碳氟表面活性剂FCI-3及其复配体系对碳钢表面的缓蚀性能

本文采用失重法,电化学交流阻抗法,极化曲线法和扫描电镜法等观察缓蚀剂在HCl介质中,FCI-3及普通碳氢表面活性剂（CTAB,SDS,TX-100）复配体系对Q235钢的缓蚀性能.结果表明,FCI-3对碳钢表面有较好的缓蚀性能,三种方法测试的结果均达到90％以上;三种普通碳氢表面活性剂分别与FCI-3复配后,发现三个体系仍有较好的缓蚀效果,缓蚀效率达到90％以上,缓蚀效率从高到低的顺序是CTAB＞ TX-100＞ SDS.     

稀土Sm2O3对WCoB-TiC复相陶瓷组织的影响

以WC、TiB2、Co粉末为基本原料,添加稀土Sm2 O3为抑制剂,采用真空液相反应烧结技术制备WCoB-TiC复相陶瓷材料,利用XRD、SEM和 EDS对其微观形貌和相组成进行表征。结果表明,添加一定量稀土Sm2 O3后,WCoB-TiC复相陶瓷晶粒细小且分布均匀,晶粒的长大得到抑制;随着稀土Sm2 O3的过量加入,复相陶瓷中有棒状晶粒出现,晶粒有粗化的趋势。在1400℃下烧结时,当Sm2 O3添加量为0．3％时,制成的WCoB-TiC复相陶瓷材料密度达到10．01 g/cm3,硬度HRA达到91。     

An International Collaborative Study on Trypsin Inhibitor Assay for Legumes,Cereals, and Related Products

For determining trypsin inhibitor activity (TIA) in soy products, the American Oil Chemists' Society (AOCS) Method Ba 12-75 has been used. It measures differences in absorbance at 410 nm of bovine trypsin activity toward a synthetic substrate (Nα-benzoyl-DL-arginine-p-nitroanilide) in the absence and presence of an inhibitor. Recently, a significantly improved method was developed (JAOCS, 2019, 96:635–645), featuring 5 mL of total assay volume, enzyme-last sequence, and single inhibitor level in duplicate. It is proposed as the AOCS Method Ba 12a-2020. As a part of the AOCS method approval process, a collaborative study involving 12 international laboratories was conducted to evaluate the performance of the proposed method. The study involved measuring TIA in 10 selected test samples plus a blind duplicate. They included soybeans, pulses, cereals, and their processed products (flours, concentrates, and isolates). After rigorous statistical treatment of the data, only three outliers were removed from the data of two samples. Repeatability relative standard deviations (RSDr) for the 11 samples ranged from 0.99% to 5.52%. Reproducibility RSD (RSD_R) ranged from 7.07% to 22.92%, with seven samples having RSD_R around 10% or less. The remaining four samples had very low TIA, and their RSD_R values ranged from 13.34% to 22.92%. The study has demonstrated reliable performance of the proposed AOCS method. Several collaborators carried out additional experiments addressing some aspects of the method, leading to further refinements. The proposed method is undergoing evaluation by the AOCS Uniform Methods Committee for adoption as an Official Method for measuring TIA in various legume and grain products.     

Comparison of ISO 14902:2001 with AOCS Ba 12a-2020 for determining trypsin inhibitor activity in protein products

For measuring trypsin inhibitor activity (TIA), there are two major official methods: American Oil Chemists Society (AOCS) method Ba 12a-2020 and International Organization for Standardization (ISO) 14902:2001. The former was recently approved. The two methods differ in sample preparation, extraction, colorimetric assay systems and TIA calculations. In this study, the two methods were symmetrically compared using three unique sets of samples: assorted protein products of soybeans, pulses, and grains; soybeans boiled for varied durations; and soy white flakes toasted for varied durations. For given samples, significant differences existed in TIA measured by the two methods, resulting from effects related to the assay systems and TIA calculations, not from the difference in sample preparation and extraction. When the same trypsin was used, TIA (in mg trypsin inhibited/g sample) measured by the two methods were highly correlated (r = 0.9973, n = 27), giving an equation of y = 0.5464x − 0.4887, where y represents ISO values and x for AOCS values. The line connecting ratios of ISO/AOCS in TIA and AOCS values remained relatively flat around 0.53 but started to curve down when TIA approached the lowest. Furthermore, for the same samples, TIA values measured by the ISO method decreased with increasing specific activity of trypsin used, while AOCS values remained consistent, leading to decreasing ratios of ISO/AOCS. Therefore, accurate and direct comparison of the two methods was impossible. It could not be resolved by simply changing ISO method's calculations as hypothesized earlier. Regardless, for most samples, ISO values were roughly about 55% of AOCS values.     

冷柱头进样气相色谱法分析橡胶防护蜡的碳数分布

研究冷柱头进样气相色谱法分析橡胶防护蜡的碳数分布以及正构烷烃/非正构烷烃比例。结果表明,采用冷柱头进样方法,在样品量为10 mg、样品完全溶解后静置10~30 min并取上层清液以及进样量为1μL时,分析得到的气相色谱峰的峰形和响应信号最优。本方法测定橡胶防护蜡的碳数分布以及正构烷烃/非正构烷烃比例结果准确、可靠。     

咪唑啉型缓蚀剂的合成及其缓蚀机理的研究

以棕榈酸、二乙烯三胺、马来酸酐为原料合成了一种咪唑啉型缓蚀剂YQ-01,与YQ-02复配后得到能有效抑制二氧化碳腐蚀的缓蚀体系YQ-03。应用静态挂片失重法、电化学极化曲线、X射线光电子能谱分析研究了YQ-03抑制二氧化碳腐蚀的电化学特征,分析了腐蚀前、后及加入缓蚀体系YQ-03后A3钢的表面产物,探讨了YQ-03的缓蚀机理。结果表明,由主剂YQ-01和助剂YQ-02组成的复配缓蚀体系有良好的协同作用,腐蚀产物膜有3层,能有效抑制饱和CO2的高矿化度盐水对A3钢的腐蚀。     

新型咪唑啉衍生物油田注水缓蚀剂的研究

使用长链脂肪酸、多胺、甲醛和三氯化磷等为原料合成了咪唑啉有机膦酸类缓蚀剂。在模拟油田注水条件下，采用静态挂片、极化曲线和交流阻抗等测试方法评价了缓蚀剂的缓蚀性能，并对缓蚀剂的成膜机理进行了一些研究与探讨。     

缓蚀剂对316L不锈钢在酸性氯离子溶液中应力腐蚀开裂的作用

研究表明316L不锈钢在55℃的1mol/L HCl+1mol/L NaCl溶液中对SCC比较敏感。316L不锈钢在所研究的体系中处于活化溶解状态。对添加缓蚀剂的体系的电化学参数的测试和分析表明,缓蚀剂抑制SCC的能力与缓蚀剂抑制阳极反应有关。     

纳米晶WC-10Co复合粉末的烧结致密化行为

研究了机械合金化纳米晶WC-10Co复合粉末的真空烧结致密化行为和一般规律.结果表明:烧结温度的提高和烧结时间的延长有利于样品的烧结致密化过程,在1 275～1 300℃致密化速度快,在1 300℃,15 min左右致密化过程已基本完成;VC、Cr3C2等复合晶粒长大抑制剂含量的增加不利于致密化过程;新型晶粒长大抑制剂A可以更有效地阻碍晶粒长大;纳米晶WC-10Co-0.8VC/Cr3C2-0.2A复合粉末压坯在1375℃,30min烧结条件下,所得的密度为14.48 g/cm3,晶粒尺寸约为180 nm.     

一种海水缓蚀剂缓蚀行为的研究

利用电化学方法和表面分析测试技术，研究了有机膦酸醇酯类缓蚀剂(YKI-05)对于907A钢在天然海水中的缓蚀行为．实验表明，在静态海水中，浓度为300mg／L的YKI-05缓蚀剂能在907A钢表面形成稳定的缓蚀膜层，是一负催化阴极型缓蚀剂，在实验周期内其对907A钢的缓蚀效率较高；并用原子力显微镜(AFM)和俄歇电子能谱(AES)对该缓蚀膜的表面形貌和成分进行分析．