热致液晶性纤维素衍生物及其热塑性塑料复合物熔体流变行为的研究

用毛细管流变仪研究了乙基纤维素（ＥＣ）及其高密度聚乙烯（ＨＤＰＥ）复合物，纤维素芳族酯（ＣＡＥ）及其聚碳酸酯（ＰＣ）复合物的剪切流变特性和机理。结果表明，ＥＣ对ＨＤＰＥ／ＥＣ复合物的粘度影响不大，而少量（５％）ＣＡＥ的加入使ＰＣ／ＣＡＥ复合物粘度大大下降，且复合物流变曲线呈现新的特征。     

轴端沟槽底部激光强化工艺参数优化研究

分析了选用不同激光能量密度对HT300进行表面强化处理时，材料表面呈现的四种状况；未相变硬化、相变硬化、表面微熔与表面熔凝的金相组织。根据工艺要求，选取相变硬化方法对轴端沟槽底表面进行处理。分析了工件激光处理方法并通过试验研究，寻找轴端沟槽底部激光强化工艺参数；激光功率（P）、光斑直径（D）及扫描速度（V）的优化组合。硬度测试及耐磨性能试验表明：激光相变处理和激光熔凝处理后轴端沟槽底部表面较表面感应淬火硬度分别提高7%和34%，绝对磨损体积分别下降了13%和25%。实践证实，对轴端沟槽底部激光相变硬化处理方法较其他表面处理方法工艺简单，加工工件符合技术要求，试验结果对零件表面处理提供了可靠依据。     

Formation of GaAsP interface layers monitored by reflectance anisotropy spectroscopy

Reflectance anisotropy spectroscopy (RAS) has been used to study As-by-P exchange during metalorganic vapor phase epitaxy. The study focuses on the processes occurring during switching from GaAs to GaInP, especially the effect of purging PH₃ over a GaAs surface. GaAsP/GaAs superlattices of different periodicity were grown and the P-content was determined by high-resolution x-ray diffraction and correlated to the RAS spectra. From the temperature dependence of the P-content, an activation energy of 0.56 eV was estimated for the incorporation mechanism. In addition to the insights into the processes at mixed group-V heterointerfaces, our study demonstrates the reproducibility of RAS transients that thus can be used for process monitoring.     

Distinguished Scientific Awards for an Early Career Contribution to Psychology.

The Early Career Awards recognize the large number of excellent young psychologists. Recipients of this award may not have held a PhD for more than nine years. The areas considered in 1991 were animal learning and behavior, developmental, and personality. The winners for 1991 were Kent C. Berridge, Susan A. Gelman, and Randy J. Larsen. For each winner a citation, biography, and selected bibliography of their works are presented. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

单元系T—p相图的数学结构

作者以化学元素的稳定单质为基准,推演出了任意物质M_i(相态Ω)的热力学生成活度{相态Ω)的函数形式:?D_Ω数值的大小体现着相态Ω的热力学相对稳定性.根据集合论原理沿D(稳定性)座标取极大值的方法把物理性质互不连续的各个异相态连结在一起,建立了单元系在T-p面上的优势分布方程(PSDE):■作者以H_2O为实例,计算了T-p相图,与实验相图基本一致.     

Estimation of Thermodynamic Properties from Binary Phase Diagram

The general relationship between binary phase diagrams and the thermodynamic properties was system-atically derived without any assumption.A procedure was presented to estimate the thermodynamic proper-ties from the binary phase diagrams.     

Determination of the liquidus lines and isotherms of the Hg-Zn-Te system by a modified direct observation method

The modified direct observation method is employed for the determination of the liquidus lines in the (Hg_{1_x}Zn_x)_{1_y}Te_y, ternary system. The liquidus temperatures of the ternary samples of various compositions withx from 0.05 to 0.30 andy from 0.5 to 0.9 are measured. The temperature-composition phase diagrams and some liquidus isotherms are established for this system.     

Hydrothermal Synthesis of Acicular Lead Titanate Fine Powders

A pure, acicular lead titanate (PbTiO₃) fine powder with a white color has been prepared by hydrothermal synthesis. It is a new phase of PbTiO₃ with I 4 symmetry, cell parameters of a = 12.358 Å and b = 14.541 Å, and a density of 6.80 g.cm⁻³. The influences of pH (12.5 to 14.4), Pb/Ti ratio (1.0 to 1.6) in the feedstock, reaction temperature (130° to 230°C), time (0.25 to 4 h), starting materials, and additives on the formation of acicular PbTiO₃ under hydrothermal conditions have been investigated. The acicular PbTiO₃ with I 4 symmetry, referred to as the PX phase, can be converted to the perovskite-type (PE phase) of PbTiO₃ at about 605°C while its acicular morphology is essentially unchanged. The preferable conditions for preparing pure acicular PX-phase PbTiO₃ are that the pH is 13.0 to 14.0, Pb/Ti ratio is >1.3, reaction temperature is 170° to 200°C, time is 0.5 to 1.0 h, titanium butoxide (Ti[O(CH₂)₃CH₃]₄) is the starting material, and poly(vinyl alcohol) is an additive. The acicular grain of the PX phase is usually less than 100 nm in diameter and more than 1000 nm in length.     

航空齿轮表面硬化层断裂性能研究

按照航空齿轮的具体工艺过程，对材料12Cr2Ni4A的拉伸试样和断裂试样进行设计和加工，通过三点弯曲实验，重点研究了齿轮材料硬化层的硬度分布，硬化试样拉伸力学性能参数和断裂性能参数，实验结果表明，所采用试样的加工工艺方案是可行的，所获得的Kc基本反映我国航空硬化齿轮材料的断裂性能特征，为定量预测航空硬化齿轮疲劳寿命提供实验和理论分析的依据。