Spin Dependent Hopping in Ti Doped La0.67 Ca0.33 MnO3

A systematic investigation of the magnetic and transport properties of Ti doped La0.67Ca0.33MnO3 was reported. The Ti substitution for Mn ions results in a reduction in ferromagnetism and conductivity. The metal-insulator transition temperature is close to Curie temperature which decreases from 274 to 82 K as x increases from 0 to 0.17. The most important effect of Ti doping is to introduce spin clusters in the samples due to the distortion of local lattice and the inhomogeneous magnetic structure induced primarily by the random distribution of Mn ions. A maximum magnetoresistance ratio as large as 90% in 1 T at 122 K was obtained for the sample with x =0. 055, which is four times larger than that obtained for LCMO sample at 272 K. There is a remarkable field-history dependent MR in the cooling process for the doped samples while such phenomenon disappears in the warming run. The resistivity follows well the variable range hopping behavior in paramagnetic state. Both the size effect and spin dependent hopping of carriers between the spin clusters should be considered in this system.     

Effects of Y and Ce on Microstructures and Properties of Nb-Si System Composites

The effects of yttrium and cerium on microstructures and properties of Nb-Si system composites were investigated by scanning electron microscopy( SEM), energy dispersive spectrum(EDS), X-ray diffraction(XRD) and high temperature oxidation experiments.It is found that the coarse primary silicide phase became finer and more homogeneous with Y and Ce addition.The results of high temperature oxidation experiments show that the oxidation rates of NbSi system composites with an appropriate amount of Y and Ce decrease compared with those of alloys without Y or Ce addition, and oxidation products mainly distribute along the phase boundaries between the Nb solid solution and silicide.     

Synthesis, Characterization and Crystal Structure of Quaternary Complex of Gadolinium （Ⅲ）

Ａｎｕｍｂｅｒｏｆｌａｎｔｈａｎｉｄｅｔｅｒｎａｒｙｃｏｍｐｌｅｘｅｓｃｏｎ ｔａｉｎｉｎｇｈｅｔｅｒｏｃｙｃｌｉｃａｍｉｎｅｓｈａｖｅｂｅｅｎｒｅｐｏｒｔｅｄｓｉｎｃｅ1960 [1] .Ｉｎｒｅｃｅｎｔｙｅａｒｓｍｕｃｈａｔｔｅｎｔｉｏｎｈａｓｂｅｅｎｐａｉｄｔｏｑｕａｔｅｒｎａｒｙｃｏｍｐｌｅｘｅｓｏｆｌａｎｔｈａｎｉｄｅｓｂｅｃａｕｓｅｏｆｉｎ ｔｅｒｅｓｔｉｎｇｓｔｒｕｃｔｕｒｅ ,ｃｏｏｒｄｉｎａｔｉｏｎｍｏｄｅ ,ｃｏｍｐｅｔｉｔｉｏｎｒｅ ａｃｔｉｏｎａｎｄｐｒｏｐｅｒｔｙ[2～ 9] .ＥＳＲｃａｎｅ…     

稀土改善09CuPTiRE耐候钢耐蚀性的作用机理

应用扫描电镜(SEM)、离子探针(IMA)、X射线光电子能谱(XPS)和交流阻抗法研究含不同稀土耐候钢稀土提高耐大气腐蚀作用机理。结果表明,合适的稀土含量可显著提高钢的耐腐蚀性,稀土能促进Si、Cu和P在内锈层中以Si~(4+)、Cu~+和P~(5+)形态富集,并观察到锈层中的稀土。钢中加入稀土形成了致密连续厚而粘附性好的含硅铜稀土的复合铁锈层,从而提高了抗大气腐蚀性能。     

稀土棕红色陶瓷颜料的制备

在低温下,采用溶胶均匀共沉淀法合成了含少量稀土氧化物CeO2的棕色陶瓷颜料,并应用颜色测定、SEM及XRD分析等手段对颜料的颜色、粒度及结晶构造进行了表征。同时,将合成的颜料应用于陶瓷釉料中,表明该颜料可以应用于1320℃的高温环境下。     

Effect of Rare Earth Element Cerium on Mechanical Properties and Morphology of TiN Coating Prepared by Arc Ion Plating

TiN coatings were deposited on polished substrates of W18Cr4V high speed steel by means of vacuum arc ion plating. The effect of cerium on adhesion between TiN coating and substrate was studied. The microstructures and composition of TiN coatings were also investigated by means of scanning electron microscope (SEM), Auger electron spectroscopy (AES), and X-ray diffraction (XRD) technique. It was found that cerium is an effective modifying agent and the addition of suitable amount of cerium to TiN coatings can produce relatively excellent properties such as micro-hardness, wear resistance, oxidation resistance and porosity. The experimental results show that the added cerium in TiN coatings makesa contribution to form the preferred direction along with a (111 ) or (222) close packed face, which may be one of the reasons that improves some properties mentioned above.     

Effect of Y2O3, CeO2 on Sintering Properties of Si3N4 Ceramics

The effect of rare earth oxides Y203 or Ce02 on sintering properties of Si3N4 ceramics was studied and the mechanism of assisting action during sintering was analyzed. The results in dicate that the best sintering properties appear in Si3N4 ceramics with 5% Y203 or 8% CeO2. Secondary crystallites are formed at grain boundaries after heat treatment,which decreases the amount of glass phase and contributes to the improvement of high-temperature mechanical properties of silicon nitride.     

Study on Oxygen Isotope Fractionation in RE Oxide Minerals

ＳｔｕｄｙｏｎＯｘｙｇｅｎＩｓｏｔｏｐｅＦｒａｃｔｉｏｎａｔｉｏｎｉｎＲＥＯｘｉｄｅＭｉｎｅｒａｌｓＦａｎｇＴａｏ（方涛），ＱｉｕＹｕｚｈｕｏ（裘愉卓）（ＩｎｓｔｉｔｕｔｅｏｆＧｅｏｃｈｅｍｉｓｔｒｙ，ＡｃａｄｅｍｉａＳｉｎｉｃａ，Ｇｕｉｙａｎｇ５...     

高性能各向异性Sm2Fe17Nx磁粉的制备

本文研究了高性能各向异性Ｓｍ２Ｆｅ１７Ｎｘ磁粉的制备工艺路线与工艺参数。优化了制备与工艺参数。已制备出磁性能达到：Ｂｒ＝１．３９Ｔ，Ｈｃｉ＝８５０ＫＡ／ｍ和（ＢＨ）ｍ＝２３６ＫＪ／ｍ＾３的各向异性Ｓｍ２Ｆｅ１７Ｎ２．８８磁粉，该磁粉的各向异性场ＨＡ达到２０Ｔ。     

Fe73.5Cu1Nb3Si13.5B9非晶合金的晶化动力学

用ＤＴＡ结合ＸＲＤ了Ｆｅ７３．５Ｃｕ１Ｎｂ３Ｓｉ１３．５Ｂ９晶合金的晶化动力学。表明，该事金在５００℃时析出α－Ｆｅ（Ｓｉ）相。晶化初期激活能最小为２４２ｋＪ／ｍｏｌ，它随晶化量的增加，在ＸＣ为０．４－０．８时，呈极大值为５２０ｋＪ／ｍｏｌ。在６２４℃时析出Ｆｅ２Ｂ相。