Preparation and Compressive Stress Effect of Polymer Matrix RE-Fe Giant Magnetostrictive Composite

Polymer matrix RE-Fe giant magnetostrictire composite （GMPC） was prepared using bonding and magnetic field forming technique, and magnetostriction of samples was measured for different compressive stress. The experimental results show thai there is certain compressive effect in GMPC. And the influence of compressive stress on magnetostriction of sample was investigated. It offers essential reference for application and device design of GMPC.     

Ring‐opening polymerization of D,L‐lactide by rare earth 2,6‐dimethylaryloxide

Ring‐opening polymerization of D,L ‐lactide (LA) has been successfully carried out by using rare earth 2,6‐dimethylaryloxide (Ln(ODMP)₃) as single component catalyst or initiator for the first time. The effects of different rare earth elements, solvents, monomers and catalyst concentration as well as polymerization temperature and time on the polymerization were investigated. The results show that La(ODMP)₃ exhibits higher activity to prepare poly(D,L ‐lactide) (PLA) with a viscosity molecular weight of 4.5 × 10⁴ g mol^?1 and the conversion of 97 % at 100 °C in 45 min. The catalytic activity of Ln(ODMP)₃ has following sequence: La > Nd > Sm > Gd > Er > Y. A kinetic study has indicated that the polymerization is first order with respect to both monomer and catalyst concentration. The apparent activation energy of the polymerization of LA with La(ODMP)₃ is 69.6 kJ mol^?1. The analyses of polymer ends indicate that the LA polymerization proceeds according to ‘coordination–insertion’ mechanism with selective cleavage of the acyl–oxygen bond of the monomer. Copyright © 2004 Society of Chemical Industry     

Preparation and Properties of Rare Earth Modified Carbon Black/Natural Rubber Composites

The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln（OH）3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln （OH）3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what＇s more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy （OH）3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction.     

Oxides Catalysts of Rare Earth and Transient Metal for Catalytic Oxidation of Benzene

The catalysts of CeO2 and the mixture of CeO2 and CuO were prepared, and the activities of these catalysts for completely oxidizing benzene were studied.The results show that the optimal proportion of CeO2/CuO is 6: 4.The highest temperature at which benzene was completely oxidized on these catalysts at different airspeed was measured.Compared these catalysts with the noble metal used, our catalysts had superiority in the resources and the industrial cost besides good activities.     

Spin Dependent Hopping in Ti Doped La0.67 Ca0.33 MnO3

A systematic investigation of the magnetic and transport properties of Ti doped La0.67Ca0.33MnO3 was reported. The Ti substitution for Mn ions results in a reduction in ferromagnetism and conductivity. The metal-insulator transition temperature is close to Curie temperature which decreases from 274 to 82 K as x increases from 0 to 0.17. The most important effect of Ti doping is to introduce spin clusters in the samples due to the distortion of local lattice and the inhomogeneous magnetic structure induced primarily by the random distribution of Mn ions. A maximum magnetoresistance ratio as large as 90% in 1 T at 122 K was obtained for the sample with x =0. 055, which is four times larger than that obtained for LCMO sample at 272 K. There is a remarkable field-history dependent MR in the cooling process for the doped samples while such phenomenon disappears in the warming run. The resistivity follows well the variable range hopping behavior in paramagnetic state. Both the size effect and spin dependent hopping of carriers between the spin clusters should be considered in this system.     

Effects of Y and Ce on Microstructures and Properties of Nb-Si System Composites

The effects of yttrium and cerium on microstructures and properties of Nb-Si system composites were investigated by scanning electron microscopy( SEM), energy dispersive spectrum(EDS), X-ray diffraction(XRD) and high temperature oxidation experiments.It is found that the coarse primary silicide phase became finer and more homogeneous with Y and Ce addition.The results of high temperature oxidation experiments show that the oxidation rates of NbSi system composites with an appropriate amount of Y and Ce decrease compared with those of alloys without Y or Ce addition, and oxidation products mainly distribute along the phase boundaries between the Nb solid solution and silicide.     

Synthesis, Characterization and Crystal Structure of Quaternary Complex of Gadolinium （Ⅲ）

Ａｎｕｍｂｅｒｏｆｌａｎｔｈａｎｉｄｅｔｅｒｎａｒｙｃｏｍｐｌｅｘｅｓｃｏｎ ｔａｉｎｉｎｇｈｅｔｅｒｏｃｙｃｌｉｃａｍｉｎｅｓｈａｖｅｂｅｅｎｒｅｐｏｒｔｅｄｓｉｎｃｅ1960 [1] .Ｉｎｒｅｃｅｎｔｙｅａｒｓｍｕｃｈａｔｔｅｎｔｉｏｎｈａｓｂｅｅｎｐａｉｄｔｏｑｕａｔｅｒｎａｒｙｃｏｍｐｌｅｘｅｓｏｆｌａｎｔｈａｎｉｄｅｓｂｅｃａｕｓｅｏｆｉｎ ｔｅｒｅｓｔｉｎｇｓｔｒｕｃｔｕｒｅ ,ｃｏｏｒｄｉｎａｔｉｏｎｍｏｄｅ ,ｃｏｍｐｅｔｉｔｉｏｎｒｅ ａｃｔｉｏｎａｎｄｐｒｏｐｅｒｔｙ[2～ 9] .ＥＳＲｃａｎｅ…     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     

稀土棕红色陶瓷颜料的制备

在低温下,采用溶胶均匀共沉淀法合成了含少量稀土氧化物CeO2的棕色陶瓷颜料,并应用颜色测定、SEM及XRD分析等手段对颜料的颜色、粒度及结晶构造进行了表征。同时,将合成的颜料应用于陶瓷釉料中,表明该颜料可以应用于1320℃的高温环境下。     

Effect of Rare Earth Element Cerium on Mechanical Properties and Morphology of TiN Coating Prepared by Arc Ion Plating

TiN coatings were deposited on polished substrates of W18Cr4V high speed steel by means of vacuum arc ion plating. The effect of cerium on adhesion between TiN coating and substrate was studied. The microstructures and composition of TiN coatings were also investigated by means of scanning electron microscope (SEM), Auger electron spectroscopy (AES), and X-ray diffraction (XRD) technique. It was found that cerium is an effective modifying agent and the addition of suitable amount of cerium to TiN coatings can produce relatively excellent properties such as micro-hardness, wear resistance, oxidation resistance and porosity. The experimental results show that the added cerium in TiN coatings makesa contribution to form the preferred direction along with a (111 ) or (222) close packed face, which may be one of the reasons that improves some properties mentioned above.