doping on graded Cu(In1−xGax)Se2 thin films prepared by chemical spray pyrolysis

In the present work we have studied the effect of Na on the properties of graded Cu(In_1−xGa_x)Se₂ (CIGS) layer. Graded CIGS structures were prepared by chemical spray pyrolysis at a substrate temperature of 350 °C on soda lime glass. Sodium chloride is used as a dopant along with metal (Cu/In/Ga) chlorides and n, n-dimethyl selenourea precursors. The addition of Na exhibited better crystallinity with chalcopyrite phase and an improvement in preferential orientation along the (112) plane. Energy dispersive analysis of X-rays (line/point mapping) revealed a graded nature of the film and percentage incorporation of Na (0.86 at%). Raman studies showed that the film without sodium doping consists of mixed phase of chalcopyrite and CuAu ordering. Influence of sodium showed a remarkable decrease in electrical resistivity (0.49–0.087 Ω cm) as well as an increase in carrier concentration (3.0×10¹⁸–2.5×10¹⁹ cm⁻³) compared to the un-doped films. As carrier concentration increased after sodium doping, the band gap shifted from 1.32 eV to 1.20 eV. Activation energies for un-doped and Na doped films from modified Arrhenius plot were calculated to be 0.49 eV and 0.20 eV, respectively. Extremely short carrier lifetimes in the CIGS thin films were measured by a novel, non-destructive, noncontact method (transmission modulated photoconductive decay). Minority carrier lifetimes of graded CIGS layers without and with external Na doping are found to be 3.0 and 5.6 ns, respectively.     

Graphite Oxide and Aromatic Amines: Size Matters

Experimental and theoretical studies are performed in order to illuminate, for first time, the intercalation mechanism of polycyclic aromatic molecules into graphite oxide. Two representative molecules of this family, aniline and naphthalene amine are investigated. After intercalation, aniline molecules prefer to covalently connect to the graphene oxide matrix via chemical grafting, while napthalene amine molecules bind with the graphene oxide surface through π–π interactions. The presence of intercalated aromatic molecules between the graphene oxide layers is demonstrated by X‐ray diffraction, while the type of interaction between graphene oxide and polycyclic organic molecules is elucidated by X‐ray photoelectron spectroscopy. Combined quantum mechanical and molecular mechanical calculations describe the intercalation mechanism and the aniline grafting, rationalizing the experimental data. The present work opens new perspectives for the interaction of various aromatic molecules with graphite oxide and the so‐called “intercalation chemistry”.     

Synthesis and characterization of Manganese doped Tungsten oxide by Microwave irradiation method

The aim of this article is to synthesis tungsten oxide (WO₃) nanoparticle along with Manganese (3 wt% and 10 wt%) by Microwave irradiation method. The physical properties of the synthesized Manganese doped Tungsten oxide materials were characterized by X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Transmission Electron Microscope (TEM), UV-Diffuse Reflectance Spectroscopy, SEM-EDAX and Photoluminescence studies. The predominant peaks obtained in X-ray diffraction pattern reveal the crystalline nature of the nanoparticles and the structure belongs to Monoclinic for pure and Mn doped WO₃. FTIR analysis shows the presence of Tungsten and oxygen in the synthesis material and verified with EDAX. TEM analysis shows both pristine and Mn doped WO₃ nanopaticles. They are having spherical shaped morphology with average particle size from 35 to 40 nm. UV-DRS revealed that the bandgap energy for pure and Manganese doped WO₃ are discussed in this article. The Scanning Electron Microscope analysis shows the plate like morphology for pure WO₃ and the morphology were decreased by doping Manganese. The defects and oxygen deficiencies were analysed by photoluminescence spectroscopy.     

Efficient hydrogen production for industry and electricity storage via high-temperature electrolysis

The paper describes the development status of Sunfire's reversible solid oxide cell (RSOC) technology. Here, Sunfire is a pioneer in the field of high-temperature electrolysers (HTE) for renewable hydrogen production which can be operated as a fuel cell for power generation in a reverse mode. The maturity of the technology is improved stepwise so that first applications in the field of hydrogen production for industry and electricity storage can be tackled. Three application examples where larger scale prototype has been installed will be discussed: 1) A power-to-power electricity storage based on hydrogen, 2) a RSOC unit that is installed in an iron and steel works, and 3) a pressurized SOEC prototype which will be integrated with a methanation unit. Results show the potentials of the technology in connection with fluctuating renewable energy sources.     

Charge injection in metal/organic/metal structures with ZnO:Al/organic interface modified by Zn1−xMgxO:Al layer

Aluminum-doped zinc oxide (ZnO:Al, AZO) electrodes were covered with very thin (∼6 nm) Zn_1−xMg_xO:Al (AMZO) layers grown by atomic layer deposition. They were tested as hole blocking/electron injecting contacts to organic semiconductors. Depending on the ALD growth conditions, the magnesium content at the film surface varied from x = 0 to x = 0.6. Magnesium was present only at the ZnO:Al surface and subsurface regions and did not diffuse into deeper parts of the layer. The work function of the AZO/AMZO (x = 0.3) film was 3.4 eV (based on the ultraviolet photoelectron spectroscopy). To investigate carrier injection properties of such contacts, single layer organic structures with either pentacene or 2,4-bis[4-(N,N-diisobutylamino)-2,6-dihydroxyphenyl] squaraine layers were prepared. Deposition of the AMZO layers with x = 0.3 resulted in a decrease of the reverse currents by 1–2 orders of magnitude and an improvement of the diode rectification. The AMZO layer improved hole blocking/electron injecting properties of the AZO electrodes. The analysis of the current-voltage characteristics by a differential approach revealed a richer injection and recombination mechanisms in the structures containing the additional AMZO layer. Among those mechanisms, monomolecular, bimolecular and superhigh injection were identified.     

Enhancement of optical and electrical properties of SILAR deposited ZnO thin films through fluorine doping and vacuum annealing for photovoltaic applications

Undoped and fluorine doped ZnO thin films were deposited onto glass substrates using successive ionic layer adsorption and reaction (SILAR) technique and then annealed at 350 °C in vacuum ambience. The F doping level was varied from 0 to 15 at% in steps of 5 at%. The XRD analysis showed that all the films are polycrystalline with hexagonal wurtzite structure and preferentially oriented along the (002) plane. Crystallite sizes were found to increase when 5 at% of F is doped and then decreased with further doping. It was seen from the SEM images that the doping causes remarkable changes in the surface morphology and the annealing treatment results in well-defined grains with an improvement in the grain size irrespective of doping level. All the films exhibit good transparency (>70%) after vacuum annealing. Electrical resistivity of the film was found to be minimum (1.32×10⁻³ Ω cm) when the fluorine doping level was 5 at%.     

Fully solution-processed and multilayer blue organic light-emitting diodes based on efficient small molecule emissive layer and intergrated interlayer optimization

Efficient and fully solution-processed blue organic light-emitting diodes (OLEDs) based on fluorescent small-molecule and methanol/water soluble conjugated polymer as electron-injection material are reported. The emitting layer is 3,6-bis(9,9,9′,9′-tetrakis (6-(9H-carbazol-9-yl)hexyl)-9H,9′H-[2,2′-bifluoren]-7-yl)dib-nzo[b, d]thiophene 5, 5-dioxide (OCSoC) with a blue-fluorescent small-molecule, and a methanol/water soluble polymer poly[(9,9-bis(30-(N,N-dimethylamino)propyl)-2,7-fluorene)-alt-2,7-(9,9-dioctyl-fluorene)] (PFN) acted as electron-injection layer (EIL). All the organic layers are spin-coated from solution. The multilayer device structure with emitting layer/electron-injection layer is achieved by solution-processed method without the dissolution problem between layers. The performances of the devices show that the maximum luminous efficiency of the multilayer device is increased about 43%, compared to the single-layer device. PFN acting as the EIL material plays a key role in the improvement of the device performance when used in solution-processed small-molecule OLEDs.     

On‐the‐Spot Immobilization of Quantum Dots,Graphene Oxide,and Proteins via Hydrophobins

Class I hydrophobin Vmh2, a peculiar surface active and versatile fungal protein, is known to self‐assemble into chemically stable amphiphilic films, to be able to change wettability of surfaces, and to strongly adsorb other proteins. Herein, a fast, highly homogeneous and efficient glass functionalization by spontaneous self‐assembling of Vmh2 at liquid–solid interfaces is achieved (in 2 min). The Vmh2‐coated glass slides are proven to immobilize not only proteins but also nanomaterials such as graphene oxide (GO) and quantum dots (QDs). As models, bovine serum albumin labeled with Alexa 555 fluorophore, anti‐immunoglobulin G antibodies, and cadmium telluride QDs are patterned in a microarray fashion in order to demonstrate functionality, reproducibility, and versatility of the proposed substrate. Additionally, a GO layer is effectively and homogeneously self‐assembled onto the studied functionalized surface. This approach offers a quick and simple alternative to immobilize nanomaterials and proteins, which is appealing for new bioanalytical and nanobioenabled applications.     

测井资料在优选压裂层位中的应用

压裂是低孔、低渗油层改造的主要增产措施。根据常规测井资料、岩石物理实验分析数据及试油成果。研究储层四性关系，确定区块的低孔、低渗储层评价标准。进一步对油层进行分类，有针对性地为油层压裂提供施工层位和准确的储层参数。通过商543区块实例，阐述了选择压裂层位的方法。