Influence of Heat Treatment on Damping Behaviour of the Magnesium Wrought Alloy AZ61

The effect of isochronal heat treatments for 1h on variation of damping, hardness and microstructural change of the magnesium wrought alloy AZ61 was investigated. Damping and hardness behaviour could be attributed to the evolution of precipitation process. The influence of precipitation on damping behaviour was explained in the framework of the dislocation string model of Granato and Lücke.     

选矿拜耳法种分生产工艺优化与实践

选矿拜耳法新工艺产业化以来,随着拜耳法系统有机物的积累,造成种分分解率低、产品粒度细化等问题,提出向拜耳法种分系统添加碳分活性氢氧化铝晶种、向拜耳法种分系统补充一定量的烧结法精液、后加矿增浓溶出等优化措施,改善种分分解效果。经产业化应用后,取得了较好的经济效果,为选矿拜耳法新工艺的进一步优化提供了宝贵的经验。     

Sr对AZ91D镁合金枝晶生长和相析出的影响

加入微量Sr(0.01%-0.1%,质量分数)可明显细化AZ91D镁合金晶粒,随Sr含量增加,初生相α-Mg尺寸逐渐减小,而二次枝晶间距变化不大,同时β-Mg17Al12析出相增多.Sr添加量为0.1%时,针状或块状Al4Sr相依附在枝晶间的β-Mg17Al12相上析出.Sr在AZ91D合金凝固固-液界面前沿富集,并且优先在曲率较大的枝晶端面富集,从而抑制晶粒长大,细化了合金中初生相α-Mg;同时,Sr在枝晶的尖端富集降低了初生相α-Mg的尖端生长优势,改变了初生相形貌.     

V、N、Nb微合金化对薄板坯连轧带钢组织和性能的影响

在试验室模拟薄板坯连铸连轧过程，板坯均热后被轧制到7mm厚并通过控冷来模拟辊道冷却和带钢的缓慢卷取过程。本文选用低碳钢，研究了V、N、Nb微合金化对其组织和性能的影响。通过试验证明在V-N钢中加入Nb对钢的强化机制有较大影响，使V-N-Nb钢中的析出强化增大，这表明V-N-Nb微合金化可充分地发挥微合金元素在钢中的析出强化作用，析出强化对屈服强度的贡献比V-N微合金化提高17MPa。     

Precipitation kinetics of GP zones,metastable η′ phase and equilibrium η phase in Al−5.46wt.%Zn−1.67wt.%Mg alloy

Thermal analysis is one of the most used techniques for analyzing the behavior of aluminum alloys in order to analyze the precipitation of Guinier?Preston (GP) zones and different phases formed. In the present work, the behavior of the Al?5.46wt.%Zn? 1.67wt.%Mg alloy was studied. The mechanism and kinetics of precipitation of the GP, the metastable phase η′ and the equilibrium phase η were investigated using DSC carried out between room temperature and 480 °C at heating rates of 5, 10, 15 and 20 °C/min. The apparent activation energies, calculated by DSC from isothermal calculation method using JMAK model, for GP, η′ and η were 56, 79 and 96 kJ/mol, respectively, and those calculated by non-isothermal calculation method using Kissinger methods were 57, 82 and 99 kJ/mol, respectively. The values of Avrami parameter, n, from isothermal calculation, during the precipitation of the GP, η′ and η were 1.103, 1.9075 and 1.92, respectively, and those calculated by non-isothermal were 0.86, 2.30 and 2.24, respectively. The results show that GP zones formation is governed by the migration of Zn and Mg atoms while the precipitation of the η′ metastable phase and the η stable phase is governed by both the migration and the diffusion of the solute atoms.     

高温激光共聚焦显微镜在钢铁材料中研究进展

介绍了高温激光共聚焦显微镜的工作原理及主要功能,详细汇总了近年来高温激光共聚焦显微镜在钢铁冶金领域、材料研发领域、焊接领域的研究进展,包括钢液在高温熔融过程中夹杂物上浮、聚集、长大行为以及夹杂物聚集的动力学机制研究、相变行为等。利用高温激光共聚焦显微镜研究钢中典型珠光体、贝氏体和马氏体相变基本特征,探讨了不同尺寸粒子在高温对晶界的钉扎、溶解等行为,分析了当前应用过程中存在的主要问题,提出了相应的改进建议,并为后期高温激光共聚焦在钢铁材料领域的应用研究提供参考。     

W-Cu合金深冷处理及其组织性能研究

对粉末冶金熔渗技术制备的不同成分W—Cu合金在-196℃，保温48h进行深冷处理。采用X射线衍射仪和透射电子显微镜分析长时间深冷处理的现象与机理。结果表明：深冷处理后铜颗粒以短棒状形态在钨基体上弥散析出。析出的细小弥散的铜颗粒阻碍晶粒粗化和位错移动，铜颗粒部分填充到材料微孔内，同时深冷处理过程中的体积收缩也使材料内的部分缺陷如空位和微孔得到弥合，从而使不同成分的W—Cu合金的硬度提高，密度增大，电导率降低。     

三元体系γ′相和θ相沉淀早期计算机研究

基于三元合金沉淀动力学相场方程的微观离散格点形式建立模型。首次对Ni75Al11V14合金的γ′和θ2个有序相析出的早期过程进行了模拟，并计算了γ′有序相的成分序参数和长程序参数。结果表明：Ni75Al11V14合金中γ′相的沉淀机制为非经典形核长大兼有失稳分解特征，先形成非化学计量比有序相，然后才形成化学计量比有序组；非化学计量比θ有序相在γ′相界处形成，距离γ′相界越远，其有序程度越低，θ有序畴存在2种类型：水平分布和垂直分布，和它所依附的γ′相界面取向有关。     

铝酸钠(钾)溶液种分过程的分解率和粒度分布

采用等温间歇式反应器研究了纯铝酸钠和铝酸钾溶液在种分过程的分解率、粒度分布(PSD)的变化规律,同时对分解产品进行了XRD、SEM和TG/DTG分析.结果表明,在相同的分解条件下,铝酸钾溶液的分解率大于铝酸钠溶液;铝酸钠和铝酸钾溶液中颗粒的粒度分布随时间变化具有显著差异;产品的XRD显示,分解过程中铝酸钾比铝酸钠溶液中的晶体结晶度完整,但产品的TG/DTG曲线却没有明显的差别.对于不同ακ值的铝酸钠和铝酸钾溶液,这些差异是相似的.铝酸钾与铝酸钠溶液在种分过程中的成核速率不同可能是引起分解率和粒度分布产生差异的原因.