The reaction of ceria coatings on mica with H2S: An in-situ X-ray diffraction study

Thin layers of ceria were deposited on the surface of mica platelets in solution. The reaction of such particles with hydrogen sulfide yields a red colored special effect pigment. The ceria layer reacts with H₂S to produce a variety of sulfide and oxysulfide phases. The reaction path discovered in situ by time and temperature resolved X-ray diffraction is CeO₂→CeS₂→C-Ce₂S₃→Ce₁₀S₁₄O. The reaction itself is extremely variable depending on gas flow, heating rates and decomposition atmospheres. Effects on the thin film are recorded by scanning electron microscopy (SEM) and revealed a destruction of the layer once red Ce₁₀S₁₄O was formed. The product layer then reveals the typical nonwetting behaviour of a liquid on a surface.     

Synthesis of LiFePO4 with fine particle by co-precipitation method

LiFePO₄ is a potential candidate for the cathode material of the lithium secondary batteries. A co-precipitation method was adopted to prepare LiFePO₄ because it is simple and cheap. Nitrogen gas was needed to prevent oxidation of Fe²⁺ in the aqueous solution. The co-precipitated precursor shows the high reactivity with the reductive gas, and the single phase of LiFePO₄ is successfully synthesized with the aid of carbon under less reductive conditions. LiFePO₄ fine powder prepared by co-precipitation method shows high rate capability, impressive specific capacity and cycle property.     

Effects of gallia additions on sintering behavior of gadolinia-doped ceria

The effects of gallia additions on the sintering behavior of gadolinia-doped ceria were systematically investigated from the following aspects: the variation in sintered density, the variation in grain size, and the existing forms of Ga₂O₃ in CeO₂.Sintered density increased with increasing Ga₂O₃ content up to 5 mol.% and then it decreased with further addition of Ga₂O₃. Grain size also increased with increasing Ga₂O₃ content up to 5 mol.% and then decreased with further addition of Ga₂O₃. Decrease in grain size was caused by a pinning effect of Ga₂O₃ precipitation at grain boundaries. Lattice constant decreased with increasing Ga₂O₃ content up to 5 mol.%. This decrease will be due to the substitution of smaller Ga³⁺ ions for Ce⁴⁺ ions in the CeO₂ structure. According to the results obtained from scanning electron microscope (SEM) and X-ray diffraction (XRD) analyses, the solubility limit of Ga₂O₃ in Ce_0.8Gd_0.2O_1.9 ceramics can be estimated to be nearly 5 mol.%. The addition of Ga₂O₃ up to the solubility limit was found to promote the sintering properties of Gd₂O₃-doped CeO₂.     

Solution of a multidimensional inverse radiation problem by means of mode reduction

The Karhunen–Loève Galerkin procedure is employed to solve an inverse radiation problem of determining the time‐varying strength of a heat source, which mimics flames in a furnace, from temperature measurements in three‐dimensional participating media where radiation and conduction occur simultaneously. The inverse radiation problem is solved through the minimization of a performance function, which is expressed by the sum of square residuals between calculated and observed temperature, using a conjugate gradient method. Through the Karhunen–Loève Galerkin procedure, one can represent the system dynamics with a minimum degree of freedom, and consequently the amount of computation required in the solution of the inverse problem is reduced drastically when the present technique is adopted. Copyright © 2004 John Wiley & Sons, Ltd.     

Electrical conductivity and gas sensitivity of Zn-Sb-O thick films

The thick film of Zn-Sb-O was prepared by coating the paste of nanoparticles mixture (Sb₂O₃:ZnO=1:3) on the alumina substrate, followed by sintering at 500-900 °C for 2 h in air. The electrical resistance and gas-sensing properties to benzene, alcohol and acetone of Zn-Sb-O films were found to be dependent on the change of phase structure caused by sintering temperature.     

Fast microwave detection system for coherent synchrotron radiation study at KEK: Accelerator test facility

A fast room temperature microwave detection system based on the Schottky Barrier-diode detector was created at the KEK ATF (Accelerator Test Facility). It was tested using Coherent Synchrotron Radiation (CSR) generated by the 1.28 GeV electron beam in the damping ring. The speed performance of the detection system was checked by observing the CSR from a multi-bunch (2.8 ns bunch separation time) beam. The theoretical estimations of CSR power yield from an edge of bending magnet as well as new injection tuning method are presented. A very high sensitivity of CSR power yield to the longitudinal electron distribution in a bunch is discussed.     

Assessing organo-clay dispersion in polymer layered silicate nanocomposites: A SAXS approach

A SAXS method for the quantitative assessment of the morphology of polymer layered silicate nanocomposites is proposed. Fitting the SAXS patterns, the number of clay layers, the periodicity of the layers in the tactoids, the thickness of the regions interposed between the clay platelets and their distributions can be measured. A good agreement with TEM data was obtained, avoiding the inconsistencies with microscopical observations often reported in the literature.     

Time dependent crystal-smectic transformation in perylene-containing polyimides

The crystalline conformations of perylene polyimides (PPIs), with alkyl spacers varying in length from C₃ to C₁₂ are discussed. Although modeling of single chains would suggest the possibility that those with odd number of CH₂ groups adopt a flat helical shape, X-ray diffraction suggests that the chains with odd and even spacers have the same conformation, due to the necessity to pack the perylene units. Upon annealing, the UV-vis absorption maximum red-shifts by about 10 nm, indicating enhanced π-stacking between the perylenes. Several changes in the spectra are seen with an increase in annealing time, at a given temperature. With an increase in annealing time, X-ray diffraction patterns show changes in the number of reflections, indicative of a crystal to mesogenic transition. The time required for this transition increases with a decrease in the spacer length, and annealing temperature, suggesting that the dynamics of this transition is very slow.     

Life cycle of hydroprocessing catalysts and total catalyst management

Hydroprocessing catalysts based on Ni, Co, Mo and W are used in various refinery processing applications where several deactivation mechanisms become of importance (coke formation, active phase sintering, metals deposition, poisoning) in the catalyst's life cycle. The life cycle of commercial hydroprocessing catalysts is very complex and includes the catalyst production, sulfidation, use, oxidative regeneration followed by re-sulfidation and reuse or, if reuse is not possible, recycling or disposal. To understand the changes in catalyst properties taking place during a life cycle, the catalyst quality in the different stages can be best monitored by using advanced analytical techniques. The catalyst's life cycle is further complicated by numerous technical, environmental and organizational issues involved. In principle, different companies can be involved in each of the life cycle steps. Leading catalyst manufacturers, together with specialized firms, offer refineries a total catalyst management concept, starting with the purchase of the fresh catalyst and ending with its final recycling or disposal. Total catalyst management includes a broad range of services, ensuring optimal timing during the change-out process, reliable, smooth and safe operations, minimal downtime and maximum catalyst and unit performance.     

A small-angle X-ray scattering study of powder compaction

This work demonstrated a novel and potentially important application of two-dimensional small-angle X-ray scattering (2D-SAXS) to investigate powder compaction. SAXS from powder compacts of three materials commonly used for pharmaceutical tabletting exhibited azimuthal variations, with stronger intensity in the direction of the applied compaction force, relative to the transverse direction. This implied that compaction of a (macroscopic) powder could also produce changes on the molecular (nanometre) scale, which can be probed by 2D-SAXS. Two possible explanations for this effect were suggested. A combination of anisometric (i.e. elongated or flattened) granules with anisotropic morphologies could result in azimuthal variation in X-ray scattering due to granule orientation. It is expected that this mechanism would require relatively low packing density, so may operate during die filling. Granule re-orientation appeared less likely at higher packing densities and compaction pressures, however. Under these conditions, the changes in the 2D-SAXS patterns would be consistent with the powder granules becoming relatively flattened in the compression direction, with corresponding changes in their nano-scale morphology. The magnitude of this effect was found to vary between the materials used and increased with compaction pressure. This suggested that 2D-SAXS studies could provide useful information on force-transmission within a compressed powder. Further analysis of the data also suggested differences in the compaction mechanisms (i.e. granule re-orientation, deformation or fragmentation) between the materials studied.