Hydrogen Absorption and Release Behavior in Hydrogen Decrepitation Process of Nd-Fe-B Alloys

The behavior of hydrogen absorption and release in hydrogen decrepitation (HD) process of Nd-Fe-B alloys were investigated. The results reveal that the reactivity and the amount of hydrogen absorption in HD process are related to the surface activity of the alloy so that the fresh and active surface has a higher efficiency. The presence of Nd-rich phase at the grain boundary is an essential factor of the HD activity of the alloy at room temperature. On degassing, hydrogen is released from the HD powder continuously with increasing temperature. And the residual hydrogen is as low as 0.0015% at 1073K, which shows that the hydrogen is almost exhaused. It is feasible to remove the hydrogen from the HD powder by heating treatment at the temperature of 523-723K for 1h prior to the magnetic field forming in order to decrease the harmful effect of hydrogen on the easy axis alignment of HD magnet.     

鱼雷罐喷粉预处理过程水模研究

在鱼罐喷粉预处理水模实验数据的基础上，进一步利用线性回归确定各工艺操作参数对喷吹基本参数（均混时间、粉剂穿透比和粉剂停留时间）的影响，得出各传输动力学基本参数的函数关系式。     

纳米β-Ni(OH)2与球型Ni(OH)2的热性能比较研究

用配位沉淀法合成出纳米级Ni（OH）2，并对其进行XRD，TEM，DSC分析，分析结果表明，所得纳米β-Ni（OH）2为可用作电极材料的β-Ni（OH）2，粒径为30－40nm，且热分解温度比普通球镍低10℃左右，摩尔分解热比普通球镍低4－7kJ，从理论上分析了产生此现象的原因。     

石英砂物料气流冲击粉碎效果影响因素分析

通过对石英砂物料在不同实验条件下的粉碎结果分析，论述了流化床式超细气流粉碎机工艺参数对产品粒度的影响。     

激光法合成SiC超细粉末物理化学过程的研究——Ⅰ.实验规律及粉末特性

用50W连续波CO_2激光器为热源,诱发SiH_4和C_2H_4反应,合成SiC超细粉末。实验确定了反应腔体内压力p、气源中的C/Si原子比、喷嘴内径2r以及激光功率密度与粉末特性之间的关系,并对合成的产物进行物理、化学表征。     

高强度烧结钢

为开拓粉末冶金材料新的应用领域，近年来对高强度烧结钢进行了大量的研究与开发。本文简要介绍Ｈｏｇａｎａｓ公司开发的一些高强粉末冶金材料及对一些高强度烧结材料尺寸变化的控制。     

超细铁粉和氧化铁颗粒的研究

用透射电镜和图像分析仪等研究了超细铁粉和γ-Fe_2O_3粉末的结构、形貌、粒子的平均尺寸以及粒度分布。研究结果表明,多数超细铁粉粒子近似呈球形,并且,铁粉粒子由两相组成,粒子的核心部分是金屑a-Fe,表面的包裹层为氧化物层,它由Fe_3O_4和7-Fe_O_3的混合物组成。氧化层的平均厚度大约占整个粒子直径的20％左右。羰基铁粉粒子(含氧化层)的平均直径为16nm。直径在4～24nm范围的粒子数占总粒子数的91％,而7-Fe_2O_3粉末既有雪茄状粒子,也有小球状粒子。分析表明,球状粒子的平均直径为113nm,雪茄状粒子的平均直径(按<长 宽>/2计算)为148nm。由于超细铁粉粒子很细,且有磁性,制备电镜试样时分散比较困难。本文比较了几种分散方法后,使用了一种较好的分散方法——超声喷管分散法。     

TiO_2粉体性能对PTC热敏电阻性能的影响

ＴｉＯ_２的纯度、粒度及粒形对ＢａＴｉＯ_３系ＰＴＣＲ的性能影响很大，对所用ＴｉＯ_２加以选择非常重要，国产和日本产ＴｉＯ_２原料在粉体性能上存在差异。     

Statistical studies of branched ester latex and paint properties

Vinyl versatate, butyl acrylate and 2-ethylhexyl acrylate were compared as comonomer, for colloid-stabilized vinyl acetate latex polymers to assess their impact on latex coating properties. Vinyl versatate afforded advantages in scrub resistance, gloss, hydrophobicity and higher glass transition temperatures. Butyl acrylate developed better wet adhesion efficiency, gel content and hiding efficiency. 2-Ethylhexyl acrylate offered performance comparable to butyl acrylate in hiding efficiency, lowering copolymer glass transition temperatures, and gloss development. Combinations of these monomers, in many instances, afforded a better balance of performance properties than individual monomers alone. In the subject study, a simplex-centroid design was utilized to statistically map polymer compositions for determining the effect of comonomer composition on latex and paint film properties. In addition to developing contour maps of polymer and paint properties as a function of composition, a technique for studying structure-property relationships is presented.     

相转移法制备高纯超细TiO2技术研究

报道了用相转移法制备高纯超细ＴｉＯ２的新技术；探讨了Ｔｉ（Ⅳ）从有机相转移到水相发生水解反应的机理 ；通过ＴＧ－ＤＴＡ分析以及ＸＲＤ物相分析对水解产物的组成、热分解机理，晶型转变规律进行了研究，建立了水解产物焙烧的最佳温度。