高合金铁基烧结材料在轧钢导位中的应用研究

本文研究了高合金铁基烧结材料在轧钢导位中的应用。实验表明,通过粉末冶金液相烧结技术,可以获得具有优良综合性能的制品,材料密度ρ≥7.5 g/cm3,硬度≥55 HRC,抗弯强度≥1 000 MPa,冲击韧度αk≥3.9 J/cm2,满足了轧钢导位辊的工作要求。材料利用率可达95%以上、降低了制备成本。使用寿命是普通轧辊寿命的3~6倍,适用于线材和小型型材的轧钢生产。     

Development of sealing compositions with nanostructure iron-based fillers

The possibility of utilizing nanopowders of iron and Fe-Co-Ni produced bu a thermochemical method in the fabrication of sealing composition materials is investigated. It is established that such hermetic sealing composition materials function reliably under extremal conditions and guarantee elevated strength of adhesion to the surface of the metal and high corrosion and temperature stability. __________ Translated from Poroshkaya Metallurgiya, Nos. 3–4(448), pp. 112–117, March–April, 2006.     

纳米镍粉的制备工艺及产业化研究进展

综述了纳米镍粉的制备方法(包括物理法和化学法)及产业化现状,对纳米镍粉的各种制备方法进行了分析和评价。与物理法相比,化学法的产量高、成本低廉,能制备出性能优异的纳米镍粉,适合规模化生产;使用化学法制备的纳米镍粉的纯度、粒径及成本的控制仍需进一步加强。同时,对今后纳米镍粉的制备和产业化发展提出了建议。     

Synthesis and characterisation of a submicrometre silicon carbide powder

A beta-silicon carbide powder with a surface area of 30m²g^?l and a mean particle size of < 1μm was produced from the thermal conversion of silicon resin in an atmosphere of hydrogen. The amount of product increased with increasing iron content (0–2.1 wt%) and firing temperature (1200–1500°C). Chemical analysis, X-ray diffraction and i.r. absorption spectrometry were used to follow the conversion reaction.     

超细氧化锌粉体的制备及尺寸控制

根据气相化学反应法 (CAD)制备超细粉的原理 ,从低品位氧化锌矿中采用火法冶金方法直接制备超细氧化锌粉 ,对所得氧化锌的粒度尺寸、微观结构和粒度分布进行测试 ;考察了冷却强度以及收集装置对超细氧化锌粒度及粒度分布的影响 ;讨论了氧化锌粉体团聚的原因及对策、试验条件对氧化锌尺寸的控制等     

土壤固化剂无侧限抗压强度试验研究

针对山西省长治市石子河河道处理问题 ,采用固化剂粘土进行了无侧限抗压强度试验 ,并与水泥土进行了比较。发现固化剂 2的无侧限抗压试验强度最佳 ,为工地现场试验及河道综合治理提供了更为有力的理论依据     

水平浓缩燃烧器在65t/h煤粉炉上的应用

介绍65t/h煤粉炉的基本概况和存在的问题，详细阐述了采用水平浓缩煤粉燃烧技术对原燃烧器的改造过程，对改造前后运行参数及经济效益进行了对比。     

Influence of melt superheat on breakup process of close-coupled gas atomization

In close-coupled gas atomization（CCGA）, the influences of melt superheat on breakup process are fundamental to obtain desired or finer powder. Based on a series of Cu atomization experiment under different superheating conditions, the influences of melt superheat on breakup process were studied. Experimental results indicate that as the melt superheat is increased to 150, 200, 250 and 300 K, the mean particle size （D50） decreases consequently to 34.9, 32.3, 30.9 and 19.7 μm. Theoretical analysis reveals that the primary breakup and secondary breakup processes are close coupled, and the melt superheat radically influences the melt properties, and plays a crucial role on governing the filming process of primary breakup and the atomization modes of secondary breakup. There exists a strong nonlinear decrease of contact angle of melt to nozzle orifice wall when the superheat is increased fi＇om 250 K to 300 K, leading to a marked fall of the film thickness formed in primary breakup, and D50 of copper powders is therefore sharply reduced. However, the log-normal distribution feature of particle size has not been substantially improved.     

莫来石材料的研究现状及其应用

较详细地介绍了莫来石的性能、生产、研究现状和用途。尤其对多元复合莫来石韧性陶瓷及莫来石超细粉末的制备进行了评述,同时展望了莫来石作为高级陶瓷材料的发展前景。     

Rolling contact fatigue behavior of sintered and hardened steels

Powder-metal-processed bearings and gears are finding increasing application because of their economical and technical advantages. The residual pores from the sintering operatives act as lubricant pockets and dampen sound and vibration. However, porosity also decreases the mechanical strength and reduces the life of components fabricated by powder processing relative to similar wrought components. The rolling contact fatigue behavior of sintered and heat treated steel rollers was investigated using a fatigue test machine designed and fabricated for that purpose. The powder-metal-processed and the wrought steel rollers that were tested had similar composition and hardness and were mated against wrought steel rollers of high hardness. The contact stress versus number of cycles to failure data showed that the wrought steel had a very high endurance limit under rolling contact fatigue compared to the sintered steels investigated. Rolling contact fatigue behavior was found to depend on the porosity present in the material. Large surface peeling failures and pitting type fatigue failures were observed in the sintered and hardened steels, while only pitting type failures were observed in the wrought steels