Heat resistance of Escherichia coli O157:H7 in cook‐in‐bag ground beef as affected by pH and acidulant†

Summary The heat resistance of a four‐strain mixture of Escherichia coli O157:H7 was tested. The temperature range was 55–62.5 °C and the substrate was beef at pH 4.5 or 5.5, adjusted with either acetic or lactic acid. Inoculated meat, packaged in bags, was completely immersed in a circulating water bath and cooked to an internal temperature of 55, 58, 60, or 62.5 °C in 1 h, and then held for pre‐determined lengths of time. The surviving cell population was enumerated by spiral plating meat samples on tryptic soy agar overlaid with Sorbitol MacConkey agar. Regardless of the acidulant used to modify the pH, the D ‐values at all temperatures were significantly lower (P < 0.05) in ground beef at pH 4.5 as compared with the beef at pH 5.5. At the same pH levels, acetic acid rendered E. coli O157:H7 more sensitive to the lethal effect of heat. The analysis of covariance showed evidence of a significant acidulant and pH interaction on the slopes of the survivor curves at 55 °C. Based on the thermal‐death–time values, contaminated ground beef (pH 5.5/lactic acid) should be heated to an internal temperature of 55 °C for at least 116.3 min and beef (pH 4.5/acetic acid) for 64.8 min to achieve a 4‐log reduction of the pathogen. The heating time at 62.5 °C, to achieve the same level of reduction, was 4.4 and 2.6 min, respectively. Thermal‐death–time values from this study will assist the retail food processors in designing acceptance limits on critical control points that ensure safety of beef originally contaminated with E. coli O157:H7.     

Strength of Metals at High Strain Rates

Results of metal testing in impact tension–compression and indentation are analyzed. As the analysis of these data demonstrates, the strength of metals increases greatly with strain rates and at moderate indentation rates. At high indentation rates, a decrease in the specific energy (per unit volume of a displaced material) necessary for the formation of a conical cavity was observed. The account of the effects of viscosity, temperature increase upon plastic deformation and its localization can be used to explain the above phenomena.     

Modelling thermal degradation of composite materials

A one–dimensional, transient thermal degradation heat transfer model for the response of composite materials when exposed to fire is presented. The model can handle layers of different materials. Material properties are functions of temperature. The reaction can be specified using Arrhenius‐type parameters or by inputting a density–temperature relationship determined by any experimental technique such as thermogravimetric analysis. The model is validated against the experimental data presented in Boyer's 1984 dissertation. Overall, the model provides excellent agreement with the experimental data. It is shown that very little difference is found between results arrived at by Arrhenius kinetics and results obtained by specifying the easier to measure density–temperature relationship. From this it is concluded that this technique is a viable alternative to Arrhenius‐type models. Copyright © 2006 John Wiley & Sons, Ltd.     

A dynamic linear programming approach to market allocation of renewable resources in the italian energy system: The case of solar thermal and biogas technologies

In Italy solar thermal energy and energy from biogas are two possible means of reducing dependence on energy imports. Using a multiperiod LP model (MARKAL) the authors assessed the likely potential of both technologies under various circumstances. The study covered the period 1980–2005, in five segments of five years. It focused only on the subsystem of the energy end-uses which can be substituted for by solar thermal and biogas technologies. The overall non-renewable sources which can be saved in 20 years by these technologies total 450 PJ (1 PJ = 10^{1 5} J) if the fuel prices rise at 0 per cent average annual, 1450 PJ if the fuel prices rise at 4.2 per cent average annual, 1860 PJ if the fuel prices rise at 7.2 per cent average annual and 3780 PJ if the fuel prices rise at 15 per cent average annual. However the most competitive technologies appear to be solar water heaters used mainly in the private and commercial sectors and biogas systems used mainly in the agricultural sector. The study was carried out by APRE under ENEA (formerly CNEN) contract and was intended to serve as an analytical basis for establishing an overall development and demonstration strategy for end-use renewable technologies in Italy.     

Thermal Evaluation of Scorched Graphite-Epoxy Panels by Infrared Scanning

A simple measurement system is described for evaluating damage to graphite-epoxy panels, such as those used in high-performance aircraft. The system uses a heating laser and infrared imaging system to measure thermal performance. Thermal conductivity or diffusivity is a sensitive indicator of damage in materials, allowing this thermal measurement to show various degrees of damage in graphite-epoxy composites. Our measurements track well with heat-flux damage to graphite epoxy panels. This measurement system, including analysis software, could easily be used in the field, such as on the deck of an aircraft carrier or at remote air strips.     

The flame retardant mechanism of polyolefins modified with chalk and silicone elastomer

This paper presents the current understanding of the flame retardant mechanism of Casico?. The study includes the flame retardant effect of each individual component: ethylene–acrylate copolymer, chalk and silicone elastomer, as well as the formation of an intumescent structure during heating. The flame retardant properties were investigated by cone calorimetry and oxygen index tests. To obtain insight into the flame retardant mechanism, heat treatment under different conditions has also been performed. The results indicate that the flame retardant mechanism of Casico is complex and is related to a number of reactions, e.g. ester pyrolysis of acrylate groups, formation of carbon dioxide by reaction between carboxylic acid and chalk, ionomer formation and formation of an intumescent structure stabilized by a protecting char. Special emphasis is given to the formation of the intumescent structure and its molecular structure as evaluated from ¹³C MAS‐NMR and ²⁹Si MAS‐NMR, ESCA and XRD analysis. After treatment at 500°C the intumescent structure consists mainly of silicon oxides and calcium carbonate and after treatment at 1000°C the intumescent structure consists of calcium silicate, calcium oxide and calcium hydroxide. Copyright © 2003 John Wiley & Sons, Ltd.     

Copolymerization of bromophenylmaleimide with ethyl or butyl methacrylate

N‐p‐Bromophenylmaleimide (BrPMI) does not polymerize in solution by conventional free radical mechanism. However, it readily polymerized in bulk when mixed with a free radical initiator and heated in a microwave oven for 7–8 min. Copolymerization of ethyl methacrylate or butyl methacrylate with BrPMI was conducted in dioxane. The copolymers were characterized by IR and ¹H NMR spectroscopy and gel permeation chromatography. The monomer reactivity ratios were calculated by a non‐linear least‐square analysis. Thermal analysis indicated a great improvement in thermal stability of the copolymers compared with the methacrylate homopolymers. BrPMI was also polymerized in bulk in the DSC pan, which allowed the calculation of the activation energy of its polymerization. Copyright © 2003 Society of Chemical Industry