Synthesis and characterization of an interpenetrating polymer network composed of poly(methacrylic acid) and poly(vinyl alcohol)

Temperature and pH‐responsive interpenetrating polymer network (IPN) hydrogels, constructed with poly(methacrylic acid) (PMAA) and poly(vinyl alcohol) (PVA), by a sequential IPN method, were studied. The characterization of IPN hydrogels was investigated by Fourier‐transform infrared spectroscopy, differential scanning calorimetry (DSC) and swelling under various conditions. The IPN hydrogels exhibited relatively high swelling ratios, in the range 230–380 %, at 25 °C. The swelling ratios of the PMAA/PVA IPN hydrogels were pH and temperature dependent. DSC was used for the quantitative determination of the amounts of freezing and non‐freezing water. The amount of free water increased with increasing PMAA content in the IPN hydrogels. Copyright © 2004 Society of Chemical Industry     

Synthesis and characterization of poly(ethylene aspartate)-metal complexes

Poly(ethylene aspartate) [PEA] was synthesized by the melt condensation of D,L-aspartic acid and ethylene glycol. PEA containing pendent amino and carbonyl groups in its repeating chain was used as the polymeric ligand for complexation with transition metal ions, viz. Co(II), Ni(II), Cu(II), Mn(II), Zn(II), Cd(II), Ca(II), Mg(II), Pb(II) and Hg(II). Complexation was found to be most effective in DMSO. The resulting polyester-metal complexes were solid coloured materials which have been characterized by IR spectroscopy, elemental analysis and magnetic susceptibility measurements. The thermal stability of the polyester-metal complexes was investigated by thermogravimetric analysis (TGA). On the basis of the physico-chemical studies, an oxygen and nitrogen coordinated structure for the polyester-metal complexes is proposed.     

Morphology and structure of poly(p-phenylene terephthalamide) crystallized from dilute organic solution

The high-temperature crystallization of poly(p-phenylene terephthalamide) (PPTA) from dilute organic solutions was achieved through the introduction of a non-solvent, or precipitating agent, at the desired crystallization temperature. The morphology and crystal structure were examined for crystals produced from PPTA polymer with two different molecular weights (M_w = 46000 and 3430 g mol⁻¹), using transmission electron microscopy. For the high-molecular-weight polymer, ribbon-like crystals were produced, while the low-molecular-weight polymer yielded small needles or platelets. In both cases, electron diffraction showed that the Northolt allomorph was obtained. For the high-molecular-weight polymer, the molecular axes were parallel to the ribbon axes in a chain-extended type structure. A hypothesis for the orientation of the low-molecular-weight PPTA in the small platelets, is also given.     

Associative properties of perfluorooctyl end‐functionalized polystyrene–poly(ethylene oxide) diblock copolymers

The synthesis of 2,2,3,3‐tetrahydro‐perfluoroundecanoyl end‐functionalized polystyrene–poly(ethylene oxide) block (PS‐block‐PEO‐R_F) copolymers and their matching PS‐block‐PEO diblock copolymers was carried out by sequential anionic polymerization. Viscometry and ¹⁹F NMR studies show that the PS‐block‐PEO copolymers, in contrast to their matching PS‐block‐PEO‐R_F copolymers, exhibit a micellar rather than the associative behavior seen for the latter. However, the presence of an excess of fluorinated acid, used for end‐functionalization, produces a reduction of the associative behavior above the overlap concentration, with the fluorinated acid acting like a surfactant. A competition may also occur between PS—and R_F—mediated micellization. Copyright © 2004 Society of Chemical Industry     

Decreasing miscibility with greater heterogeneity in ternary polymer blend: poly(cyclohexyl methacrylate), poly(α‐methyl styrene) and poly(4‐methyl styrene)

A ternary blend system comprising poly(cyclohexyl methacrylate) (PCHMA), poly(α‐methyl styrene) (PαMS) and poly(4‐methyl styrene) (P4MS) was investigated by thermal analysis, optical and scanning electron microscopy. Ternary phase behaviour was compared with the behaviour for the three constituent binary pairs. This study showed that the ternary blends of PCHMA/PαMS/P4MS in most compositions were miscible, with an apparent glass transition temperature (T_g) and distinct cloud‐point transitions, which were located at lower temperatures than their binary counterparts. However, in a closed‐loop range of compositions roughly near the centre of the triangular phase diagram, some ternary blends displayed phase separation with heterogeneity domains of about 1 µm. Therefore, it is properly concluded that ternary PCHMA/PαMS/P4M is partially miscible with a small closed‐loop immisciblity range, even though all the constituent binary pairs are fully miscible. Thermodynamic backgrounds leading to decreased miscibility and greater heterogeneity in a ternary polymer system in comparison with the binary counterparts are discussed. © 2003 Society of Chemical Industry     

Synthesis and characterization of poly(siloxane-urethane)s

A series of polyurethane block copolymers based on hydroxy-terminated polydimethylsiloxane and poly(propylene glycol) soft segments of molecular weights 1818 and 2000, respectively, were synthesized. The hard segments consisted of 4,4′-diphenylnethane diisocyanate and 1,4-butanediol as the chain extender. Samples with different molar ratios were prepared. We tried to synthesize polydimethylsiloxane-based polyurethanes (PDMS-PU) containing a hard block as major fraction and a soft block as minor fraction for preparing toughened rigid systems. After a study of the pure polydimethylsiloxane-based polyurethane and poly(propylene glycol)-based polyurethane (PPG-PU), (mixed polyol)-based block copolymers and blends of PDMS-PU and PPG-PU were synthesized, and characterized by means of differential scanning calorimetry, tensile testing and scanning electron microscopy. In (mixed polyol)-based copolymers and lower hard-segment content blends, macro-phase separation occurred, but blends with higher hard-segment contents showed significant reduction in amounts of phase separation.     

Phenol novolac/poly(4- hydroxyphenylmaleimide) blend hardeners for DGEBA-type epoxy resin

Phenol novolac/poly (4-hydroxyphenylmaleimide) (PHPMI) blends were used as an epoxy resin hardener. The curing behavior of the above system and the thermal and mechanical properties of the cured epoxy resin were studied. It was not necessary to use a curing accelerator for this system, because PHPMI caused acceleration of the curing reaction. The curing mechanism of this system was investigated by using model compounds. Test pieces from the neat resins and the glass fiber reinforced resins were evaluated in terms of thermal and mechanical properties, respectively. It was found that heat resistance and mechanical properties were improved by increasing the amount of PHPMI in the hardener.     

In-chain functionalization by alternating anionic copolymerization of styrene and 1-(4-dimethylaminophenyl)-1-phenylethylene

Anionic copolymerizations of styrene (M₁) with excess 1-(4-dimethyl-aminophenyl)-1-phenylethylene (M₂) were conducted in benzene at 25°C for 24h, using sec-butyllithium as initiator. Narrow molecular weight distribution copolymers with M?;_n = 16.1 × 10³ g/mol (M?_w/M?_n = 1.04) and 38.2 × 10³g/mol (M?_w/M?_n = 1.05), and 24 and 38 moles of M₂ per macromolecule, respectively, were characterized by size exclusion chromatography, ¹H NMR spectroscopy and DSC. The monomer reactivity ratio, r₁ = 5.6, was obtained from the copolymer composition at complete consumption of M₁, assuming that the rate constant k₂₂ =0,i.e. r₂ =0. The polymers exhibited T_g values of 128 and 119°C, respectively, which correspond to an estimated T_g = 217°C for the hypothetical homopolymer of M₂.     

Head-to-head polymers: 33. Bromination of cis-1,4-polybutadiene to head-to-head poly(vinyl bromide)

Cis-1,4-polybutadiene (PB) in a 0.5% solution of a solvent mixture of dichloromethane and 1,2-dibromoethane or tetrahydrofuran was quantitatively brominated with elemental bromine at 0°C under careful exclusion of oxygen to head-to-head poly(vinyl bromide). Partially brominated PB has a structure of random or block sequences of butadiene units in the polymer depending on the bromination solvent but shows no stereospecificity in the CHBrCHBr-dyads. Partially brominated PB with block structure showed a microphase-separated morphology over a wide range of composition. Microphase separation is less pronounced for the more random structure of butadiene units. I.r and ¹³C n.m.r. spectroscopy of the partially brominated PB was used to follow the progress of the bromination.     

Melting and crystallization behaviour of elastoplastic semicrystalline copolymers: poly(ether ester)

The melting and crystallization behaviour of an elastoplastic semi-crystalline poly(etherester) has been studied by differential scanning calorimetry. The shape of the melting endotherm is strongly dependent on heating rate and annealing time and results from the sum of simultaneous melting and crystallization phenomena. Samples prepared by different techniques, i.e. by solvent evaporation or by melt extrusion, behave very differently owing to specific crystal morphologies. By applying the Hoffman-Weeks plot, the equilibrium melting temperature has been extrapolated. The Avrami treatment allows the calculation of the index n and of the rate constant K from the isothermal kinetic data.