Inhibition of atmospheric corrosion of mild steel by sodium benzoate treatment

The objective of this study was to evaluate the effectiveness of sodium benzoate as an inhibitor to slow down or prevent atmospheric corrosion/discoloration of the local mild steel during storage in the Arabian Gulf region. Test specimens were prepared from locally produced reinforcing steel products. The inhibitor solution was applied on steel specimens at a concentration of 100 mM for 1 day at room temperature. Wooden exposure racks were used to hold as-received and inhibitor-treated specimens during atmospheric exposure for different periods. Corrosion was evaluated through weight loss determination and electrochemical technique. As expected, the Arabian Gulf atmosphere was corrosive on the as-received local mild steel. On the other hand, treatment of steel with sodium benzoate lowered its corrosion rate during initial days of its exposure to atmosphere. However, atmospheric corrosion inhibition performance of sodium benzoate deteriorated with exposure time after 30 or more days of atmospheric exposure, and the corrosion rates of sodium benzoate-treated specimens reached that of the unprotected specimens at the end of 90 days of atmospheric exposure.     

十二酰胺丙基二甲基羟乙基氯化铵与十二烷基硫酸钠水溶液的表面吸附和胶束形成

利用十二酰胺丙基二甲胺和氯乙醇反应 ,合成了十二酰胺丙基二甲基羟乙基氯化铵 (DDHA)阳离子表面活性剂 ,将其与十二烷基硫酸钠 (SDS)以不同摩尔比进行混合 ,测定了混合系统的表面张力 ,计算了单一系统和混合系统的饱和吸附量、分子最小截面积 ,表面层和胶束中 DDHA的摩尔分率及分子间相互作用参数 ,目视观察了混合系统的浑浊情况。结果表明 :在降低γcmc和 cmc方面 ,DDHA SDS混合系统有协同效应 ,表面层和胶束的组成与二组分配比有关 ,但是非对称的 ,等物质的量混合物中 ,DDHA在胶束和表面层中具有较大的摩尔分数。DDHA与 SDS在实验测定的各混合系统中都不出现混浊     

PEG20000中试放大的工艺研究

在一定温度和催化剂作用下 ,分别利用本体聚合和溶剂聚合的方法 ,在 1L、10 0L不锈钢高压反应釜中合成了相对分子质量为 2 0 0 0 0的聚乙二醇 ,并讨论了聚合反应机理 ,研究了催化剂用量、反应温度、反应时间对聚合反应的影响。经过红外、核磁共振、凝胶色谱、化学分析等方法对产物进行了表征。     

高温预析出对Al-Zn-Mg系铝合金时效硬化和应力腐蚀的影响

研究了高温固溶后降温处理工艺对中强可使预析出LC52和7039铝合金的组织、时效硬化和应力腐蚀的影响。金相观察发现,高温预析出可优先在晶界处产生,并提高随后时效状态下晶界析出相的不连续分布程度,温度降低到一定程度晶内和晶界产生大量析出。合金拉伸性能和应力腐蚀结果表明,预析出在保持强度和塑性的同时,可提高抗应力腐蚀性能。而预析出温度降低,合金强度呈下降趋势。     

用硫酸铁铵容量法测定钛精矿中二氧化钛含量

样品在过氧化钠熔融、水浸取及盐酸酸化后，在盐酸和硫酸介质中，隔绝空气，用金属铝将钛(Ⅳ)还原至钛(Ⅲ)，以硫氰酸盐为指示剂，用硫酸铁铵标准溶液滴定。     

Continuous precipitation of calcium sulfate dihydrate from waste sulfuric acid and lime

Precipitation of calcium sulfate dihydrate, gypsum, from (i) a pure sulfuric acid/lime suspension and (ii) a waste sulfuric acid/lime suspension in a continuous pilot plant in the temperature range from 40 °C to 80 °C was studied. It was observed that in the case of waste sulfuric acid with a high content of Mg²⁺ and Fe²⁺ ions, several hours after the beginning of the precipitation, partial dissolution of the product and modification of the crystals from needle‐ and plate‐like to agglomerated structures occurred. It is suggested that the secondary changes occur due to the increased concentration of Mg²⁺ and Fe²⁺ ions in the reactor. Below 60 °C, and above 70 °C plate‐like and needle‐like single crystals respectively were formed. The mean size (d₅₀) of the crystals was found to increase with increasing temperature and decrease with the initial concentration of lime. Gypsum produced between 70 °C and 80 °C is suitable for further processing for construction plaster. In a precipitation process with pure sulfuric acid only single perfect needle‐like crystals occurred. Copyright © 2005 Society of Chemical Industry     

Grain Growth Behavior of 5Cr21Mn9Ni4N Steel Micro-Alloyed by Rare Earth

Grain growth behavior of 5Cr21Mn9Ni4NRE steel was experimentally studied at various solid solution treatment temperatures and holding for different times. The experimental results show that the 5Cr21Mn9Ni4NRE steel has the feature of sharp austenite grain coarsening after solid solution treatment at the temperature above 1150 ℃. RE added in the steel has the benefit to restrain grain growth and increase grain growth activation energy.     

LW15-252型SF_6断路器存在的问题和对策

国产SF6断路器已在电力系统中得到了广泛的应用,随着时间的推移,这种断路器存在的问题也逐渐地暴露出来。笔者介绍了LW15-252型SF6断路器在实际运用中存在的问题和采取的对策。     

有机羧酸钠盐对PET结晶和熔融行为的影响

采用差示扫描量热仪研究了5种具有不同取代基的苯甲酸钠盐作为结晶成核剂对聚对苯二甲酸乙二醇酯（HET）结晶和熔融行为的影响，并同滑石粉进行了对比。结果表明，成核剂的加入能明显改变PET的结晶和熔融行为。苯甲酸钠、对苯二甲酸甲酯单羧酸钠和对羟基苯甲酸钠提高既汀的熔融结晶温度（Tc）分别达22．93、21．7和19．37℃，但使PET降解严重；对苯酚钠甲酸钠能够提高Tc达17．75℃且对PET相对分子质量影响很小；对苯二甲酸二钠成核作用最差。低于滑石粉。此外，成核剂的成核能力越强，PET双熔融峰中的低温峰顶温度就越高。     

新型香料苹果酯-B的合成

以硫酸高铈为催化剂,通过乙酰乙酸乙酯和1,2-丙二醇反应合成了苹果酯-B,研究了各有关因素对产品收率的影响。实验表明,硫酸高铈是合成苹果酯-B的良好催化剂,在酯醇物质的量比为1∶1.25、催化剂用量为0.3g/0.1mol乙酰乙酸乙酯、环己烷10mL、反应时间2h的条件下,苹果酯-B的收率可达91.5%。