高速钢表面PN＋PVD复合处理工艺和性能研究

采用多弧离子镀设备,在高速钢W18Cr4V上先进行等离子氮化,再沉积TiN薄膜,研究了不同渗氮温度和时间对PN＋TiN薄膜组织和性能的影响。结果表明,温度为500℃左右和时间为2h以上条件下对W18Cr4V进行渗氮处理后再沉积TiN薄膜,可以得到最佳的薄膜表面显微硬度（1800～2000HV0.05）和膜／基结合力（50N）,涂层耐磨性也得到明显提高。     

Oxidation and Fracture Strength of High-Purity Reaction-Bonded Silicon Nitride

Reaction-bonded Si₃N₄ (RBSN) made from high-purity Si powder is unusually resistant to degradation caused by exposures to air for up to 50 h at temperatures up to 1400°C. The weight gain during oxidation of this SiH₄-originating RBSN is approximately 10 times less than conventional RBSN. Contrary to normally observed strength degradations, room-temperature strengths of this high-purity, oxidized RBSN (avg = 435 MPa, max. = 668 MPa) remained at their unusually high, as-processed levels after 1000° and 1400°C oxidizing exposures. Fracture toughness values were unaffected by oxidation ( K _IC= 2.3 to 2.4 MPa · m^1/2). This superior oxidation resistance results from the high purity and the small diameter pore channels (0.01 to 0.06 μm) achieved in this SiH₄-originating RBSN.     

Loss of Curing Agent During Thin Film (Droplet) Curing of Thermoset Material

Recently, it has been reported by our group and others^1.2 that loss of curing agent is encountered during the curing of small droplets or thin films of amine cured epoxies. In our earlier study³ results were reported on loss of curing agent in small droplets used in conducting the rnicrobond, single fiber test for determination of interfacial shear strength (ISS). It was reported that use of a volatile curing agent (meta-phenylene diamine (m-PDA) with DGEBA resin) resulted in increasing amounts of curing agent being lost (as measured by T₈ of the cured droplets) with decreasing droplet size during the processing procedure. Droplets smaller than 150 micrometers were seen to lose up to 40% of the curing agent leading to alteration of the mechanical properties of the droplet and, therefore, causing measured values of ISS to be exceedingly low. Use of a less volatile curing agent (Jeffamine 700, a polyether diamine, Texaco Specialty Chemicals) in combination with DGEBA resin produced results which indicated that loss of curing agent was not occuring. This study was undertaken to show the relationships between film (or droplet) size and the amount of curing agent lost (during the processing) for three different aminecured epoxy systems.     

A Thermo-Mechanical Study of Some Epoxy Adhesives Subjected to Combined Dynamic and Static Stresses

The object of the present study was to investigate the effect of superimposed dynamic and static stresses on mechanical and thermal properties of some epoxy adhesives. It was found that combinations of shear creep and torsional oscillations, applied simultaneously to adhesive joints at temperatures within the glassy range of the adhesive, led to strengthening of the joints in shear and to an increase in the glass transition temperature of the adhesive. Similar loading stresses applied at temperatures close to the T_g of the adhesive, led to opposite effects on the above mentioned properties of the joints. The width of the glassy-rubbery transition of the adhesives increased, in the whole range of temperatures used in this study and for all epoxy compositions, as a result of subjecting the joints to superimposed dynamic and static stresses. The broadening of the glass transition was interpreted as a result of the stiffening of polymer network during the combined stressing experiments. A linear relationship was found between the area of endothermal peaks in the first DSC scan of specimens subjected prior to test to superimposed dynamic and static stresses at temperatures below T_g, and the shear strength of the joints. In agreement with this observation and with literature data, a linear relationship was revealed also between the glass transition temperature of the resins (measured in the first DSC scan) and the shear strength of the joints. Based on experimental observations and on some literature information, it was suggested that the strengthening of the joint, as well as the changes in thermal properties of the adhesives, are mainly due to physical processes, such as short-range orientation of network chains and an increase in intermolecular interaction between highly polar sites of the network. The possibility that superimposed stressing led to changes in chemical crosslinking was discussed but it seems that no such reactions occurred.     

高功率移相器粘接工艺初探

主要介绍了粘接技术在高功率铁氧体移相器上的应用。通过对其工艺途径及关键工序的控制，提出了采用粘接技术完成高功率移相器铁氧体的连接，不仅可以大量地缩短工作时间，而且可以使制造成本大幅度降低。     

投资项目经济评价指标的研究

本文在探讨“平坦”模糊数及其运算的基础上,提出模糊内部收益率的概念;并利用Prade与Dubois提出的比较两个模糊数大小的指标,给出“近似相等”的概念;从而给“模糊内部收益率”的计算提供了一个方法。     

铁路选线环境影响量化分析计算方法及应用研究

根据防护费用法、影子工程法等折算办法对环境破坏导致的经济损失等价为具体货币值,并将这些环境影响量化分析计算方法应用于西宝客运专线建设的环境评价问题中.结果表明:提出的算法对铁路选线多目标决策方案比选有应用价值.     

基于表面反应和扩散迁移控制的灰岩单裂隙渗流—溶解模型及其数值模拟

针对碳酸盐类可溶岩地区水电站坝址流场、化学场以及固相介质属性等随时间发生改变,从而对工程安全运行造成不利影响等问题,研究了灰岩地区地下水运移过程中各物理场间的相互作用,分析了影响灰岩溶解速率的两个因素,即表面反应控制和扩散迁移控制。在此基础上,建立了单裂隙中的渗流—溶解耦合模型,并进行数值求解。模拟结果表明,在垂直裂隙延伸方向,其溶蚀锋面为非齐整平面,而是呈似“虫洞”状非均一变化,而沿裂隙延伸方向即自上游侧向下游方向溶蚀程度逐渐减轻;而通过裂隙的流量呈现随时间逐渐增大的趋势,但变幅不大;根据流量求得的等效水力隙宽,其增幅和增长速率均小于实际平均隙宽;同时,化学场中Ca2+浓度的分布与裂隙开度变化具有相似性,不同时刻下上游侧反应速率R均大于下游侧。就反应机制而言,在初期均受表面反应控制,而随反应进行,位于上游补给区部位转为受扩散迁移控制,但在下游位置仍受表面反应控制。     

金属材料屈服强度的应变率效应和热激活理论

对４种金属材料进行了应变率为１０＾－４－１０＾３ｓ＾－１的拉伸试验，结果表明，屈服中度随应变率的升高分两阶段线性升高，提出了位错线热振动对加载频率的响应的热激活作用机理，依据该机理计算所得Ⅰ，Ⅱ区临界应变εｃ与实测值相符，并在此基础上将应变率对掘强度影响的机制图重新划分为：Ｉ区，富热激活区；Ⅱ区，贫热激活区。