热处理对Ti-25V-15Cr-2Al-2Mo-0.2C合金组织稳定性的影响

研究了热处理对Ti-25V-15Cr-2A1-2Mo-0.2C阻燃β钛合金组织稳定性的影响。结果表明，高温固溶并直接时效处理导致合金β基体上析出较多的α相沉淀，尤其在随后的热暴露组织中形成了恶化合金塑性的连续晶界α膜。然而，若在时效前再进行一次低温固溶处理则可明显减少α相的析出数量，合金的热稳定性因此而得到显著改善。     

Pool boiling on a superhydrophilic surface

Titanium Dioxide, TiO₂, is a photocatalyst with a unique characteristic. A surface coated with TiO₂ exhibits an extremely high affinity for water when exposed to UV light and the contact angle decreases nearly to zero. Inversely, the contact angle increases when the surface is shielded from UV. This superhydrophilic nature gives a self-cleaning effect to the coated surface and has already been applied to some construction materials, car coatings and so on. We applied this property to the enhancement of boiling heat transfer. An experiment involving the pool boiling of pure water has been performed to make clear the effect of high wettability on heat transfer characteristics. The heat transfer surface is a vertical copper cylinder of 17 mm in diameter and the measurement has been done at saturated temperature and in a steady state. Both TiO₂-coated and non-coated surfaces were used for comparison. In the case of the TiO₂-coated surface, it is exposed to UV light for a few hours before experiment and it is found that the maximum heat flux (CHF) is about two times larger than that of the uncoated surface. The temperature at minimum heat flux (MHF) for the superhydrophilic surface is higher by 100 K than that for the normal one. The superhydrophilic surface can be an ideal heat transfer surface. Copyright © 2002 John Wiley & Sons, Ltd.     

Comparison between photocatalytic ozonation and other oxidation processes for the removal of phenols from water

Photocatalytic ozonation (1O₃ + VUV + TiO₂), ozonation (O₃), catalytic ozonation (O₃ + TiO₂), ozone photolysis (O₃ + VUV), photocatalysis (TiO₂ + VUV) and photolysis (VUV) have been compared in terms of formation of intermediates, extent of, mineralization (TOC, COD, chloride, nitrate) and kinetics in the aqueous treatment of three phenols (phenol, p‐chlorophenol and p‐nitrophenol). In all cases, photocatalytic ozonation led to lower degradation times for chemical oxygen demand and total organic carbon removal. Intermediates formed were similar in the different oxidation systems with some exceptions. They can be classified into three different types: polyphenols (resorcinol, catechol, hydroquinone), unsaturated carboxylic acids (maleic and fumaric acids) and saturated carboxylic acids (glyoxylic, formic and oxalic acids). First order kinetic equations have been checked for the oxidation processes studied in the case of the parent compound. Rate constants of these systems have also been calculated. Copyright © 2005 Society of Chemical Industry     

Evolution of grain structure in thin film reactions

In this paper, we examine, both experimentally and theoretically, the kinetics of formation and microstructure of product phases in thin film reactions, using the Nb/Al and Ti/Al systems as our prototypes. The results of calorimetry and microscopy studies are interpreted using simple kinetic and morphology models. In particular, the kinetic models employed here focus on the nucleation and growth components of the phase formation process and the morphology models provide a starting point for the classification of product grain structures. An erratum to this article is available at .     

新型重整催化剂的研究——Pt／L中沸石酸碱性的作用

Ｐｔ／ＫＬ、Ｐｔ／ＢａＫＬ及Ｐｔ／ＨＬ上的铂与沸石的酸碱位发生相互作用，导致催化剂上存在不同电子状态和粒度分布的铂位，从而产生有着完全不同催化作用、不同抗硫性能的两类催化剂，即以碱性沸石为载体的“单功能”催化剂和以酸性沸石为载体的“双功能”催化剂。在Ｐｔ／ＫＬ、Ｐｔ／ＢａＫＬ催化剂上，存在着对硫敏感的具有环化脱氢功能和对硫不敏感的仅具有脱氢功能的两类铂活性位。     

掺钛蓝宝石激光晶体中夹杂物的分析

本文用大视场光学显微镜、电子探针观察和分析了掺钛蓝宝石激光晶体中夹杂物的形状、尺寸大小及元素组成，并提出消除和减少这些夹杂物的方法．     

钛容器的特点

根据钛材的化学、物理、力学和工艺性能介绍了钛容器在设计、制造、检验和应用方面的特点。     

助催化剂对TiCl_4/MgCl_2催化丙烯高温聚合的影响

研究了助催化剂种类(三甲基铝、三异丁基铝、三正己基铝、三乙基铝和甲基铝氧烷)及其含量对无内、外给电子体的TiCl4/MgCl2催化剂催化丙烯高温(100℃)聚合性能的影响,并用结晶分级分析、示差扫描量热和凝胶渗透色谱等方法分析了所得聚丙烯的结晶熔融行为和微观结构。实验结果表明,聚合温度从70℃升至100℃时,TiCl4/MgCl2催化剂的定向能力基本不变;100℃聚合时,以烷基化能力较弱的三异丁基铝为助催化剂时TiCl4/MgCl2催化剂的活性最高,而采用烷基化能力最强的三甲基铝为助催化剂时TiCl4/MgCl2催化剂的活性最低;100℃聚合时,助催化剂的种类对TiCl4/MgCl2催化剂的定向能力影响很小。     

Oxidation of porous nanocrystalline titanium nitride. II. Scale structure and composition

We have used x-ray phase analysis to study the composition of the products of reaction between oxygen and nanocrystalline powders with particle sizes 15, 40, 55, and 80 nm, and also specimens pressed (and sintered) from them. The powders were oxidized in air at 100°C (400 h) to 500°C (5 min), while the sintered specimens were oxidized at 600–900°C for 15, 120, and 240 min. In all cases, in the initial oxidation step the oxynitride Ti(O_xN_y) is formed, which over time is oxidized to TiO, Ti₂O₃, Ti₃O₅, TiO₂ (anatase) and TiO₂ (rutile). In the range 600–800°C, formation of a continuous oxide layer and conversion of anatase to rutile slows down diffusion of oxygen in the scale. We have established that at 900°C, the growth rate of the scale thickness increases and so the reflections from the oxynitride are barely noticeable on the diffraction patterns taken from the surface of the oxidized specimen. In these diffraction patterns, along with strong reflections from the rutile, we also observed weak reflections from lower oxides and anatase, which may be due to reaction between oxygen and the titanium ions diffused to the scale surface. We have concluded that at T > 850°C, the mechanism for oxidation of TiN changes. This is due to superposition of counterdiffusion of titanium ions on the diffusion of oxygen. __________ Translated from Poroshkovaya Metallurgiya, Nos. 3–4(448), pp. 72–78, March–April, 2006.     

原位TiCp/Fe复合材料的切削力及切屑形状

从退火态原位TiCp／Fe复合材料的切削力和切屑形状方面分析了其切削性能。研究结果表明其切削力及切削力的波动范围都小于铸态45钢，其切削性能比45钢好。TiCp／Fe复合材料的切屑为C形屑、长紧卷屑和发条状卷屑，在机加工中，产生这几种切屑是比较理想的。从切屑方面看，TiCp／Fe复合材料的切削性能较好。