新一代高活性，高水热稳定性3961（PS－Ⅳ）型连续重整催化剂于1996年在上海石化芳烃厂400kt/a连续重整装置上首次进行工业应用试验。开工5a，催化剂跟踪分析结果表明，该剂保持了良好的物化性质和反应性能，表现为良好的比表面积稳定性和持氯能力，经过200个以上再生周期的催化剂未发现有明显的相变和金属分散度的变化。     

固载于SBA-15分子筛中的同双核金属配合物催化剂

合成了3种同双核金属配合物[M2LCl3]Cl(L代表配体三亚乙基四胺,M代表Co,Cu,Cr),采用微波加热法合成了SBA-15分子筛,采用浸渍法将3种同双核金属配合物分别固载在表面官能化的SBA-15分子筛(SBA-15-NH2分子筛)中制得负载型催化剂。傅里叶变换红外光谱、X射线衍射、紫外可见光谱和热分析表征结果表明,同双核金属配合物被固载后,其结构仍保持完整。以环己烷氧化反应为探针反应,考察了[Co2LCl3]Cl/SBA-15-NH2,[Cu2LCl3]Cl/SBA-15-NH2,[Cr2LCl3]Cl/SBA-15-NH2催化剂的活性,环己烷转化率分别为11.0%,49.5%,57.9%;对于[Cr2LCl3]Cl/SBA-15-NH2催化剂,当分别以乙睛、丙酮和冰醋酸为溶剂时,环己烷转化率分别为57.9%,52.1%,34.2%,3次重复实验的环己烷转化率分别为57.9%,47.8%,46.5%,表明该催化剂具有较好的活性和重复使用性。     

Ti-silicalite as catalyst for gas-phase ammoximation of cyclohexanone with molecular oxygen

The catalyst behaviour of titanium silicalite, which was found the most active and selective catalyst for liquid-phase ammoximation of cyclohexanone to the corresponding oxime with hydrogen peroxide, was investigated in the gas-phase ammoximation with molecular oxygen in and compared with those of pure silicalite and samples of vanadium and chromium silicalites. The results showed that Ti-silicalite is a selective catalyst not only in the reaction with hydrogen peroxide but also in the reaction with molecular oxygen. However, a big limitation was found in the poor activity of the silicalites which do not allow to reach high oxime yields.     

La-OMS-2催化剂催化甲苯氧化制苯甲醛

合成了氧化锰八面体(OMS-2)分子筛,采用离子交换法和浸渍法制备了稀土金属La改性的OMS-2分子筛(La-OMS-2)催化剂,并用于甲苯液相选择性氧化制苯甲醛,考察了催化剂用量、反应温度、反应时间、氧气流量及溶剂种类对甲苯转化率和苯甲醛选择性的影响,对La-OMS-2催化剂进行了X射线衍射表征和BET比表面积测定。实验结果表明,离子交换法制备的La-OMS-2-A催化剂的活性高于浸渍法制备的La-OMS-2-B催化剂,在甲苯0.1mol、溶剂冰乙酸10mL、氧气流量60mL/min、La-OMS-2-A催化剂用量0.10g、反应温度353K、反应时间1.0h的条件下,甲苯转化率达61%,苯甲醛收率为56%。加入La对OMS-2分子筛中的MnO晶格结构产生了影响,提高了苯甲醛的收率。     

悬浮床加氢裂化油溶性催化剂与沥青质的作用

在高压釜反应器中对添加了油溶性 Ni 催化剂(UPC-O)和水溶性 Ni 催化剂(UPC-W)的辽河稠油常压渣油(LHAR)进行了悬浮床加氢裂化实验。通过元素分析和傅里叶变换红外光谱(FTIR)分析对抑制反应生焦效果好的 UPC-O 与 LHAR 沥青质的作用进行了研究。元素分析结果显示,在 LHAR 中加入 UPC-O1000μg/g,沥青质和脱沥青质油中 Ni 含量分别出476μg/g和110μg/g 增加到7 559μg/g 和1 024μg/g,表明 UPC-O 在沥青质中有富集的趋势。FTIR 表征结果显示,UPC-O 和沥青质发生了相互作用。UPC-O 可在沥青质原位硫化为活性组分,对沥青质在悬浮床加氢裂化反应中的缩合起到好的抑制作用。     

降低汽油烯烃含量裂化催化剂LBO-12的研制与开发

探讨了催化裂化过程降低汽油烯烃的反应原理，研究了催化剂各组分对裂化汽油性质影响的规律性，围绕提高氢转移活性，提出制备降烯烃裂化催化剂的技术路线，并研制开发了新型LBO-12降烯烃催化剂，固定流化床反应器对中试样品的评价和工业应用结果表明，该催化剂在不损失汽油辛烷值的前提下，降低催化裂化汽油烯烃能力较强，并具有较高的水热活性稳定性和良好的抗重金属污染特性。     

大庆蜡油在酸性催化剂上反应机理的研究

以大庆蜡油为原料，采用两种不同类型的催化剂，在流化床反应器实验装鬣上进行催化裂化反应。结果表明，大庆蜡油在酸性催化剂上反应所产生的干气组成与高烯烃催化裂化汽油相同，干气的产生主要是单分子裂化反应所造成的。从干气产率、组成以及液化气组成可以看出，大庆蜡油在不同类型的催化剂上明显地表现出裂化反应类型的差异。     

Syngas production via combined oxy-CO2 reforming of methane over Gd2O3-modified Ni/SiO2 catalysts in a fluidized-bed reactor

In this research, Ni/SiO₂ catalyst was modified with different amount of Gd₂O₃ and characterized with temperature-programmed desorption of CO₂ (CO₂-TPD) and NH₃ (NH₃-TPD), temperature-programmed reduction with H₂ (H₂-TPR) and X-ray diffraction (XRD). It was found that Gd₂O₃-modified Ni/SiO₂ catalysts possessed higher CO₂ adsorption and activation ability due to the formation of surface carbonate species. H₂-TPR and XRD characterizations found that the strong interaction among nickel, Gd₂O₃ and SiO₂ took place, which improved the dispersion of Ni. Gd₂O₃-modified Ni/SiO₂ catalysts exhibited higher activity and stability for the combined oxy-CO₂ reforming of methane in fluidized-bed reactor. The H₂/CO ratio in produced syngas could be controlled via controlling reaction temperature and CO₂/O₂ ratio in feed.     

Effect of carbon surface oxidation on platinum supported carbon particles on the performance of gas diffusion electrodes for the oxygen reduction reaction

The effect of carbon surface oxidation on platinum supported carbon particles (Pt/C) with nitric acid was investigated by cyclic voltammetry, electrochemical impedance spectroscopy, polarization experiments and chronoamperometry. Cyclic voltammograms, polarization curves and electrochemical impedance spectra showed that the treated catalyst had much larger active surface area and higher ionic conductivity than the untreated catalyst, and provided enhanced performance for oxygen reduction. The formation of acidic groups was examined by IR spectra. The Pt/C surface oxidation had a large effect on the performance of a gas diffusion electrode for oxygen reduction reaction.     

Towards a new definition of EPOC parameters for anionic electrochemical catalysts: case of propene combustion

The electrochemical promotion of catalysis (EPOC) of propene combustion was investigated using Pt sputtered thin film on an O²⁻ conductor, 8 mol% Y₂O₃-stabilized-ZrO₂ (YSZ). In order to separate the influence of the thermal migration of the O²⁻ oxide ions from the electrolyte to the catalyst surface and the impact of an electrical polarization on the catalytic activity, several light-off experiments (cool down and heat up procedures) were successively performed under different polarizations, i.e. OCV, +2 and −2 V. These experiments have clearly shown that the presence of O²⁻ (thermally or electrochemically induced) inhibits the catalytic activity of the platinum for the propene deep oxidation. These results demonstrate the importance to define a normalized rate enhancement ratio, ρ _n , from a reference value of the catalytic rate corresponding to a Pt surface state free of O²⁻ ions.